황인동,염희남,정윤중 한국세라믹학회 2000 한국세라믹학회지 Vol.37 No.8
Recently, the protection of construction is demanded with environmental pollution. These protect modes are use of concrete admixture, coat of protective polymer and impregnate of surface with chemicals etc. The most widely used impregnation is economical and effective. The define of Impregnation for construction protect is reacted in and consolidated substrate after absorbed. The impregnation agents are Polyesters, Acrylic monomers, Epoxy and Silicone derivatives. Commonly, because the Silane has good water repellency and environmental advantages that it widely used to water proofing agents, dampproofing agents and absorption reducer for concrete of bridges. When application of Silane, it occurs pollution and harmfulness as included organic solvent. The manufactures have tired to emulsification of Silane for the reducing of the defects. The Silane emulsion is vary unstable and does not stored long periods, and it is diminished in good properties with internal reaction. In this study we tried to emulsification of Silane for effectiveness improvement and reduce pollution and hazard and discussed properties variation of emulsion. The Silane emulsions are achieved emulsifying with W/O and O/W type surfactants. It used 0.24% PVA as protective colloid and stable phase is creamy. The creamy Silane emulsion performance as the penetration depth and water absorption rate are above 4 mm and below 0.1. It stable about 6 month at room temperature.
콘크리트에서의 n-octyl ethoxy silane 발수제의 성능평가
황인동,이완조,염희남,정윤중 한국세라믹학회 2000 한국세라믹학회지 Vol.37 No.12
최근 콘크리트 보호 재료는 코팅을 이용하는 과거의 방법에서 함침을 이용하는 기법으로 전환하였다. 이중 발수제는 콘크리트의 표면의 특성을 변화시키는 것으로 친수성의 콘크리트를 소수성 물질을 결합시켜 물에 의한 젖음을 방어하는 것으로 콘크리트에 사용하였을 경우 콘크리트의 고유한 표면 장력을 작게 변화시키고 장력이 큰 물질 중의 하나인 물의 흡수를 방어하게 한다. 본 실험은 발수제의 성능 평가를 위하여 다공질의 재료인 콘크리트의 접촉각을 측정하여 그 변화를 관찰하였으며, 발수제들의 우수한 기능 중의 하나인 통기성을 시편의 중량 감소로 측정하였다. 발수제로 n-octyl ethoxy silane을 사용한 콘크리트 시편의 흡수 능력은 사용하지 않은 것의 약 10% 정도로 측정되었으며 시편의 수분 중량 감소는 7일 동안 90~130%로 관찰되어 통기성이 유지되어 콘크리트의 강도 유지에 효과적임을 알 수 있었다. 또한 겉보기 접촉각은 처리하지 않은 시편에서 24~33$^{\circ}$로 측정되었으나 처리된 시편의 최초면에서 130~141$^{\circ}$이었으며 2mm의 연마면에서는 127~132$^{\circ}$로 측정되어 콘크리트 표면 장력 변화가 유지되고 있음을 알 수 있었다.
황인동,염희남,정윤중 한국세라믹학회 2000 한국세라믹학회지 Vol.37 No.6
Two type of expanding cement generally referred to as CSA with Hauyne(3CaO 3Al2O3 CaSO4) and Quick lime(CaO). Hauyne is formed to ettringite when there are presented with CaO and CaSO4, and CaO reacts wtih water to form Ca(OH)2. REcently, the mechanism of compensation and expand mortar or concrete tend to same and it has been used improving on its shrink property. The volume of cement paste varies with its water content shrink with drying and re-wetting. Concrete and mortar works are required shrinking compensation and expansion properties to reduce of potential crack. The use of expansion cement may improve on its shrinking volume changes. CSA dosages for shrinking compensation limited by cement weight, but obtained difference expansion rate with varied W/C or inorganic admixture. This paper studies expansion rate according to expansion cement dosages, water and inorganic admixtures as Silica fume. Therefor, the expansion factor has to considered before the application.
단면보수용 콘크리트 패치재료의 역학적 특성 및 내구성 실험
양성철,황인동,한승환,김성민 한국도로학회 2009 한국도로학회논문집 Vol.11 No.3
In this paper an experimental program was launched to determine the mechanical and durability properties of spall repair materials (RCC: 3 items, PCC: 2 items, PC: 3 items). Test items were mechanical property tests such as setting times, strengths, modulus of elasticity, plastic shrinkage, and durability tests such as dynamic modulus ratio, bond property with freeze-thaw, water absorption, chemical resistance, ultraviolet exposure. Modulus of the PC products exhibits ductile while the modulus is in the order of RCC > PCC > PC. At early ages the PC products experience higher plastic shrinkage than others, henceforth stable at 28 days. Other test results such as dynamic modulus ratio, absorption, and chemical resistance show that the PCs are superior to the PCCs and the RCCs. Except for PC-2, all patch materials had bond strength more than 1.3MPa after freeze-thaw cycles of 200∼300 while the PCs and the PCCs seem to be better than the RCCs. With 500 hours of ultraviolet exposure, all patch materials showed to have no crack or deterioration at the surface. 본 연구에서는 콘크리트포장의 단면보수용 복합재료 8개(초속경시멘트계열:RCC 3종, 폴리머시멘트계열:PCC 2종, 폴리머계열:PC 3종)에 대해 역학적인 특성 및 내구성 실험을 수행하였다. 역학적 특성으로서 응결시간, 압축강도, 휨강도, 탄성계수, 경화수축에 대해 실험하였고, 내구성으로서 동탄성계수 및 동결융해 후 부착강도, 흡수율, 내화학성, 자외선노출 실험을 수행하였다. 탄성계수는 RCC > PCC > PC계열의 순으로 나타나서 폴리머가 사용되면서 연성의 특성을 보였다. 초기 재령에서의 폴리머 콘크리트의 경화수축이 상대적으로 큰 것으로 관찰되었지만 재령 28일에서는 다소 안정된 결과를 보였다. 상대동탄성계수, 흡수율, 10% CaCl2와 10% Na2SO4의 화학용액을 사용한 내화학성 실험결과 PC계열, PCC계열, RCC계열 순으로 저항성이 우수한 것으로 나타났다. 200∼300회 동결융해 이후의 부착강도 실험결과 PC-2를 제외하고는 모두 1.3MPa 이상을 확보하였고, PC 및 PCC 제품의 부착강도가 RCC 제품보다 전체적인 면에서 우수한 것으로 나타났다. 또한 시편을 500시간동안 자외선 노출시험 결과 모든 패치재료 시편에서 균열 및 표면 결함 등이 발견되지 않아 PC 및 PCC 제품의 자외선에 대한 내구성이 확보됨을 확인하였다.