부스닥트용 내열성 에폭시 분체도료의 절연 및 열화 특성 연구
강철화,박지군,박종규,주현돈,김현희,Kang, Cheolhwa,Park, Ji-Koon,Park, Jong-Kyu,Ju, Hyun-Don,Kim, Hyun-Hee 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.9
Reported here are results of the mechanical and electrical properties of both of intact and thermally degraded epoxy-coated copper busducts that are made by fluidized bed process. To elucidate and compare the properties mentioned above, electrical breakdown by thermal and water aging, v-t characteristic, bending test, impact test and cross cut test are carried out. Although the performance of electrical and mechanical properties are gradually decreased in increasing the severe conditions such as temperature, aging time, and so forth, sample C has a better performance in both mechanical and electrical properties.
강철화(Kang, Chul-Hwa),최지현(Choi, Ji-Hyun),박지군(Park, Ji-Kun),주현돈(Ju, Hyun-Don),김현희(Kim, Hyun-Hee) 한국화재소방학회 2011 한국화재소방학회 학술대회 논문집 Vol.2011 No.추계
대용량 기기의 효율적인 전력 공급을 위해 부스닥트의 수요가 급증하고 있으며, 특히 컴팩트형 부스닥트는 케이블에 비해 무게와 부피가 가볍고 전력 효율도 25% 이상 우수하며, 기술의 핵심은 에폭시분체도료의 절연 특성 향상과 제작공정의 최적화와 안정화이다. 따라서 본 연구에서는 유동침적방식(Fluidized Bed Process)에 대한 최적화와 에폭시 분체도료의 절연설계 및 열화특성에 대해 실험 검토 하였다. 또한 전기화재의 주된 원인인 아크방전특성과 절연파괴 특성에 대한 분석과 더불어 다양한 상용제품들의 특성을 비교하였다.
KNbO<sub>3</sub> 치환이 (Li,Na,K)(Nb,Sb,Ta)O<sub>3</sub>계 세라믹스의 유전 및 압전 특성에 미치는 영향
노정래,류주현,이상돈,Noh, Jungrae,Yoo, Ju-Hyun,Lee, Sang-Don 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.3
In this study, $KNbO_3$-substituted (Li,Na,K)(Nb,Sb,Ta)$O_3$ ceramics were investigated to develop Pb-free composition ceramics for multilayer actuator and energy harvester applications. The X-ray diffraction analysis indicated that all samples were pure perovskite phase and no secondary phase was found. A tetragonality as a function of $KNbO_3$ substitution showed the maximum value at 1.5 mol% $KNbO_3$ and then decreased. The SEM image analysis showed the maximum grain size of $3.14{\mu}m$ at 1.5mol% $KNbO_3$. In the composition ceramics with 1.5 mol% $KNbO_3$ sintered at $1,100^{\circ}C$, excellent properties of density= 4.75 $g/cm^3$, electromechanical coupling factor ($k_p$)= 0.50 and piezoelectric constant($d_{33}$)= 290 pC/N were obtained, respectively, suitable for piezoelectric actuator and energy harvester applications.