http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
변창섭,임수곤,김수곤,신훈규,Byun, Chang-Sub,Lim, Soo-Gon,Kim, Su-Kon,Shin, Hoon-Kyu 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.7
We investigated the variation of anion exchange membrane of hydrogen generator of alkaline electrolysis. We detected the variation of elements and change of anion exchange membrane using EDS and FE-SEM. We detected two different sites of membrane because of different structure of membrane. $Sp_1$ shows that the distribution ratio of C, O, Al is 98% very higher than $Sp_2$ of 78%. Especially, the main elements of STS316 which is P, S, Fe, Ni were more detected at $Sp_2$ than $Sp_1$. We think that this result depends on the structure of membrane. This also affect the resistance, lifetime of membrane and decrease the efficiency of hydrogen production. We hope that this article is a foundation of developing of hydrogen production technology.
알칼리 전해액의 상호작용에 의한 Stainless Steel 주성분의 변화 분석
변창섭,임수곤,김수곤,최호상,신훈규,Byun, Chang-Sub,Lim, Soo-Gon,Kim, Su-Kon,Choi, Ho-Sang,Shin, Hoon-Kyu 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.7
In this paper, We studied the change of surface and variation of elements on both electrodes of hydrogen generator of alkaline electrolysis in use of FE-SEM and SIMS. We used the stainless steel 316(600 ${\mu}m$) as electrode in condition of 25%KOH, $60^{\circ}C$ Temperature. The results show that the intensity of elements (C, Si, P, S, Ti, Cr, Mn, Fe, Ni, Mo) of Positive Electrode are decreased as much as about $10^1{\sim}10^3 $than the original electrode. Thickness of Positive Electrode is decreased about 40 ${\mu}m$ after chemical reaction. The negative electrode, however, shows a slight variation in the intensity of elements (C, Si, P, Fe, Ni, Mn, Mo) but Change of thickness and surface' shape of electrode show nothing after chemical reaction. The change in thickness and variation of Stainless Steel 316 cause the lifetime of electrode to be shorted. We also observed hydrogen, oxygen, potassium in both electrodes. Especially, The potassium is increased in proportional with depth of positive electrode. this means the concentration of alkali solutions is changed. and so we have to supply alkaline solution to generator in order to produce same quantity of hydrogen gas continuously. we hope that this study gives a foundation to develop the electrode for hydrogen generator of alkaline electrolysis.
알칼리 용액이 수소배관으로 사용되는 Stainless steel에 미치는 영향 분석
변창섭,최진영,임수곤,황갑진,신훈규 한국수소및신에너지학회 2012 한국수소 및 신에너지학회논문집 Vol.23 No.3
This study was performed to observe the change of stainless steel pipe interacting with alkaline solution. We used STS316L and STS304 as samples which were soaked in alkaline solution. We measured the samples by use of FE-SEM, EDX, SIMS to observe the surface and depth profile of both samples. The result showed that the precipitate appeared on the surface of both samples from 5 days. but the precipitate was confirmed to be decreased as time passes. but the quantitative change of precipitates at both samples was different as time passed. The EDX showed that the precipitate is Potassium from solution of Electrolysis. The result also showed that the primary elements of stainless steel pipeline and of Alkaline Solution were changed. The change of primary elements was severe between 5 days to 16 days and was stable around 40 days at both samples. The reaction of STS316L with alkaline solution was lower than STS304. We hoped that this study would be the foundation of developing the electrode of the alkaline hydrogen generator.