http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
이임렬,이수행,김유혁,Lee, R.Y.,Lee, S.H.,KIm, Y.H. 한국재료학회 2002 한국재료학회지 Vol.12 No.9
$(Y,Gd)BO_3$: Eu, $Zn_2$$SiO_4$ : Mn and $BaMgAl_{10}$ $O_{17}$ : Eu phosphors used in PDP were continuously irradiated by vacuum ultra violet generated from the penning gas (96%Ar+4%Xe) discharge and then the change of emitting intensity with time was investigated. The brightness of these phosphors decreased exponentially with VUV excitation time. The experimental data showed that the degradation rate increased in the order of $Zn_2$$SiO_4$ : Mn>(Y,Gd)$BO_3$: Eu>$BaMgAl_{10}$ $O_{17}$ : Eu phosphor. This different degradation property of phosphors was interpreted in terms of brightness saturation and stability against VUV irradiation. It was found that the degradation property of $(Y,Gd)BO_3$ : Eu red phosphor synthesized by ultrasonic thermal spray was superior to commercial phosphor.
이임렬,Lee R. Y. 한국마이크로전자및패키징학회 2005 마이크로전자 및 패키징학회지 Vol.12 No.3
알루미나 기판에 빗살 모양의 금 전극을 형성한 후 플라즈마 화학기상법으로 탄소 나노튜브를 성장하여 이산화질소 감지 특성을 조사하였다. 탄소 나노튜브 센서의 전기저항은 온도 증가에 따라 감소하는 반도체 특성을 보였으며, 또한 이산화질소의 농도가 증가하면 센서의 전기 저항은 감소하였다. 이산화질소의 흡착에 따라 탄소 나노튜브 센서의 전기저항은 초기 3분 이내에서는 급격히 감소하였으며 $20\~30$분 후에는 일정한 값을 유지하였다. 탄소 나노튜브 센서의 감도는 공기속에서 산화 열처리하면 증가되었다. $450^{\circ}C$에서 30분간 산화 열처리한 탄소 나노튜브 센서는 작동온도 $v$에서 낮은 이산화질소 농도인 250 ppb 에서도 $27\%$의 큰 감도를 보였다. 그러나 이산화질소 검출 후 재사용하기 위하여는 20분 이상의 회복 시간이 요구되고 있다. Carbon nanotubes (CNT) which were grown, on the alumina substrate with a pair of comb-type Au electrodes, by plasma enhanced chemical vapor deposition have been investigated for $NO_2$ gas sensor. The electrical resistance of CNT film decreased with temperature, indicating a semiconductor type of CNT, and also the resistance of CNT sensor decreased with increasing $NO_2$ concentration. Upon exposure to $NO_2$ gas, the electrical resistance of CNT film sensor rapidly decreased within 3 minutes, and then showed a constant value after $20\~30$ minutes. It is found that the sensitivity of CNT sensor has been improved by air oxidation. The CNT sensor oxidized at $450^{\circ}C$ for 30 minutes showed higher sensitivity value than that without oxidation by $27\%$, even for a low 250 ppb $NO_2$ concentration at operating temperature of $200^{\circ}C$. But it needs a recovery time more than 20 minutes for reuse after detection of $NO_2$ gas.
Pd 및 CNT 첨가에 따른 $SnO_2$ 박막의 이산화질소 감지특성
김형균,이임렬,Kim, H.K.,Lee, R.Y. 한국마이크로전자및패키징학회 2008 마이크로전자 및 패키징학회지 Vol.15 No.4
이산화질소를 감지할 수 있는 센서물질로 Pd과 탄소 나노튜브(CNT)가 첨가된 $SnO_2$ 박막을 스핀코팅으로 제조하였으며, 동 시편의 이산화질소에 대한 감지 특성을 $200^{\circ}C$ 및 $1ppm{\sim}5ppm$의 $NO_2$ 농도 하에서 측정하였다. 센서시편의 전기저항은 $NO_2$ 기체의 노출과 농도에 따라 증가 하였으며, Pd이 3wt%로 첨가된 시편의 감도는 26.5로 첨가전의 감도에 비하여 10배 증가하였다. 또한 $SnO_2$ 모체에 첨가한 CNT의 량에 따라서도 감도는 증가 하였으며, 0.225wt% CNT 첨가 시 5ppm의 $NO_2$ 농도에서 감도 값은 72이었다. The $SnO_2$ thin films doped with Pd and CNT as $NO_2$ gas sensor were prepared by spin coating and then the $NO_2$ gas response of these films were evaluated under $1ppm{\sim}5ppm\;NO_2$ concentration and operating temperature of $200^{\circ}C$. It was found that the sensor resistance was increased with $NO_2$ exposure and $NO_2$ concentration. The 3wt% Pd doped sample showed a sensitivity of 26.5 which was 10 times higher than that of pure $SnO_2$. And also the sensitivity of CNT doped sample increased with CNT content and it had 72 when 0.225 wt% of CNT was added under 5ppm $NO_2$ concentration.