http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
전기방사법으로 제조된 실리카/폴리카프로락톤 적층형 부직포에 배양한 골아 세포의 중식, 분화에 관한 연구
안민국,김경화,김태일,이용무,이상훈,구영,류인철,정종평,한수부,설양조,AN, Min-Kuk,Kim, Kyoung-Hwa,Kim, Tae-II,Lee, Yong-Moo,Rhee, Sang-Hoon,Ku, Young,Rhyu, In-Chul,Chung, Chong-Pyoung,Han, Soo-Boo,Seol, Yang-Jo 대한치주과학회 2007 Journal of Periodontal & Implant Science Vol.37 No.1
Silica is known as a promising osteoconductive material, and polycaprolactone is a bioactive and degradable material. The purpose of this study was to monitor the differentiation of MC3T3-E1 cells cultured on the layer-built silica/poly caprolactone non-woven fabric produced by electrospinning. Non-woven fabric (silica, polycaprolactone, PSP, SPS) was made by electrospinning and they were inserted in the 48 well cell culture plate. MC3T3-E1 cells were prepared by subculture. Cells were seeded to each well $1{\times}10^5$ concentration per well. Dulbecco's modified eagle medium with 10% FBS and 1% antibiotic-antimycotic solution was used. Confocal laser scanning microscope was taken 4 hours after incubation (95% air. 5% $CO_2$, $37^{\circ}C$). Cell proliferation was monitored by spectrophotometer on 1, 7, 14 days, and the morphology of the growing cells was observed by field emission scanning electron microscope. To monitor the differentiation of osteoblasts on the materials, MC3T3-E1 cells were incubated in 48 well culture plate after seeding with the density of $1{\times}10^5$ concentration. Then ELISA kit & EIA kit were used on to assess osteocalcin and osteopontin expression respectively. The other conditions were the same as above. MC3T3-E1 cells were proliferated well on all of the materials. There were no statistical differences among them. The osteopontin expression of silica, PSP, SPS was significantly higher than other groups on day 3 (p/0,05), but after that time, there were no statistically signigicant differences. The osteocalcin expression was significantly higher in silica and PSP than other groups on day 14. These findings show that PSP was as good as silica on the effect of osteoblast differentiation. The PSP non-woven fabric may have the possibility as bone graft materials.
안민국,김현주,최진욱,김경화,이용무,류인철,설양조 대한치주과학회 2022 Journal of Periodontal & Implant Science Vol.52 No.5
Purpose: The purpose of this study was to evaluate and compare the healing patterns of 2-mm and 4-mm proximal infrabony defects adjacent to dental implants in canine mandibles. Methods: Four male beagles were used. Two groups were created: a 2-mm group (n=4) and a 4-mm group (n=4) depending on the horizontal dimension of proximal infrabony defects adjacent to implants. Bone healing patterns between the 2 groups were evaluated and compared at 8 and 16 weeks using radiographic, histological, histomorphometric, and fluorescent labelling analyses. Results: According to microcomputed tomography, the median bone volume fraction, bone mineral density, and the percentage of radiographic distance from the defect bottom to the most coronal bone-to-implant contact (radio-mcBIC) were 32.9%, 0.6 g/cm3 , and 73.7% (8 weeks) and 45.7%, 0.7 g/cm3 , and 76.0% (16 weeks) in the 2-mm group and 57.7%, 0.8 g/ cm3 , and 75.7% (8 weeks) and 50.9%, 0.8 g/cm3 , and 74.7% (16 weeks) in the 4-mm group, respectively. According to histomorphometry, the median bone area fraction, mcBIC and the percentage of BIC amounted to 36.7%, 3.4 mm, and 58.4% (8 weeks) and 49.2%, 3.4 mm, and 70.2% (16 weeks) in the 2-mm group and 50.0%, 3.0 mm, and 64.8% (8 weeks) and 55.7%, 3.0 mm, and 69.6% (16 weeks) in the 4-mm group, respectively. No statistically significant differences were found between the groups for any variables (P>0.05). Conclusions: The proximal defects that measured 2 mm and 4 mm showed similar healing patterns at 8 and 16 weeks, and the top of bone formation in the defects was substantially limited to a maximum of 1.6 mm below the implant shoulder in both groups.