류지승,노태민,김진성,이희수,Ryu, Ji-Seung,Noh, Tai-Min,Kim, Jin-Seong,Lee, Hee-Soo 한국결정성장학회 2012 한국결정성장학회지 Vol.22 No.2
The structural change and the electrical conductivity with Sr content in $La_{1-x}Sr_xMn_{0.8}Cu_{0.2}O_3$ (LSMCu) were studied. $La_{0.8}Sr_{0.2}MnO_3$ (LSM) and $La_{1-x}Sr_xMn_{0.8}Cu_{0.2}O_3$ ($0.1{\leq}x{\leq}0.4$) were synthesized by EDTA citric complexing process (ECCP). A decrease in the lattice parameters and lattice volumes was observed with increase of Sr content, and these results were attributed to the increasing $Mn^{4+}$ ions and $Cu^{3+}$ ions in B-site. The electrical conductivity measured from $500^{\circ}C$ to $1000^{\circ}C$ was increased with increase of Sr content in the $0.1{\leq}x{\leq}0.3$ composition range, and it was 172.6 S/cm (at $750^{\circ}C$) and 177.7 S/cm (at $950^{\circ}C$, the maximum value) in x = 0.3. The electrical conductivity was decreased in x = 0.4 because of the presence of the second phase in the grain boundaries. The lattice volume was contracted by increase of $Mn^{4+}$ ions and $Cu^{3+}$ ions in B-site according to increase of Sr content and the electrical conductivity was increased with increase of charge carriers which were involved in the hopping mechanism. $La_{1-x}Sr_xMn_{0.8}Cu_{0.2}O_{3-{\delta}}$(LSMCu)에서 Sr 함량에 따른 구조적 변화와 전기전도도에 대해 연구, 고찰하였다. EDTA citric complexing process(ECCP)로 페로브스카이트 구조를 갖는 $La_{0.8}Sr_{0.2}MnO_3$(LSM)와 $La_{1-x}Sr_xMn_{0.8}Cu_{0.2}O_3$($0.1{\leq}x{\leq}0.4$)을 제조하였다. Sr 함량이 증가할수록 격자상수와 격자부피는 감소하는 경향을 나타내었으며, 이는 Sr 함량이 증가함에 따라 B-site에서 증가하는 $Mn^{4+}$ 이온과 $Cu^{3+}$ 이온의 영향인 것으로 판단하였다. $0.1{\leq}x{\leq}0.3$ 범위의 조성에서 Sr 함량이 증가할수록 $500{\sim}1000^{\circ}C$에서 측정된 전기전도도는 증가하였고, x = 0.3 조성에서는 $750^{\circ}C$와 $950^{\circ}C$에서 각각 172.6 S/cm와 177.7 S/cm (최고값)를 나타내었다. 반면, x = 0.4 조성에서는 전기전도도가 감소하였는데 이는 입계에 발생한 산화물에 의한 영향으로 판단하였다. Sr 함량이 증가함에 따라 B-site에 존재하는 $Mn^{4+}$ 이온과 $Cu^{3+}$ 이온의 증가로 인해 격자수축이 발생하고, hopping mechanism에 관여하는 charge carrier들이 늘어나 전기전도도가 증가한 것으로 판단하였다.
노태민,류지승,김진성,정철원,이희수,Noh, Tai-Min,Ryu, Ji-Seung,Kim, Jin-Seong,Jeong, Cheol-Weon,Lee, Hee-Soo 한국결정성장학회 2011 한국결정성장학회지 Vol.21 No.4
이종 원자가를 가시는 Cu의 도핑이 LSM에 미치는 영향을 구조적인 분석과 열팽창계수를 통해서 고찰하였다. 고상반응을 이용하여 $La_{0.8}Sr_{0.2}Mn_{1-x}Cu_xO_3$($0{\leq}x{\leq}0.3$)음 제조하였으며, Cu의 도핑 함량에 따른 결정구조 및 열팽창계수를 확인하였다. Cu 함량이 증가함에 따라서 격자상수외 열팽창계수가 감소하는 경향을 나타냈지만, x = 0.3인 경우에는 증가 하였다. 이러한 격자상수와 열팽창계수의 변화는 Cu 이온의 B-site에서의 Mn 자리에 치환될 때 $0{\leq}x{\leq}0.2$의 범위에서는 $Cu^{3+}$의 존재로 인한 이온 반성의 감소에 의한 것으로 판단되었고, x=0.3인 경우에는 $Cu^{2+}$와 $Mn^{4+}$의 존재로 인한 산소 공공의 증가에 기인한 것이었다. The doping effect of Cu in the Sr-doped lanthan manganites (LSM) has been investigated in terms of structural analysis and thermal expansion coefficient (TEC). The $La_{0.8}Sr_{0.2}Mn_{1-x}Cu_xO_3$ ($0{\leq}x{\leq}0.3$) were prepared by solid state reaction method and their crystal structure and TEC were measured. A decrease in the lattice parameters and the TEC were observed with increase eu content, whereas they were decreased for x = 0.3. For $0{\leq}x{\leq}0.2$, the decrease of the lattice parameter and the TEC with increase Cu content were attributed to the reduction of ionic radius of Cu ions due to the presence of $Cu^{3+}$ ions. For x = 0.3, however, the increase was originated from the formation of oxygen vacancies due 10 the presence of $Cu^{2+}$ and $Mn^{4+}$.
Dysprosium과 Erbium이 동시 첨가된 X7R MLCC용 페로브스카이트 BaTiO<sub>3</sub>의 전기적특성과 온도안정성
노태민,김진성,류지승,이희수,Noh, Tai-Min,Kim, Jin-Seong,Ryu, Ji-Seung,Lee, Hee-Soo 한국세라믹학회 2011 한국세라믹학회지 Vol.48 No.4
The effects of $Dy_2O_3$ and $Er_2O_3$ co-doping on electrical properties and temperature stability of barium titanate ($BaTiO_3$) ceramics were investigated in terms of microstructure and structural analysis. The dielectric constant and the insulation resistance (IR) of 0.7 mol% $Dy_2O_3$ and 0.3 mol% $Er_2O_3$ co-doped dielectrics had about 60% and 20% higher than the values of undoped one, respectively, and the temperature coefficient of capacitance (TCC) met the X7R specification. The addition of $Dy_2O_3$ contributed to electrical properties caused by increase of tetragonality; however, preferential diffusion of $Dy^{3+}$ ions toward A site in $BaTiO_3$ grain exhibited an adverse effect on temperature stability by grain growth. On the other hand, The $Er_2O_3$ addition in $BaTiO_3$ could affect the TCC behavior and the IR with suppression of grain growth caused by reinforcement of grain boundary and electrical compensation. Therefore, the enhanced electrical properties and temperature stability through the co-doping could be deduced from the increase of tetragonality and the suppression of grain growth.
R 과 분석 알고리즘을 활용한 기업의 성장성 예측에 관한 연구
강희석 ( Hui-seok Kang ),김경수 ( Kyung-su Kim ),류지승 ( Ji-seung Ryu ),이가연 ( Ga-yeon Lee ),이민정 ( Min-jung Lee ) 한국정보처리학회 2017 한국정보처리학회 학술대회논문집 Vol.24 No.2
기업의 성장성과 기업 주식가치를 매출, 매출원가, 영업이익율 등의 정형데이터와 경제, 경영 관련 뉴스 등 비정형 데이터를 토대로 다양한 알고리즘을 활용해 분석하고, 그 결과의 유의성을 검증한다. 주성분회귀분석, 인공신경망, 나이브 베이지안 분류자, 긍/부정 사전분석 모델을 통해 분석된 결과를 검토하여 각 분석모델 별성능을 확인하고, 기업 성장성 예측을 위해 활용 가능한 모델과 필요한 데이터를 제시한다.