길남규,성기완,안창윤,민택기 충남대학교 공업교육연구소 1999 論文集 Vol.22 No.1
This study deals with the mechanical properties of welding part, by friction welding of SM45C steel rod and SWS41A yoke which have being used Steering-Joint. The experimental results are summrized as follows ; 1. When CO₂welding is replaced with friction welding, we can get benefit manufacture. 2. The result of tensile test showed the highest tensile strength of 612MPa(150% of base metal strength 402MPa). 3. The result of bending test showed the highest bending strength of 1066MPa(80% of base metal strength 1259MPa).
성기완,길남규,신석우,민택기 충남대학교 산업기술연구소 2000 산업기술연구논문집 Vol.15 No.1
This study dealt with the mechanical properties of aluminum alloy A5083 friction welds contained upset length, tensile test, hardness test, observation of microstructure and tensile fractured surface. The welding conditions of the maximum tensile strength of friction weld were revolution 2000rpm, friction pressure 50MPa, upset pressure 110MPa, friction time 1.0sec, and upset time 6.0sec. This study came to these conclusion as follow : 1.The maximum tensile strength was 355MPa which was 102% of the tensile strength 348MPa of the base material. 2.The conditions when maximum tensile strength was acquired, occurred dimple on the tensile fracture surface and upset length was 4.9mm. 3.The maximum hardness was Hv89 in the weld interface and soft zone was confirmed on the heat affected zone(HAZ).