김상원,Kim S. W. 한국재료학회 2005 한국재료학회지 Vol.15 No.2
Effects of stainless steel-making dusts and binder content on compacting $density(\rho)$ and magnetic properties were evaluated. Cores compacted with the mixture of pure Fe powders, $5wt.\%$ dusts and $0.25wt.\%$ binder showed good AC magnetic properties. For example, permeability$({\mu}a)$ and core loss(P) of the cores containing $5wt.\%$ dusts at 500 kHz were 62 and $4008\;{\mu}W/cm^3$, respectively. These properties are almost equivalent to those of competitor's products (i.e, Ancorsteel TC 80 produced by $H\ddot{o}gan\ddot{a}s$ Corp.). The powdered cores obtained from the present work are expected to apply for high-performance soft magnetic components such as normal mode choke filter and pulse transformer.
Fe-Cr-Al계 합금 빌렛의 상온 표면균열 원인에 관한 연구
김상원,박종혁,김인배,Kim S. W,Park J. H,Kim I. B. 한국재료학회 2004 한국재료학회지 Vol.14 No.1
Metallurgical and mechanical experiments were performed to explain unexpected surface cracks encountered in fabricating ground rolled-billet of Fe-Cr-Al alloys at room temperature. The toughness of these alloys containing between 220 and 236 ppm (C+N) has been assessed using notched-bar impact tests. According to our results, with a larger grain size, a higher interstitial content of (C+N) or a smaller size of precipitates, ductile to brittle temperature(DBTT) increased and absorbed energy decreased at room temperature. These results suggest that the surface cracks at room temperature stem from a poor resistance to brittle fracture, due to dislocation movement by the finely dispersed carbides within grains under the condition of higher (C+N) content.