http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
LTCC RF 모듈용 $BaO-Nd_2O_3-TiO_2$계 세라믹스의 저온소결 및 마이크로파 유전특성
신동순,최영진,박재환,남산,박재관,Shin, Dong-Soon,Choi, Young-Jin,Park, Jae-Hwan,Nahm, Sahn,Park, Jae-Gwan 한국마이크로전자및패키징학회 2003 마이크로전자 및 패키징학회지 Vol.10 No.1
The effects of glass addition on the low-temperature sintering and microwave dielectric properties of $BaO-Nd_2O_3-TiO_2$ dielectric ceramics were studied. When 10∼13 wt% of lithium borosilicate glass was added, the sintering temperature decreased from 130$0^{\circ}C$to 850-$900^{\circ}C$relative density of more than 97% was obtained. When the sample was sintered at $850^{\circ}C$ with 10 wt% of glass, the dielectric properties of $\epsilon_r{\ge}54$, $Q{\times}f_0{\ge}2300$, and $\tau_f{\ge}+8ppm/^{\circ}C$ were obtained. $BaO-Nd_2O_3-TiO_2$계 유전체 세라믹스에 lithium borosilicate계 유리를 첨가하여 저온소결특성과 마이크로파 유전특성을 조사하였다. 유리 프릿을 10∼l3 wt%의 범위로 첨가함으로서 순수한 $BaO-Nd_2O_3-TiO_2$계 세라믹스의 소결온도($1300^{\circ}C$)보다 현저히 낮은 850∼$900^{\circ}C$의 온도범위에서 상대밀도 97%이상의 소결체를 얻을 수 있었다. 10 wt%의 유리 프릿을 첨가함으로서 85$0^{\circ}C$의 소성온도에서 유전율($\epsilon_r$)54 및 품질계수($Q{\times}f$)2400 GHz그리고 공진주파수의 온도계수($\tau_f$)는 $+8ppm/^{\circ}C$으로서 우수한 유전 특성을 가지는 소결체를 얻을 수 있었다.
Glass첨가에 의한 BaO-Nd<sub>2</sub>O<sub>3</sub>-TiO<sub>2</sub>계 세라믹스의 저온소결과 마이크로파 유전특성
신동순,최영진,박재환,남산,박재관,Shin, Dong-Soon,Choi, Young-Jin,Park, Jae-Hwan,Nahm, Sahn,Park, Jae-Gwan 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.1
BaO-Nd$_2$O$_3$-TiO$_2$계 유전체 세라믹스에 유리를 첨가하여 저온소결특성과 마이크로파 유전특성을 조사하였다. 알칼리가 첨가된 lithium borosilicate계 유리 프릿을 10~30wt% 범위로 첨가함으로서 소결온도를 130$0^{\circ}C$에서 100$0^{\circ}C$로 낮추었으며, 95% 이상의 상대밀도를 갖는 소결체를 얻을 수 있었다. 유리의 첨가량이 l0wt% 이상으로 증가함에 따라 결정상의 변화가 뚜렷이 나타났고 이에 따라 밀도 및 전기적 특성이 크게 변화하였다 l0wt%의 유리 프릿을 첨가하여 100$0^{\circ}C$에서 소결한 경우 유전율($\varepsilon$$_{r}$) 65 및 품질계수(Qxf) 2800GHz의 특성을 얻을 수 있었다. The effect of glass addition on the low-temperature sintering and microwave dielectric properties in $BaO-Nd_2O_3-TiO_2$ dielectric ceramics were studied. When 10~30 wt% of alkali lithium borosilicate glass was added, the sintering temperature decreases from $1300^{\circ}C$;to;1000^{\circ}C$ and the relative density more than 95% was obtained. When the added amount of glass increased above 10 wt%, the density as well as dielectric properties changed, which was attributed to the second phase formation. When the sample was sintered at 100$0^{\circ}C$ with l0wt% of glass, the dielectric properties of $Qxf_o{ge}2800,;{varepsilon}_r{ge}65;and;{ au_f=+55 ppm/^{\circ}C$ were obtained.
(Mg<sub>0.93</sub>Ca<sub>0.07</sub>)TiO<sub>3</sub> 세라믹스의 저온소결과 마이크로파 유전특성
신동순,최영진,박재관,박재환,남산,Shin, Dong-Soon,Choi, Young-Jin,Park, Jae-Gwan,Park, Jae-Hwan,Nahm, Sahn 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.6
(M $g_{0.93}$C $a_{0.07}$)Ti $O_3$마이크로파 유전체 세라믹스에 alumine borosilicate계 유리를 5~30wt% 첨가하여 저온소결 특성과 마이크로파 유전 특성을 조사하였다. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$에 alumine borosilicate계 유리를 첨가함으로서 소결온도를 135$0^{\circ}C$에서 95$0^{\circ}C$로 낮추었으며, 유리의 첨가량이 증가함에 따라 소결밀도의 증가 및 입성장이 뚜렷이 나타났고 20~30wt%의 유리가 첨가된 영역에서는 95%의 상대밀도를 갖는 소결체를 얻을 수 있었다. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$에 20wt%의 alumino boiosilicate계 유리를 첨가함으로서 95$0^{\circ}C$에서 유전율($\varepsilon$$_{r}$)은 15~16, 품질계수(Q$\times$f)는 8000이었으며, 이때 공진주파수의 온도 계수($ au$$_{cf}$ )는 -45 ppm/$^{\circ}C$을 나타내었다. The effects of alumine borosilicate glass composition on the densification and the microwave properties of (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ ceramics were studied. As the amount of glass increase, the density of ceramics increases and grain growth enhances. When 20 ~30 wt% of glass added, it was densified to over 95% of (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ theoretical density. (M $g_{0.93}$C $a_{0.07}$)Ti $O_3$ ceramic sintered at 95$0^{\circ}C$ exhibits dielectric constants of 15~16, quality factor of 8000 and temperature coefficient of resonant frequency of -45 ppm/$^{\circ}C$ by adding 20 wt% alumine borosilicate glass.