Pushpendra Kumar Dwivedi,R. Vinjamuri,S. K. Sahoo,Krishna Dutta 대한금속·재료학회 2022 METALS AND MATERIALS International Vol.28 No.8
Ratcheting deformation in association with bulk texture evolution in HSLA steel is studied in this investigation. The cyclicdeformation behaviors and damage modes of the specimens are obtained at room temperature, employing asymmetric stresscontrolledtests under various combinations of mean stress and stress amplitudes. Bulk texture measurements of the specimensare done adopting an X-ray diffraction analysis. The results exhibit an increase in strain accumulation from 0.23 to 30.61%associated with a sharp reduction in ratcheting life from 3320 to 880 cycles by the increment in mean stress/stress amplitude. A continuous cyclic softening until the final failure is observed for all the ratcheting tests. It is noticed that variation of meanstress is more detrimental than stress amplitude in controlling strain accumulation while the effect of stress amplitude is morepronounced than mean stress for the reduction of ratcheting life. The fracture surface morphology indicates typical striationformation in the crack propagation region along with overload failure. The bulk texture studies indicate that there is a transitionbetween ‘ϒ’ fiber and ‘ζ’ fiber during all loading conditions. The texture intensity is increased from 5.71 to 11.68 withprogressive ratcheting strain accumulation. Here also, influence of stress amplitude is more significant than the mean stress.
연관 검색어 추천
이 검색어로 많이 본 자료
활용도 높은 자료