박성식,우승욱 한국지반공학회 2019 한국지반공학회논문집 Vol.35 No.1
About 3% of Casein is included in milk and it accounts for 80% of milk’s protein. It has an adhesive property when mixed with calcium hydroxide and sodium hydroxide solutions. It has been usually used to bond woods under dry condition but becomes weak when exposed to moisture. Such weakness is very critical when casein is applied for soil cementation under groundwater condition. Therefore, this study was aimed to protect such weakness by changing or adding certain ingredients of casein adhesive. Two types of cemented specimens were prepared with Nakdong river sand and tested for unconfined compressive strength and durability. Each specimen was mixed with casein or cement. Ingredients of casein binder suggested by the University of Wisconsin, which is called a standard casein recipe, was also prepared. This study tried 6 different types of casein binder recipe. Among them, one with 30% hydroxide calcium increase and 50% hydroxide sodium decrease compared with the standard casein was most effective. Based on the most effective casein recipe, cemented sand with 1-4% of casein ratio was prepared and tested. The unconfined compressive strength and durability index were 6,253kPa and 92% for the specimen with 4% of casein ratio and 1,500kPa and 62% for the one with 8% of cement ratio. Therefore, casein cemented sand showed better performance. In addition, over 3% of casein cemented sand had over 80% durability index.
전기-역학적 임피던스를 이용한 모래의 단위중량 및 강도 평가
박성식,우승욱,이정신,이새벽,이준철 한국지반공학회 2018 한국지반공학회논문집 Vol.34 No.2
In this study, the EMI (electro-mechanical impedance) of a small piezoelectric sensor was applied for measuring a unit weight and cementation (strength) of sand. Three different sizes of uncemented Nakdong River sand were filled loosely or densely into a compaction mold. A piezoelectric sensor with 20 mm in diameter was installed within sand for impedance measurement. A small Nakdong River sand was mixed with cement ratios of 4, 8 12, 16% and then compacted into a specimen with 50 mm in diameter and 100 mm in height. The specimen consisted of 6 layers with a sensor at the third layer. The impedance signals for 3 days and unconfined compressive strength at the 3rd day were measured. As the unit weight of uncemented sand increased, the resonant frequency increased slightly from 102 to 105 kHz but a conductance at resonant frequency decreased. For cemented sands, as the curing time and cement ratio increased, the resonant frequency increased significantly from 129 to 266 kHz but the conductance at resonant frequency decreased. The unconfined compressive strength (UCS) of cemented sands was between 289 and 1,390 kPa for different cement ratios. The relationship of UCS and resonant frequency linearly increased but one with a conductance at resonant frequency was in inverse proportion.