http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
김부안,남기우 한국세라믹학회 1997 한국세라믹학회지 Vol.34 No.2
소결온도 및 열처리에 의하여 미세조직을 변화시킨 질화규소의 파괴강도특성 및 그 신뢰성 평가를 하였다. 결정립이 클수록 파괴인성치는 증가하였지만 굽힘강도는 저하하였다. 균열재의 파괴응력 $\sigma$c와 등가균열길이 ae와의 관계는 프로세스 존 크기 파기기준에 의한 계산 결과와 매우 잘 일치하였다. 그리고 굽힘파괴응력 $\sigma$F와 파괴인성치 KIC의 통계적 특성을 고려한 파괴평가고건을 제안하였다. Silicon Nitride samples with different microstructure were prepared by hot pressing and subsequent heat treatment under N2 gas pressure. The fracture toughness (KIC)of Si3N4 increased with the increase of grain size, but the bending strength of plain specimen($\sigma$F) decreased. The relation between fracture stress($\sigma$c) and equivalent crack length(ae) agreed well with the calculated values by process zone size failure criterion. A probabilistic failure assessment curve is proposed based on both statistical character of $\sigma$F and KIC.
링 형 PZT 세라믹스의 기계적 물성에 대한 소결 조건의 영향
김부안,문창권,최영민,김헌주 한국동력기계공학회 2019 동력시스템공학회지 Vol.23 No.2
본연구에서는 소결조건의 영향에 따른 링형 PZT 세라믹스의 기계적물성을 조사하였다. 이러한 링형 PZT 세라믹스의 성형체는 HP 장치를 이용였고, 소결시에는 폐쇄형 도가니 안에서 실시하였다. 소결은 상압소결장치에서 하였는데 이때의 승온속도는 분당 3도, 5도 및 10도의 세종류로 하였다. 얻어진 결론은 다음과 같다. 상압소결에서 개방형 도가니보다 폐쇄형 도가니를 이용하면 고밀도의 PZT 세라믹스를 얻을 수 있었으며, 성형압력이 높을수록 더 높은 밀도를 얻을 수 있었다. 이것은 PZT 세라믹스의 각 성분의 증기압을 최대한 유지시킴으로써 소결 구동력이 향상되었기 때문으로 판단된다. 승온 속도가 낮을수록, 그리고 성형압력이 높을수록 치밀화 된 PZT 세라믹스를 얻을 수 있있으며 그에 따른 압축 강도가 향상되는 것으로 나타났으며, 특히, 도가니의 종류에 강도가 크게 변화하였다. PZT 세라믹스의 경도는 성형압력이 높을수록 그리고 승온 속도가 느릴수록 증가하는 경향을 보였지만 도가니의 종류에는 거의 차이가 나타나지 않았다. PZT 세라믹스의 파면의 관찰에서는, 승온 속도와 성형압력의 차이에 따른 결정립 크기의 변화가 비교적 명확하게 나타났다.
김부안 한국마린엔지니어링학회 2003 한국마린엔지니어링학회지 Vol.27 No.6
An experimental method to investigate the fracture strength and fracture toughness for the silicon nitrides sintered at various sintering temperature is established. The erosion rate for these materials in the various concentration of NaOH solution is also investigated. In result, the fracture strength of Si3N4 is decreased with the increase of sintering temperature. On the other hand, the fracture toughness KIC is increased with the increase of sintering temperature. The erosion rate of silicon nitride in the NaOH solution depend largely on the grain size and the concentration of NaOH solution. The erosion rate of silicon nitride sintered at $1800^{\circ}C$ was much higher than that at $1950^{\circ}C$. These results are due to the unique columnar structure of silicon nitride.
김부안(Bu Ahn Kim),남기우(Ki Woo Nam),조문호(Mun Ho Cho) 한국해양공학회 1999 韓國海洋工學會誌 Vol.13 No.1
67Ni-22Cr-10Al-1Y and ZrO₂-8Y₂O₃ were coated on the substrate surface of STS304 and Al2024 by the plasma spraying method. The adhesion of the films varies depending on the substrates and the laminating method. In the case of STS304, the cracks were observed at thermal shock temperature difference △T of 900℃ in the non functionally gradient material(NFGM) and at 1100℃ in the functionally gradient material(FGM). The film adhesion of the FGM is better than that of the NFGM in STS304.<br/> The cumulative AE count of the FGM of STS304 increased continuously at the bending test. But the NFGM of STS304 showed discontinuity of the AE count. The total AE count for the FGM of STS304 decreased as the number of thermal shock increased, and this tendency was evident as the thermal shock temperature difference increased.