http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
UV-Curable Fluorinated Crosslinkable Polyurethane-Acrylates for Marine Antifouling Coatings
Jin-Myung Park,Sung Yeol Kim,Seung-Kook An,Young-Hee Lee,Han-Do Kim 한국청정기술학회 2017 청정기술 Vol.23 No.2
To prepare UV-curable polyurethane-acrylate oligomer, NCO-terminated urethane prepolymers with trimethylolpropane, [TMP; 0 (0), 0.1 (0.021) and 0.2 (0.043) mole (mole fraction)] as crosslinkable tri-functional chain extender were end-capped with pentaerythritol triacrylate [PETA; 2.0 (0.400), 1.7 (0.354) and 1.4 (0.304) mole (mole fraction)] with one hydroxyl group/three vinyl functionalities. The stable as-formulated UV-curable polyurethane-acrylates [stable mixtures of PETA-capped oligomer/reactive acrylic monomer diluents without/with heptadecafluorodecyl methacrylate (PFA; 0, 6 and 9 wt%)] were formed up to 0.2 (0.043) mole (mole fraction) of TMP content in the prepolymer, while homogeneous-mixing failed at 0.3 (0.068) mole (mole fraction), in which the crosslink density in NCO-terminated urethane prepolymer was too high to enable the formation of stable mixture. This study examined the effect of TMP/PETA molar ratio and heptadecafluorodecyl methacrylate (PFA) content (wt%) on the properties of UV-cured polyurethane-acrylates as marine antifouling coating materials. The properties of UV-cured polyurethane-acrylate were found to be significantly dependent on the crosslinkable TMP/PETA ratio and PFA content. With the increasing of the TMP and PFA contents, the contact angles increased, and consequently the surface tension decreased. The adhesion of algae/barnacles to PFA contained film samples were found to be sufficiently weak to allow their easy removal. These results suggest that the UV-cured samples containing PFA have strong potential as coating materials for antifouling applications.
UV-Curable Fluorinated Crosslinkable Polyurethane-Acrylates for Marine Antifouling Coatings
Park, Jin-Myung,Kim, Sung Yeol,An, Seung-Kook,Lee, Young-Hee,Kim, Han-Do The Korean Society of Clean Technology 2017 청정기술 Vol.23 No.2
To prepare UV-curable polyurethane-acrylate oligomer, NCO-terminated urethane prepolymers with trimethylolpropane, [TMP; 0 (0), 0.1 (0.021) and 0.2 (0.043) mole (mole fraction)] as crosslinkable tri-functional chain extender were end-capped with pentaerythritol triacrylate [PETA; 2.0 (0.400), 1.7 (0.354) and 1.4 (0.304) mole (mole fraction)] with one hydroxyl group/three vinyl functionalities. The stable as-formulated UV-curable polyurethane-acrylates [stable mixtures of PETA-capped oligomer/reactive acrylic monomer diluents without/with heptadecafluorodecyl methacrylate (PFA; 0, 6 and 9 wt%)] were formed up to 0.2 (0.043) mole (mole fraction) of TMP content in the prepolymer, while homogeneous-mixing failed at 0.3 (0.068) mole (mole fraction), in which the crosslink density in NCO-terminated urethane prepolymer was too high to enable the formation of stable mixture. This study examined the effect of TMP/PETA molar ratio and heptadecafluorodecyl methacrylate (PFA) content (wt%) on the properties of UV-cured polyurethane-acrylates as marine antifouling coating materials. The properties of UV-cured polyurethane-acrylate were found to be significantly dependent on the crosslinkable TMP/PETA ratio and PFA content. With the increasing of the TMP and PFA contents, the contact angles increased, and consequently the surface tension decreased. The adhesion of algae/barnacles to PFA contained film samples were found to be sufficiently weak to allow their easy removal. These results suggest that the UV-cured samples containing PFA have strong potential as coating materials for antifouling applications.
UV-Curable Fluorinated Crosslinkable Polyurethane-Acrylates for Marine Antifouling Coatings
박진명,김성열,안승국,이영희,김한도 한국청정기술학회 2017 청정기술 Vol.23 No.2
To prepare UV-curable polyurethane-acrylate oligomer, NCO-terminated urethane prepolymers with trimethylolpropane, [TMP; 0 (0), 0.1 (0.021) and 0.2 (0.043) mole (mole fraction)] as crosslinkable tri-functional chain extender were end-capped with pentaerythritol triacrylate [PETA; 2.0 (0.400), 1.7 (0.354) and 1.4 (0.304) mole (mole fraction)] with one hydroxyl group/three vinyl functionalities. The stable as-formulated UV-curable polyurethane-acrylates [stable mixtures of PETA-capped oligomer/ reactive acrylic monomer diluents without/with heptadecafluorodecyl methacrylate (PFA; 0, 6 and 9 wt%)] were formed up to 0.2 (0.043) mole (mole fraction) of TMP content in the prepolymer, while homogeneous-mixing failed at 0.3 (0.068) mole (mole fraction), in which the crosslink density in NCO-terminated urethane prepolymer was too high to enable the formation of stable mixture. This study examined the effect of TMP/PETA molar ratio and heptadecafluorodecyl methacrylate (PFA) content (wt%) on the properties of UV-cured polyurethane-acrylates as marine antifouling coating materials. The properties of UV-cured polyurethane-acrylate were found to be significantly dependent on the crosslinkable TMP/PETA ratio and PFA content. With the increasing of the TMP and PFA contents, the contact angles increased, and consequently the surface tension decreased. The adhesion of algae/barnacles to PFA contained film samples were found to be sufficiently weak to allow their easy removal. These results suggest that the UV-cured samples containing PFA have strong potential as coating materials for antifouling applications.