Haibo Jin,Heng Jiang,Qiwei Wang,Suohe Yang,Guohua Luo,Guangxiang He 한국화학공학회 2017 Korean Journal of Chemical Engineering Vol.34 No.2
A novel solid superbase 3%K/K2CO3 was prepared by loading metallic potassium on K2CO3. The optimized preparation conditions included a loading time of 1.5 h, loading temperature of 150 oC, loading amount of 3wt% and average carrier size of 120 μm. Under the optimum conditions, the conversion of propylene is about 60% with the selectivity of dimers 98.5% and the selectivity of 4MP1 86.3%. In addition, the superbase 3%K/K2CO3 has a base strength of H−≥37, and the concentration of basic sites of H−≥35 is approximately 0.3mmol·g−1 CAT. The microcrystal of metallic potassium was determined using X-ray diffraction (XRD) and differential scanning calorimetry (DSC). It was assumed that the oxygen species, which are adjacent to lattice defects, such as the crystalline corners, edges and vacancies of metallic potassium microcrystals, constituted the superbasic sites.