http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Duan, Zhongyu,Ma, Guoli,Zhang, Wenjun Korean Chemical Society 2012 Bulletin of the Korean Chemical Society Vol.33 No.12
A novel copper nanoparticles were synthesized from cupric sulfate using hydrazine as reducing reagents. A series of aromatic nitro compounds were reacted with sodium borohydride in the presence of the copper nanoparticles catalysts to afford the aromatic amino compounds in high yields. Additionally, the catalysts system can be recycled and maintain a high catalytic effect in the reduction of aromatic nitro compounds.
Zhongyu Duan,Guoli Ma,Wenjun Zhang 대한화학회 2012 Bulletin of the Korean Chemical Society Vol.33 No.12
A novel copper nanoparticles were synthesized from cupric sulfate using hydrazine as reducing reagents. A series of aromatic nitro compounds were reacted with sodium borohydride in the presence of the copper nanoparticles catalysts to afford the aromatic amino compounds in high yields. Additionally, the catalysts system can be recycled and maintain a high catalytic effect in the reduction of aromatic nitro compounds.
Haifeng Bian,Guoli Zhang,Qingxi Zhai,Yanyan Du,Yujie Ma,Beibei Yang,Shaochun Tang,Duan Bin,Xiangkang Meng,Hongbin Lu 한국공업화학회 2023 Journal of Industrial and Engineering Chemistry Vol.122 No.-
Stainless steel (SS) is a promising material for designing bipolar plates (BPs), but their further applicationis limited by serious corrosion problems in the acidic environment. Ti3C2Tx is expected to be used for SSBPs coatings, while galvanic corrosion will occur after the damage of Ti3C2Tx coating. Herein, a PPY/Ti3C2Tx-AE double-layer coating (DC) is well-designed and prepared on 304SS BP, which is composedof an inner electropolymerized PPY layer and an outer Ti3C2Tx-acrylic epoxy layer. When tested in0.2 M HCl solution, the corrosion potential and corrosion current density of the DC are 38 mV and0.00927 lA cm2 respectively, which are superior to those of the PPY coating and the Ti3C2Tx coating. Moreover, the DC presents the best long-term stability among the three coatings. The excellent corrosionresistance is attributed to the barrier and anodic protection effects as well as the solution of galvanic corrosion. The new coating system provides a new insight into the design of DC coatings of SS BPs.
Li Jiang,Junaid Ali Syed,Guoli Zhang,Yujie Ma,Jun Ma,Hongbin Lu,Xiangkang Meng 한국공업화학회 2019 Journal of Industrial and Engineering Chemistry Vol.80 No.-
The enhanced corrosion resistance with sustained conductivity are the prerequisites of stainless steelbipolar plates for practical application in proton exchange membrane fuel cell. Herein, we prepare aconductive polypyrrole-graphene oxide/polypyrrole-camphorsulfonic acid bilayer composite coating(PPY-GO/PPY-CSA) on 304 stainless steel bipolar plate by electrodeposition method. The electrochemicaltests are conducted in the simulated bipolar plates working environment, the potentiostatic polarizationresults imply that the PPY-GO/PPY-CSA composite coating offers stable corrosion resistance with lowpotentiostatic corrosion current density in comparison with the PPY-GO coating. The correspondingelectrochemical impedance spectroscopy measurements reveal that the PPY-GO/PPY-CSA compositecoating exhibits satisfactory conductivity and displays sustained anodic protection effect with superioranticorrosion performance during the 696 h of immersion. The excellent corrosion protection ability ofthe PPY-GO/PPY-CSA composite coating owing to its good adhesion strength, compact structure,satisfactory conductivity as well as the synergetic interaction between the two layers of the coating.