화학당량에 따른 우라니아의 핵분열 기체 확산 계수 측정
김희문(H. Kim),박광헌(K. Park),김봉구(B. G. Kim),주용선(Y. S. Choo),김건식(K. S. Kim),송근우(K.W. Song),홍권표(K. P. Hong),강영환(Y. H. Kang) 한국표면공학회 2002 한국표면공학회지 Vol.36 No.1
The diffusion coefficient of Xe-133 was obtained from an annealing test. The specimens were made from a UO₂ single crystal powder with natural enrichment. Weight and grain size were 300mg and 23(㎛, respectively. Oxygen potentials were obtained from an oxygen sensor. Released fractions were obtained from both results of gamma scans and quantitative analysis with MCNP code, The annealing test was performed at three temperatures at once. Diffusion coefficients of Xe-133 were calculated using slope of Booth theory in each O/M ratios. Activation energy and the pre-exponential factor of the diffusion coefficient were obtained. The activation energy of near stoichiomeric UO₂ is 310 kJ/mol. The measured values of near stoichiometric UO₂ are very close to other data available. Diffusion coefficients increase with hyper-stoichiometry, due to higher concentration of cation vacancies.