The corrosion failure analysis for the heating pipeline of apartment was performed. Usually, the heating pipe was layed in the concrete. However, it was known that the corrosion problems could be induced by admixture containing chlorine such as set accelerant. antifreezer and so on. Therefore the new construction method using stone ash instead of concrete was attempt to solve these problems. However water leaking accidents by corrosion occurred after 1 month from the completion of the apartment. In this paper, the reason of corrosion failure was investigated by the field study and laboratory analysis in many aspects.
무전해 Ni-P-X(X : $Al_2O_3$, Diamond) 복합도금층의 내마모성
김만,장도연,노병호,한성호,이규환,Kim, Man,Jang, Do-Yeon,No, Byeong-Ho,Han, Seong-Ho,Lee, Gyu-Hwan 한국기계연구원 1992 硏究論文集 Vol.22 No.-
The wear resistance of electroless Ni-P-X(X A1203, Diamond) composite coating layers was studied by Taber abrasion test technique. The wear resistance of composite coating layers was particularly relied upon the codeposited content, particle size and distribution of particles, and heat treatment of coating layers, as well as the electroless nickel plating bath employed. In this study, we lay emphasis on the wear resistance of electroless composite coating layers containing A1203 particles(1.2~Im, 6.7hIm, 11.5lIm, 20l1m) or diamond particles (1.5jim, 5gm). From the result of composite coating A1203 and diamond particles, the wear resistance of composite coating layers is as follows.