Microfibrillated Cellulose (MFC)와 중질탄산칼슘 (GCC)로 구성된 복합충전제를 이용한 종이 물성 향상
이중명(Jung Myoung Lee) 한국펄프·종이공학회 2016 펄프.종이技術 Vol.48 No.2
Increasing the amount of filler in paper is of high interest for paper industry while maintaining its key sheet quality properties. In this study, a MFC-GCC composite, made through a co-grinding NBSK (Northern bleached softwood kraft) pulp with a ground calcium carbonate (Intracarb 60), was used as a strength aid in paper in order to evaluate a potential cost reduction through filler increase without sacrificing paper quality. Handsheets were made of NBSK and/or eucalyptus pulp by using white water recirculation in a Tappi sheet former and was compared its properties without or with MFC additions at different filler levels. It was found that the MFC-GCC composite has a large surface area compared to the fiber, allowing the formation of more hydrogen bonds in the web, thus giving natural strength to the paper. Overall results are encouraging that the MFC-GCC composite allows papermaker to reduce basis weight and maintain critical sheet properties.
이중명(Jung Myoung Lee),안은별(Eun-Byeol Ahn),최효석(Hyo-Seok Choi),류지애(Ji-Ae Ryu),엄태진(Tae-Jin Eom) 한국펄프·종이공학회 2018 펄프.종이技術 Vol.50 No.5
We compared the characteristics of the three LMCFs (lignin rich micro-cellulosic fines) prepared by microwave irradiation, oil bath treatment and high pressure steam treatment from pine wood powder. The residual lignin contents of the LMCFs prepared by the three methods were almost similar but the yields were different. The microwave irradiation method hydrolyzed the pine wood powder more greatly compared to the other methods. So, the LMCFs prepared by microwave irradiation showed the lowest particle size and the least amount of hydroxyl groups but, showed the highest total crystallinity index. It was found that the LMCFs prepared by the three methods were similar in morphology but different in content of aromatic ring and carbonyl group. Based on these results, LMCFs could be produced efficiently depending on the manufacturing time, energy cost, and uniformity of micronized samples. It was concluded that the high pressure steam treatment method, which produces the uniform production of LMCFs as the purpose, is the optimum micronization method.
이중명(Jung Myoung Lee) 한국펄프·종이공학회 2018 펄프.종이技術 Vol.50 No.5
Microwave irradiation is one of pretreatment technologies in the biorefinery area. In this paper, we carried out a comparative study of the two distinct bio-based materials such as pine and eucalyptus as feedstocks subjected to a combination treatment of microwave irradiation and chemical micronization at a given reaction severity. The micronized residues were characterized in terms of reaction yields, residual lignin contents, sugar compositions, crystallinity, and dissolution behaviors on a aqueous Urea/NaOH solution. It was found that hardwood under the combination treatment of microwave and chemical micronization is more sensitive than softwood, resulted to a rapid decrease in yields, and residual lignin contents. The pronounced losses of hemicellulose and lignin in the hardwood made easily soluble in the aqueous Urea/NaOH solution.
< 전시-P-92 > 3D 프린터용 MFC 필라멘트의 제조
이중명 ( Jung Myoung Lee ),박지수 ( Ji-su Park ),안지효 ( Ji-hyo Ahn ),류지애 ( Ji-ae Ryu ),최사랑 ( Sa-rang Choi ),안은별 ( Eun-byeol Ahn ),서은지 한국목재공학회 2019 한국목재공학회 학술발표논문집 Vol.2019 No.1
3D 프린팅은 고체, 액체 및 분말 형태의 소재를 분사 혹은 적층하여 3차원 입체물을 제조하는 방식을 사용함에 따라, 지난 수 년 동안 산업분야 뿐만 아니라 일반 대중에 대한 3D 프린팅의 접근성이 크게 증가하였다. PLA(polylactic acid)는 우수한 기계적 성질, 재생 가능성, 생분해성 그리고 상대적으로 저렴한 비용을 가지고 있는 대표적인 바이오폴리머(biopolymer)로 3D 프린터용 필라멘트의 원료로 사용되며 석유화학 유래의 고분자 재료를 대체할 수 있는 대안으로 떠오르고 있다. 반면, PLA와 같은 생분해성 고분자는 충격저항이 낮고 밀도가 높기 때문에 포장 및 건축 사업과 같은 응용 분야에서 제한적으로 이용되고 있다. 따라서 본 연구는 MFC와 리그닌 첨가에 따른 3D 프린터용 필라멘트 물성을 비교하기 위해 수행되었다. MFC와 리그닌 모두 분말 형태로 제조하여 PLA 대비 0.5, 1, 2., 5 wt%로 투입하였으며 사용된 PLA는 진공 건조하여 사용하였다. 혼합 시료는 사출기의 150℃-160℃사이로 제조하여 인장강도를 측정하였으며 MFC와 리그닌의 분산성을 알아보기 위해 시료의 표면 및 단면을 관찰하였다. 그 결과 사출 온도에 따른 인장강도의 차이를 관찰하였으며 150℃에서 필라멘트를 제조하였을 때 MFC와 리그닌의 모든 조건에서 PLA만으로 제조한 필라멘트보다 높은 인장강도를 나타내었다. 또한 리그닌을 첨가함에 따라 인장강도가 감소하는 경향을 나타냈으며 MFC 첨가량에 따른 강도 차이는 그게 나타나지 않았다.
단순 아세틸화 공정에 의한 바이오매스의 치환도 상관관계 분석
이윤지 ( Yunji Lee ),김동현 ( Donghyun Kim ),엄태진 ( Tae-jin Eom ),이중명 ( Jung Myoung Lee ),김강재 ( Kang-jae Kim ) 한국목재공학회 2021 한국목재공학회 학술발표논문집 Vol.2021 No.2
기존의 아세틸화법은 목재로부터 최종산물에 이르기까지 수많은 공정을 필요로 하는 단점이 있으며, 펄프화 공정부터 시작하여 공정에 따라 셀룰로오스의 높은 순도가 요구되기도 하여 정제, 세척이 요구된다. 본 연구에서는, 고비점 용매인 glycol ether와 초산 및 무수초산을 용매로 하여 유기용매 프로세스 (organosolv process)를 거쳐 바이오매스로부터 단순화된 공정을 통해 다양한 조건의 아세틸화물을 제조하였다. 제작된 아세트화물은 Eberstadt 적정법에 의거하여 치환도를 측정할 수 있다. 하지만, Eberstadt 적정법은 시료의 치환도 분석까지 오랜 시간이 걸리고, 실험자에 따른 오차의 범위가 많이 발생되기 때문에 측정의 정확성과 효율성이 떨어지는 단점이 있다. 따라서, 본 연구에서는 단순 아세틸화 공정에 의해 제조된 시료의 치환도 측정에 있어서 Eberstadt 적정법과 더불어 IR 분석을 통한 치환도 계산법을 도입하여 두가지 치환도 측정법간의 상관관계를 알아보고자 하였다.