비고정성 연결장치의 위치에 따른 고정성 보철물의 응력분석
양홍서,Yang, Hong-So 대한치과보철학회 1996 대한치과보철학회지 Vol.34 No.1
Finite element models were constructed to analyze the mechanical behavior of a three unit fixed partial denture (FPD) with a 2nd premolar and 2nd molar abutment either employing a rigid and nonrigid connector. Gap elements were used to model the clearance space of the nonrigid connector. 1. High stress was generated in the FPD and supporting abutment around the rigid connector. 2. The pattern of stress and deflection is very similar between vertically and 20 degree mesially tilted nonrigid connector at the distal aspect of premolar abutment. 3. FPD with an inverted nonrigid connectors exhibited the worst undesirable mechanical stress states and deformations. 4. Nonrigid connector of normal orientation transmit the load to the abutment tooth, but inverted connector doesn't transmit the force.
Pd-Ag 및 Ni-Cr 합금의 금 전착이 전장 레진의 색채에 미치는 영향
양홍서,박영준,Yang, Hong-So,Park, Yeong-Joon 대한치과보철학회 1995 대한치과보철학회지 Vol.33 No.4
As the mechanical property of composite resin improved, composite resin has been widely used esthetic dentistry. In the field of esthetic dentistry, the color of prosthetic material is very important. The purpose of this study was to evaluate the color difference of specimens, by the types of alloys and gold electrodeposit. Experimental groups were as follows : Group Prec : Au-Pt alloy with no gold coating and no resin veneer. Group Semi : Pd-Ag alloy with no gold coating and no resin veneer. Group BAse : Ni-Cr alloy with no gold coating and no resin veneer. Group Gsem : Pd-Ag alloy with no gold coating and no resin veneer. Group Gbas : Ni-Cr alloy with no gold coating and no resin veneer. Group PreR : Resin veneer on the Pd-Ag alloy without gold coating. Group SemR : Resin veneer on the Pd-Ag alloy without gold coating. Group GbsR : Resin veneer on the Ni-Cr alloy with gold coating Group BasR : Resin veneer on the Ni-Cr alloy without gold coating. In this study, colors of metal surfaces and veneered resins were evaluated by the CIE $L^{*}a^{*}b$ system. The results obtained were as follows : 1. different alloy types and gold coating make the $L^{*}a^{*}b$ system. 2. The ${\Delta}E^*$ab value between groups semi and Base was less than 1.5 and there was no $a^*$ and $b^*$ value difference between groups Gsem and Gbas 3. The values of $L^*$ and $a^*$ ain groups GsemR and GbasR were so similar that the ${\Delta}E^*$ab value was as small as 0.58. 4. In resin specimens with gold coated semiprecious or base alloys showed yellower and redder deviation than the resin specimens with precious alloy. 5. The ${\Delta}E^*$ab values between goups PreR-GsemR and groups PreR-GbasR were as small as 2.68 and 2.22 respectively.
임플랜트와 자연치를 지대치로 한 고정성 보철물의 응력분석
양홍서,Yang Hong-So 대한치과보철학회 1993 대한치과보철학회지 Vol.31 No.3
A two dimensional finite element model was constructed to analyze the mechanical behavior of four unit fixed partial dentures (FPD) with a 2nd premolar abutment either employing a rigid or nonrigid connector and a 2nd molar abutment(Branemark implant, IMZ implants and natural tooth). Gap elements were used to model the clearance space of the nonrigid connectors and each components of implants. All FPDs with a implant abutment alter the patterns of stress distribution and displacement, but the magnitude of stress in the periodontium was not greater than that of the control. A FPD with rigid connectors induced the smaller stresses in the periodontium than a FPD with a nonrigid connector. A FPD with a Branemark implant exhibited the more desirable mechanical stress states as compared to the IMZ implants with IME or IMC.
금전착이 치과용 합금과 전장 레진간의 접착 강도에 미치는 영향
양홍서,박영준,Yang, Hong-So,Park, Yeong-Joon 대한치과보철학회 1997 대한치과보철학회지 Vol.35 No.1
The purpose of this experiment was to determind whether the gold electrodeposit on Pd-Ag and Ni-Cr alloys influences on the shear bond strength between veneering resin and silicoated metal surface. All the metal specimens were sandblasted with $250{\mu}m$ aluminum oxide and followed by silicoating and resin veneering. According to the metal surfaces to be veneered, experimental groups were divided into five. Group Prec : Gold alloy without gold coating Group Semi : Pd-Ag alloy without gold coating Group Base : Ni-Cr alloy without gold coating Group Semi-G : Pd-Ag alloy with gold coating Group Base-G : Ni-Cr alloy with gold coating All specimens were thermocycled 1,000 times at temperature of $5^{\circ}C$ to $55^{\circ}C$. The effects of gold electrodeposit on the shear bond strength between resin and metal interface were measured and fractured surface of the resin veneered metal was examined under the scaning electron microscope. The following results were obtained 1. The shear bond strength between resin and metal was $64.51{\pm}11.11Kg/cm^2$ in Prec group, $62.77{\pm}11.23Kg/cm^2$ in Base group and $58.97{\pm}9.20Kg/cm^2$ in Semi Group. There was no significant difference among the groups. 2. The bond strength in groups Semi-G and Base-G decreased about 17%, compared to the nongold-electrodeposit groups(Semi, Base). 3. In groups of non electrodeposit(Prec, Semi, Base), fracture occurred at the interface between alloy and resin, while fracture interface was observed between gold coating and resin in group Semi-G, and between metal substrate and gold coating in group Base-G respectively.
골결손부가 있는 발치직후 매식 임플란트에서 탈회동결건조골과 GTAM차단막이 골재생에 미치는 영향
김형수,양홍서,Kim, Hyeong-Soo,Yang, Hong-So 대한치과보철학회 1997 대한치과보철학회지 Vol.35 No.1
Dental implant may be immediately placed in postextraction socket which has alveolar bone defect. The purpose of this study was to compare the bone regeneration and bone quality around defects adjacent to implants that were placed into extraction sockets according to EFEB, GTAM barrier and GTAM barrier with DFDB. Mandibular P2, P3 and P4 were extracted bilaterally in dogs, and buccal defects were created about 4mm in depth and 3.3mm in width. Screwed pure titanium implants, 3.8mm in diameter and 10mm in length, were placed into the extraction sockets. The experimental groups were divided into four groups : the G group was covered with a GTAM barrier on the defective area, the D+G group was filled with DFEB and covered with a GTAM barrier, the D group was filled with DFDB only and the control group was sutured without any special treatment on the defective area. The experimental animals were killed after 12 weeks and specimens were prepared for light microscopic evaluation and fluorescent dyes were administered daily for 2 weeks after implantation, and injected on the 4th and 11th week for fluorescent microscopic examination to observe new bone formation and bone remodeling. The new Bone height of the buccal defect was measured and compared with the another for bone gain and the removal torque for the implant was measured for the comparison of bone density and bone-implant osseointegration. Results obtained were as follows : 1. Experimental groups showed bone regeneration in oder from D+G, G, D group and control. D+G and G group was significantly from D group and control(P<0.01). 2. In the defective area of control the regenerated alveolar bone showed poorly developed lamellated structure and fibrous tissue intervention into the bone-implant interface but the others showed well developed lamellated structure and osseointegration. 3. All implant groups showed no significaant difference in the removal torque for implant(P>0.05) These results suggest that immediate implants placed in defective sockets were successfully osseointegrated and utilizing placed in defective sockets were successfully osseointegrated and utilizing not only the combination of GTAM and DFDB but also only the GTAM was favorable for the predictable regeneration of the defective area.