RF 스퍼터법을 이용한 Li<sub>2</sub>MnSiO<sub>4</sub> 리튬 이차전지 양극활물질 박막 제조 및 전기화학적 특성
채수만,심중표,선호정,Chae, Suman,Shim, Joongpyo,Sun, Ho-Jung 한국전기전자재료학회 2017 전기전자재료학회논문지 Vol.30 No.7
In this study, $Li_2MnSiO_4$ cathode material and LiPON solid electrolyte were manufactured into thin films, and the possibility of their use in thin-film batteries was researched. When the RTP treatment was performed after $Li_2MnSiO_4$ cathode thin-film deposition on the SUS substrate by a sputtering method, a ${\beta}-Li_2MnSiO_4$ cathode thin film was successfully manufactured. The LiPON solid electrolyte was prepared by a reactive sputtering method using a $Li_3PO_4$ target and $N_2$ gas, and a homogeneous and flat thin film was deposited on a $Li_2MnSiO_4$ cathode thin film. In order to evaluate the electrochemical properties of the $Li_2MnSiO_4$ cathode thin films, coin cells using only a liquid electrolyte were prepared and the charge/discharge test was conducted. As a result, the amorphous thin film of RTP treated at $600^{\circ}C$ showed the highest initial discharge capacity of about $60{\mu}Ah/cm^2$. In cases of coin cells using liquid/solid double electrolyte, the discharge capacities of the $Li_2MnSiO_4$ cathode thin films were comparable to those without solid LiPON electrolyte. It was revealed that $Li_2MnSiO_4$ cathode thin films with LiPON solid electrolyte were applicable in thin film batteries.
리튬이차전지용 탄소 코팅된 Li<sub>2</sub>MnSiO<sub>4</sub> 양극활물질의 상형성 거동 및 충방전 특성
선호정,채수만,심중표,Sun, Ho-Jung,Chae, Suman,Shim, Joongpyo 한국전기화학회 2015 한국전기화학회지 Vol.18 No.4
Planetary ball mill과 고상반응법을 사용하여 실리케이트계 탄소 코팅된 $Li_2MnSiO_4$ 양극활물질 분말을 합성하였으며 충방전 특성을 조사하였다. 전기화학적 활성을 지니는 ${\beta}-Li_2MnSiO_4$ 상을 형성하기 위하여 하소 온도와 분위기를 조절하였으며 ${\beta}-Li_2MnSiO_4$ 단일상에 가까운 탄소 코팅된 $Li_2MnSiO_4$ 활물질 분말을 제조할 수 있었다. 합성된 분말은 100 nm 정도 크기의 1차 입자가 뭉쳐있는 2차 입자 형태를 보였다. $Li_2MnSiO_4$ 활물질에서 Li의 삽입/탈리가 가능하려면 탄소의 첨가가 필요하였으며, 4.8 wt%의 탄소가 코팅된 $Li_2MnSiO_4$ 활물질에서 초기용량 192 mAh/g를 얻을 수 있었다. Carbon-coated $Li_2MnSiO_4$ powders as the active materials for the cathode were synthesized by planetary ball milling and solid-state reaction, and their phase formation behavior and charge-discharge properties were investigated. Calcination temperature and atmosphere were controlled in order to obtain the ${\beta}-Li_2MnSiO_4$ phase, which was active electrochemically, and the carbon-coated $Li_2MnSiO_4$ active material powders with near single phase ${\beta}-Li_2MnSiO_4$ could be fabricated. The particles of the synthesized powders were secondary particles composed of primary ones of about 100 nm size. The carbon incorporation was essential to enable the Li ions to be inserted and extracted from $Li_2MnSiO_4$ active materials, and the initial capacity of 192 mAh/g could be obtained in the $Li_2MnSiO_4$ active materials with 4.8 wt% of carbon.