김기엽,류부형,강성화,이청,임기조,Kim, Ki-Yup,Ryu, Boo-Hyung,Kang, Seong-Hwa,Lee, Chung,Lim, Kee-Joe 한국전기전자재료학회 2000 전기전자재료학회논문지 Vol.13 No.11
Radiation effects on dielectric properties of low density polyethylene(LDPE) were investigated using the various measurements of FT-IR, gel content and elongation at break. FT-IR spectra showed that polar groups were comprised in LDPE due to radiation treatment. It was also confirmed that the formation of polar groups on LDPE caused the increased dielectric properties such as permittivity and tan $\delta$. However, in this study, any evidence of decreasing permittivity was not found although the morphological change of LDPE could be identified from the increasing gel content and the decreasing elongation.
김기엽,이청,류부형,Kim, Ki-Yup,Lee, Chung,Ryu, Boo-Hyung 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.11
This study has investigated radiation degradation of chloroprene rubber in the presence of some fire retardant. Ammonium polyphosphate, aluminium trihydroxide, magnesium hydroxide, calcium carbonate and antimony trioxide were selected as flame retardant. Samples were irradiated using a Co$^{60}$ ${\gamma}$ -ray and ray up to 2000 kGy at a dose rate of 5 kGy/hr in the presence of air atmosphere at room temperature. After irradiation, samples were assessed fire retardancy with electrical properties and mechanical properties. Some considerations concerning the effects of the fire retardants added to chloroprene rubber on the radiation and thermal stability of chloroprene rubber are presented. From fire retardancy with electrical and mechanical property measurements, it was found that addition of magnesium hydroxide resulted in maximum fire retardant effect.
열화에 따른 Polyetheretherketone의 유전완화특성
김기엽,이청,류부형,임기조,Kim, Ki-Yup,Lee, Chung,Ryu, Boo-Hyung,Lim, Kee-Joe 한국전기전자재료학회 2004 전기전자재료학회논문지 Vol.17 No.4
The dielectric properties of Y-ray irradiated and thermally aged polyetheretherketone (PEEK) have been investigated. Results of the temperature dependency of dielectric properties indicated that the glass transition temperature of aged PEEK increased as radiative and thermal ageing. The frequency dependency of dielectric properties implied that the magnitude of radiation and thermal induced dipoles, ions increased as radiative and thermal ageing. The values of relaxation intensity calculated using Cole-Cole's circular arc can be useful for evaluation of degradation level of PEEK.
$^{60}Co\;{\gamma}$-선 조사에 따른 클로프렌 고무의 열적 특성
김기엽,이청,류부형,Kim, Ki-Yup,Lee, Chung,Ryu, Boo-Hyung 한국안전학회 2003 한국안전학회지 Vol.18 No.4
The thermal properties of chloroprene rubber (CR) with $^{60}Co\;{\gamma}$-ray irradiation has been investigated. The prepared CR was irradiated up to 1000kGy radiation dose by $^{60}Co\;{\gamma}$-ray and the radiation degradation of CR was investigated by thermogravimetric analysis and differential acanning calorimetry. Dynamic mechanical properties measurement and FT-IR observation are carried out as well. From these analyses results, the glass transition temperature($T_g$), decomposition onset temperature(DOT), oxidative induction time(OIT), the peak temperature of loss modulus and mechanical tan ${\delta}$ values were compared for the radiation degradation level of CR. The tendency between $T_g$ and peak temperature of loss modulus and mechanical tan ${\delta}$ agreed well with radiation doses. Decomposition temperature, OIT and DOT showed the same tendencies as increasing radiation doses. It was verified that these analyses are available to estimate the degradation level of CR.
Flame Retardancy and Electrical/Mechanical Properties of LDPF/EVA Blend
류부형,이청,김기엽,Ryu, Boo-Hyung,Lee, Chung,Kim, Ki-Yup The Korean Society of Safety 2008 한국안전학회지 Vol.23 No.4
In this research, magnesium hydroxide as a flame retardant agents and zinc borate as a synergist were mixed with LDPF/EVA blended samples, in order to improve their flame retardancy. We attempted to select the best mixing ratio of the LDPF/EVA blend and the optimum amount of magnesium hydroxide and zinc borate by the comparison and analysis of the flame retardancy, the electrical properties such as the volume resistivity and dielectric loss tangent, and the mechanical properties such as the tensile strength and elongation at break. Particularly, specimen which is the 6phr of zinc borate and 10phr of magnesium hydroxide 70/30phr adding to the LDPF/EVA blended samples has been most excellent in flame retardancy and electrical/mechanical properties. 본 연구에서는 저밀도 폴리에틸렌과 에털렌 비닐 아세테이트 블렌드(LDPF/EVA)의 난연성을 향상시키기 위해 난연제인 수산화 마그네슘과 난연상승보조제인 zinc borate를 첨가한 후, 난연성과 체적저항률, 유전정접, 교류 절연파괴강도 등의 전기적 특성, 인장강도 및 연신율 등의 가계적 특성을 비교 분석하여 가장 우수한 LDPF/EVA 블렌드의 혼합비 및 적절한 $Mg(OH)_2$의 zinc borate의 첨가량을 선정하고자 하였다. 혼합비 70/30phr의 LDPF/EVA 블렌드에 10phr의 $Mg(OH)_2$와 6phr 정도의 zinc borate를 첨가한 시편에서 가장 우수한 난연성 및 전기/기계적 특성을 나타내었다.
Epoxy-Methacrylate Prepolymer의 合成 및 그의 單位體 混合物의 電子線硬化
변형직,박완빈,김기엽,최규석,Pyun Hyung-Chick,Park Wan-Bin,Kim Ki-Yup,Choi Kyu-Suck 대한화학회 1977 대한화학회지 Vol.21 No.4
메타크릴酸과 diglycidyl ether 型 低分子量의 에폭시樹脂로부터 에폭시樹脂의 dimethacrylate를 合成하였으며 이 prepolymer와 단위체인 스티렌 및 polyethyleneglycol dimethacrylate 混合物의 電子線硬化에 關하여 檢討하였다. 에스테르化反應은 메타크릴酸에 對하여 約 250∼300ppm以上의 hydroquinone과 $1{\%}$(wt) 以下의 triethanolamine의 添加로서 거의 定量的으로 進行되었다. 空氣中에서 행한 硬化에 있어서는 단위체 濃度10 ∼ $30{\%}$에서 最高의 겔分率을 나타내었으며 겔化速度는 prepolymer의 未反應 에폭시基와 酸의 存在에 의하여 減少되었고 polyethyleneglycol dimethacrylate內의 polyethyleneglycol의 重合度가 增加함에 따라 增加하였다. 窒氣中과 空氣中에서 겔化速度는 별다른 差異가 없었으나 生成物 性質의 差異로 보아 硬化時의 酸素의 影響은 상당히 컸으며 polyethyleneglycol dimethacrylate類를 단위체로 使用時는 더욱 그러하였다. Epoxy-methacrylate prepolymer was synthesized from methacrylic acid and a diglycidyl ether type low molecular weight epoxy resin, and the electron beam curing of the prepolymer was studied using styrene and polyethyleneglycol dimethacrylates as comonomers. The esterification was carried out quantitatively without any side reaction adding more than 250∼300ppm hydroquinone and less than $1{\%}$ (wt) triethanolamine by wt. of methacrylate acid, respectively. In the radiation curing under air atmosphere, the maximum gel fraction was observed at 10∼$30{\%}$ monomer contents. The rate of gel formation was decreased by the presence of unreacted epoxy group and acid in the prepolymer and increased with increasing degree of polymerization of polyethyleneglycol block in the dimethacrylates. Considerable oxygen effect in the curing, particularly when polyethyleneglycol dimethacrylate was used as a comonomer, was recognized through the differences of the product properties, though no remarkable differences were found in the rate of gel formation in air and nitrogen atmosphere.