Mg 첨가에 따른 A356 합금의 열처리 및 기계적 특성 변화
조재찬 ( Jae-chan Jo ),김광삼 ( Kwang-sam Kim ),임인택 ( In-taek Im ),김대환 ( Dae-hwan Kim ),심성용 ( Sung-yong Shim ),임수근 ( Su-gun Lim ) 한국주조공학회 2016 한국주조공학회지 Vol.36 No.6
The effects of Mg addition on heat treatment and mechanical properties of A356 alloy were investigated. With increased amounts of Mg addition to A356 alloy, the grain size decreased and eutectic Si was refined. And, this process can improve the mechanical properties. Solid solution heat treatment causes the spheroidizing of eutectic Si. In this study, although eutectic Si was refined with Mg addition, solid solution time increased from 2 hours to 6 hours with Mg addition, and aging time also increased, from 4 hours to 8 hours. After heat treatment, Mg2Si remained in a formation of Chinese script. And, Chinese script Mg2Si formed with Mg addition caused a reduction of the elongation of the alloys according to the stress concentration.
이용철(Yong-Chul Lee),김광삼(Kwang-Sam Kim),곽태수(Tae-Soo Kwak),이종열(Jong-Ryul Lee) 한국기계가공학회 2013 한국기계가공학회지 Vol.12 No.3
This study has focused on transparency recovering of the polycarbonate by polishing its surface for recycling. The polycarbonate has many properties such as excellent mechanical strength, electrical insulating, superior heat resistance to other plastic material and especially good transparency. It has been used as barrier for the traffic noise at the roadside and the greenhouse for the palm house. But the polycarbonate has changed slightly as time goes by 10 years because of exposure to the strong sunlight and oxidization in the atmosphere, as result has lost its transparency. Magnetic assisted polishing has been utilized as an effective polishing method to recover the transparency of polycarbonate. The polycarbonate which has been used for 10 years was adopted as the sample. The first surface roughness of the sample was 1.23μmRa, 7.5μmRz(DIN) respectively. In the experimental results, it showed that the surface roughness of the polished sample improved 0.013μmRa, 0.08μmRz(DIN) from the first surface roughness respectively. The surface roughness get almost back again by magnetic assisted polishing. These results also showed that the magnetic assisted polishing was efficient machining method to reuse the polycarbonate material.
Al-8.7Zn-2.8Mg-2.6Cu+0.1wt.%Sc Al 합금 압출재의 시효 거동 및 기계적 성질
김광삼,심성용,임수근,이상용 慶尙大學校 經營行政大學院 2004 工學硏究院論文集 Vol.20 No.-
7000계 알루미늄 합금은 시효경화에 의해 기계적 성질이 크게 향상됨으로 항공기 등 수송기기의 구조재료로서 이용되고 있으며, 합금이 개발된 이후 지속적인 성능향상을 위한 연구가 진행중이다. Al 합금에 있어 Sc 첨가는 Al_(3)Sc 상의 생성에 의한 결정립 미세화 및 분산 강화에 의해 효과적으로 강도를 향상 시킬 수 있다. 따라서 본 연구에서는 Al-8.7Zn-2.8Mg-2.6Cu+0.1wt.%Sc 합금 압출제를 이용하여 시효 열처리를 실시하여 시효 거동과 기계적 성질을 조사하였으며, 열처리에 따른 기계적 성질을 조사하였다. 압출재의 미세 조직 관찰 결과 Al_(3)Sc상이 기지 전반에 압출 방향으로 분포되어 있음을 알 수 있었고, 시효 거동 관찰 결과 최대경도 지점이 2400분에서 나타났으며, 시효 경화성 또한 기존의 Al7075 합금 보다 우수하였으며, 강도 증가에 있어서도 T6 처리한 경우 인장강도 657MPa로 나타났으며, 연신율의 경우 5%이었다.