고로슬래그 미분말의 산지 및 치환율 변화가 순환잔골재 사용 시멘트 모르타르의 특성에 미치는 영향
한천구,자오양 한국건축시공학회 2015 한국건축시공학회지 Vol.15 No.3
In this study, the quality of blast furnace slag and the engineering properties of recycled aggregate based mortarwith variable replacement of blast furnace slag have been focused. Blast furnace slag(BS) manufactured in variousareas in Korea were prepared for this study. For the investigation results, 4 types(among the all of 9 types) of theexperimental results were identified as below the standard level when using blast furnace slag chosen from differentfactories. Especially the particle size of the blast furnace slag was considered as the largest problem. When using BSin the recycled aggregates based mortar, the increase amount of blast furnace slag, increased the fluidity but delayedthe setting time and decreased strength at early age. Based on the relationship of the amount of BS and theengineering properties of mortar, this study found that the amount of SO3 and L.O.I affect the setting time, 3 daysstrength and 91 days strength to the certain standard level. 본 연구에서는 우리나라에서 생산되는 고로슬래그 미분말(BS)의 품질특성과 BS의 치환율 변화가 순환골재 사용시멘트 모르타르의 공학적 특성에 미치는 영향 및 BS 품질특성치와 모르타르의 공학적 특성치간의 상관성을 분석하고자 하였다. 분석결과 먼저 BS 품질특성은 9개 항목 중4개 항목에서 불만족하는 공장이 존재하였는데, 이중에서도 분말도의 개선이 제일 중요하게 요구되었다. 또한, BS의 치환율이 증가할수록 순환골재사용 시멘트모르타르의유동성은 증가하였으나 응결지연, 초기강도가 저하하는문제는 존재하였으나, 단 잠재수경성반응으로 후기재령에서는 증가하였다. BS의 품질특성치와 시멘트 모르타르의공학적 특성치간의 관계에서 이수석고와 관련하는 SO3 및L.O.I는 응결시간, 3 및 91일 압축강도와 미약하지만 어느 정도 상관성이 있는 것으로 분석되었다.
콘크리트의 고강도화에 관한 제안 ( A Proposal on High Strength Concrete Manufacture )
한천구 대한건축학회 1981 建築 Vol.25 No.4
본 고찰은 콘크리트를 고강도화하기 위한 방안으로서 재료에 관한 선정, 혼합 및 타설, 양성, 계획 등으로 분류하고, 이에 관한 이용 및 실무에 대한 검토를 하고자 한다.
한천구 대한건축학회 1983 建築 Vol.27 No.2
본연구는 섬유의 여러 종류중 가장 호율적이라고 알려진 강섬유 (Steel fiber)에 관한 예비실험으로서는 물.시멘트비, 재령, 사용량등 일반적인 섬유보강 콘크리트의 특성을 규명하도록 계획하였고, 본실험에서는 예비실험에 근거하어 섬유의 형태에 관한 제변수에 따라 인장강도에 미치는 영향을 중점적으로 분석하고자 하였다. 그리고 압축강도및 탄성계수에 관하여도 실험하여 비교 분석하였다.
한천구 대한건축학회 1984 建築 Vol.28 No.2
본 연구는 고갈골재자원 대책의 일환으로 천연강모래 강자갈과 쇄석 및 백토(일명 마사토)를 상호변화 조합시켜 백토및 쇄석을 사용한 콘크리트의 활용성을 구명하고 아울러 경제성도 분석하도록 실험계획 하였다.
Mock-Up 시험에 의한 고성능 콘크리트의 수축특성 분석
한천구,강수태,고경택,한창평 한국구조물진단유지관리공학회 2006 한국구조물진단유지관리공학회 논문집 Vol.10 No.5
본 연구는 개발된 저수축 고성능 콘크리트를 대상으로 모의부재 시험체에 있어서 콘크리트의 기초적 물성과 수축특성에 대하여 검토한 것이다. 실험연구 결과, 콘크리트의 배합특성으로 제안 배합은 목표 슬럼프플로우 및 목표 공기량을 만족하기 위해 SP제량 증가, AE제량 감소의 배합보정이 필요하였다. 응결시간은 제안 배합이 8시간 정도 빠르게 나타났으며, 굳은 콘크리트의 압축강도는 60MPa 이상의 고강도로 나타냈다. 수축특성으로 제안 배합 자기수축의 경우 플레인 배합 자기수축에 비해 50% 정도 저감되었고, 제안 배합의 중심부 건조수축은 수분발산이 없는 것에 기인하여 자기수축과 유사한 경향이었으나, 표면부는 크게 수축하였다. 단, 철근배근 시험체인 경우는 철근구속에 의해 내부 및 표면의 수축량이 작게 나타났다. This paper investigates the fundamental properties and shrinkage characteristics of low shrinkage high performance concrete(LSHPC), using mock-up specimens. According to the test results, the most suitable mix proportions of LSHPC need a higher dosage of SP agent and AE agent, in order to obtain the target of slump flow and air content. This is due to reduce fluidity and air content respectively. It also presented earlier setting time than control concrete by 6 hours and exhibited compressive strength of 60MPa at age 28 days. Autogenous shrinkage of LSHPC was the half of the value of control concrete. Drying shrinkage of center section of LSHPC showed similar tendency with autogenous shrinkage, because of no internal moisture movement, while surface section had larger drying shrinkage. The specimen with embedded reinforcing bar had smaller deformation owing to confinement of reinforcing bar.
알루미늄 거푸집 표면코팅재가 콘크리트 표면품질에 미치는 영향
한천구,박재순 한국건축시공학회 2010 한국건축시공학회지 Vol.10 No.3
This study is to analyze the effects of aluminum form surface coating material on surface quality of concrete. When observing the surface quality of concrete affected by the change of aluminum form surface coating material,in general, as the number of use of the coating material increased, the surface quality of concrete decreased and good surface quality was shown in plywood (hereinafter PW). For epoxy (hereinafter EP) resin, when applying form remover, good surface quality was shown. For the surface roughness of concrete by the application form oil of form remover and the number of use of the coating material, as the number of use increased, highest surface roughness value was shown which meant the leveling was bad, but the surface roughness value in EP and PW was the lowest. Just for EP, when applying form remover, surface roughness value was low. For the number of void for concrete by the application of form remover and the number of use of the coating material, In general, the number of void which was generated when applying form oil the remover decreased. 본 연구는 알루미늄 거푸집 표면코팅재가 콘크리트 표면품질에 미치는 영향에 대하여 분석한 것이다. 콘크리트 표면형상에미치는 알루미늄 거푸집 표면코팅재 변화의 영향에 따른 콘크리트 표면의 육안관찰시 전반적으로 전용횟수가 증가함에 따라 표면품질은 저하하는 것으로 나타났고, 치장합판(Plywood이하: PW)이 우수한 표면품질을 나타내었다. 에폭시(Epoxy :이하 EP)수지의 경우는 박리제를 도포하였을 시 표면품질이 우수한 것으로 나타났다. 박리제 도포여부 및 전용횟수에 따른 콘크리트의표면조도는 전용횟수가 증가함에 따라 가장 높은 표면조도 값을 나타내어 평활성이 불량한 것으로 나타났지만, EP와 PW의 표면조도 값은 가장 우수한 것으로 나타났다. 다만 EP의 경우는 박리제를 도포할 경우 표면조도 값이 낮게 나타났다. 박리제 도포여부 및 전용횟수에 따른 콘크리트의 공극갯수는 전반적으로 박리제를 도포할시 저감하는 것으로 나타났다.