보수재료로서 EVA 에멀젼과 고로슬래그 미분말 및 플라이애쉬를 혼입한 폴리머 시멘트 모르타르의 인장․접착특성
조영국 대한건축학회 2019 大韓建築學會論文集 : 構造系 Vol.35 No.11
The purpose of this study is to evaluate the effect of admixtures as blast-furnace slag(BF) and fly ash(FA) on tensile and adhesive propertiesof polymer cement mortar(PCM) with EVA emulsion. The test specimens are prepared with five polymer-cement ratio(P/C) and fiveadmixture contents, and tested for tensile strength and adhesion in tension. From the test results, the tensile strength and adhesion in tensioncould be improved by an appropriate combination of P/C and admixture contents. In particular, the maximum of tensile strength of PCMwith P/C 10% and BF content of 10% is 4.70MPa which is about 1.55 times higher than that of plain mortar, and about 1.22 times that ofPCM that does not contain any mixture. The ratio of adhesion in tension to tensile strength of PCM with admixtures averaged 55.8%. It isalso apparent that admixture contents of 5% or 10% could be proposed for improvement of tensile strength and adhesion in tension of PCM. 본 연구는 EVA 에멀젼 기반 폴리머 시멘트 모르타르에 혼화재로서 고로슬래그 미분말과 플라이애쉬를 혼입하여 인장 및 접착특성을 평가하고자 하였다. 폴리머 시멘트 모르타르(PCM)는 5가지 폴리머 시멘트비와 5가지의 혼화재 혼입율을 달리하여 제작하였으며, 인장강도 및 인장접착강도 시험을 실시하였다. 연구결과, 강도개선은 P/C와 혼화재의 혼입율의 적절한 조합에 의해 효과를 얻을 수 있었으며, P/C 10%, 고로슬래그 10%를 혼입한 PCM의 최대 인장강도는 4.70MPa로 이는 보통시멘트 모르타르의 1.55배, 혼화재를 혼입하지 않은 PCM(P/C 10%)의 1,22배 값이다. 또한 PCM의 인장강도에 대한 인장접착강도비는 평균 55.8%를 나타냈다. 본 연구를 통하여 PCM의 인장강도 및 인장접착강도의 개선을 위해 혼화재 혼입율 5% 또는 10%를 제안할 수 있었다.
발생중인 Chick Wingbud 에서 Transforming Growth Factor β 유전자의 발현
조영국,김원선 한국유전학회 1995 Genes & Genomics Vol.17 No.1
In the developing chick embryos, several kinds of growth factors are known to play some major roles in the process of pattern formation and tissue differentiation. The present study was performed to examine the expression profile of transforming growth factor β's (TGF-β) in the early phase of chick wing development. The level of TGF-β1 and TGF-β2 gene expression increased with the advancing stages of chick wing development even though the amount of increase was not profound. In the case of TGF-β3, the level of gene expression at 5 days post-incubation was somewhat lower than that at 4 days post-incubation while the level increased again at 6 days post-incubation. Among the three TGF-β's, the level of TGF-β2 expression was most strong while the level of TGF-β1 expression was most weak. Examination of spatial expression pattern of TGF-β2 in the developing wingbud revealed that the expression was high at the region of apical ectodermal ridge at 4-5 days post-incubation, and, in the anterior and posterior necrotic zones, the signal intensity became strong with advancing developmental stages. The results obtained in the present study suggest that TGF-β's play some role(s) in the wing pattern formation, especially during early phase of chick wing development.
폴리머 시멘트 슬러리 도장철근의 부착강도에 미치는 도장재 배합과 도장두께의 영향
조영국,박동열,장길수,Jo, Young-Kug,Park, Dong-Yeol,Jang, Gil-Su 대한건축학회 2011 대한건축학회논문집 Vol.27 No.6
In general, polymer cement slurry(PCS) that is made from organic polymer dispersion and cement has good adhesion to steel and cement concrete, waterproofness and acid resistance due to being of polymer films formed in cement slurry. The purpose of this study is to evaluate the effects of the mix proportions and coating thickness on the bond strength of coated rebar by PCS. The test pieces are prepared with two types of polymer dispersions such as St/BA and EVA, four polymer-cement ratios, two types of cement and four types of coating thickness, and tested for the bond strength test. From the test results, bond strength of PCS-coated rebar with St/BA and EVA is better than that of plain rebar and epoxy-coated rebar. In general, it is also high bond strength at polymer-cement ratios of 80% or more, and coating thickness of $100{\mu}m$. The maximum bond strength of PCS-coated rebar with ultra high-early strength cement and St/BA at polymer-cement ratio of 80%, and coating thickness of $100{\mu}m$ is about 1.5 and 1.6 times respectively, the strength of plain rebar and epoxy-coated rebar. It is apparent that the choice of polymer type, cement type, polymer-cement ratio and coating thickness is important to improve the bond strength of PCS-coated rebar to cement concrete.
고로 슬래그 시멘트 페이스트 내 자유염화물량과 물가용성 염화물량 평가에 관한 연구
조영국,소승영 한국건축시공학회 2004 한국건축시공학회지 Vol.4 No.4
The purpose of this paper is to compare free-chloride content with water-soluble chloride in blast furnace cement(BSC) paste. The content of free-chloride in cement paste measured by pore solution analysis and water-soluble chloride measured by ASTM. The result of this study are as follows :
건조과정에 있어서 폴리머 시멘트 모르터의 수분확산에 관한 연구
조영국,소양섭 한국콘크리트학회 1996 콘크리트학회지 Vol.8 No.5
콘크리트 및 모르터중의 수분의 확산 거동은 탄성계수, 크리프, 건축수축 등의 역학적 성질에 큰 영향을 미친다. 일반적으로 건조과정에서 폴리머 시멘트 콘크리트와 모르터의 수분의 증발에 의한 중량감소는 내부의 폴리머 필름형성에 의한 보수효과로 보통 시멘트 콘크리트 및 모르터에 비해 월등히 적다. 본 연구는 폴리머 시멘트 모르터 내부의 수분의 확산 과정을 확인하기 위하여 3종류의 폴리머디스퍼션과 에폭시 수지를 사용한 폴리머 시멘트 모르터를 제조하여 건조조건에 따른 수분의 확산 정도를 확산계수로 평가하였다. 실험결과, 폴리머 시멘트 모르터의 수분확산은 보통 시멘트 모르터에 비하여 아주 적었으며 폴리머 시멘트비에 따라 감소하였다. Diffusion of water in hardened cement concrete and mortar influences on the dry shrinkage. creep. modulus of' elasticity, etc. In general, water loss through drying process in polymer-modified concrete and mortar is small compared with that of unmodified concrete and mortar due to the films formed by polymer as cement modifieder. The purpose of this study is to investigate the diffusion process of water in the polymer-modified mortars. The polymer-modified mortars using three polymer dispersions and epoxy resin are prepared with various polymer-cement ratios, and water diffusion coefficient of polymer-modified mortars according to inside water content is calculated. From the test results, the water diffusion coefficient of polymer modified mortars i s smaller than that of unmodified mortars and decreases with increasing polymer cement ratio.
경화제 무첨가 에폭시 시멘트 모르터 및 콘크리트의 역학적 성질
조영국,소양섭 한국콘크리트학회 1996 콘크리트학회지 Vol.8 No.3
경화제 무첨가 에폭시 수지는 시멘트 모르터 및 콘크리트 중에 시멘트 수화에 의해 생성된 수산화물(예를 들어 $Ca(OH)_2$)의 존재하에서 경화할 수 있음에 착안하여, 본 연구는 경화제를 첨가하지 않은 에폭시 시멘트 모르터 및 콘크리트의 배합비 변화에 따른 역학적 성질을 파악하고 종래의 경화제 첨가 에폭시 시멘트 모르터 및 콘크리트와 비교하여 성능과 경제적인 면에서 우수한 경화제 무첨가 에폭시 시멘트 모르터 및 콘크리트를 개발하기 위하여 연구되었다. 연구 결과 종래의 경화제 첨가 에폭시 시멘트 모르터 및 콘크리트와 비교하여 10-20%의 낮은 폴리머 시멘트 비에서 우수한 역학적 성질을 가진 경화제 무첨가 에폭시 시멘트 모르터 및 콘크리트를 개발할 수 있다. The purpose of this study is to develop the epoxy-modified mortars and concretes without hardener having a good balance between performance and cost. In this study, the epoxy-modified and concretes without and with the hardener are prepared with various polymer-cement ratios, and tested for the mechanical properties of the epoxy-modified mortars and concretes without and with the hardener. From the test results, the epoxy-modified mortars and concretes without the hardener having an excellent mechanical properties are developed at low polymer-cement ratios of 10 to 20% compared with those of conventional epoxy-modified mortars and concretes with the hardener.