http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
겹치기 마찰교반접합된 Inconel 600/SS 400 합금의 미세조직과 기계적 특성 평가
송국현,Song, Kuk-Hyun,Nakata, Kazuhiro 한국재료학회 2012 한국재료학회지 Vol.22 No.3
The microstructures and mechanical properties of friction stir welded lap joints of Inconel 600 and SS 400 were evaluated; friction stir welding was carried out at a tool rotation speed of 200 rpm and welding speed of 100 mm/min. Electron back-scattering diffraction and transmission electron microscopy were introduced to analyze the grain boundary characteristics and the precipitates, respectively. Application of friction stir welding was notably effective at reducing the grain size of the stir zone. As a result, the reduced average grain size of Inconel 600 ranged from $20{\mu}m$ in the base material to $8.5{\mu}m$ in the stir zone. The joint interface between Inconel 600 and SS 400 showed a sound weld without voids and cracks, and MC carbides with a size of around 50 nm were partially formed at the Inconel 600 area of lap joint interface. However, the intermetallic compounds that lead to mechanical property degradation of the welds were not formed at the joint interface. Also, a hook, along the Inconel 600 alloy from SS 400, was formed at the advancing side, which directly brought about an increase in the peel strength. In this study, we systematically discussed the evolution of microstructures and mechanical properties of the friction stir lap joint between Inconel 600 and SS 400.
산화물 반도체의 결정입도가 가스감도와 표면특성에 미치는 영향
송국현,박순자,Song, Guk-Hyeon,Park, Sun-Ja 한국재료학회 1993 한국재료학회지 Vol.3 No.4
The effects of $SnO_2$ crystallite size on the powder characteristics, the resistance in air and the sensitivity to 0.5 vol % $H_2$, CO-air mixture were observed. The size of SnO, powder was controlled by calcining temperature variation ($500^{\circ}C$ ~$1100^{\circ}C$) of $\alpha$-stannic acid fabricated from $SnCl_4 \cdot xH_2O$. Its crystallite size. evaluated from TEM image, was in the range of 8-54nm. With the reduction of crystallite size, the adsoption peak of $H_2O$ on FTIR curve became more clear while the lattice parameters were invariable. As the crystallite size decreased, with elements of thick film, the temperatures showing a minimum resistance in air and a maximum sensitivity to H, gas reduced. The temperature variations were assigned to the changes of activation energy of the active adsorbates, and it was suggested that the decrease of activation energy can be one of the reasons for the' sensitivity increase with the' fine powder. Hydroxide법으로 ${\alpha}$-주산산(stannic acid)을 만든후, 하고온도를 $500^{\circ}C$~$1100^{\circ}C$로 조정하여 일차입자(Crystallite)크기가 8-54nm인 $SnO_2$ 분말을 제작하였다. 분말의 입자(drystalite)클기에 따른 분말특성와 $H_2$, CO가스(0.5v/o)에 대한 감응성 미치공기중에서의 저상변화특성에 미치는 영향을 조사하였다. 입자크기가 감소함에 따라, 분말의 FTIR 흡습특성은 증가하였으나, 격자상수는 일정하였다. 후막소자에서, $H_2$가스에 대해 최대감도를 나타내는 온도와 공기중에서 최소저항을 나타내는 온도는 입자크기가 미세해짐에 따라 점차 낮아졌다. 최소저항점과 최대감도점의 온도저하를 산소흡착종의 활성화에너지의 감소라고 유추하였고, 이러한 에너지의 감소가 미세입자에 의한 감도향상요인 중의 한가지라고 제의하였다.
송국현,Song, Kuk-Hyun,Nakata, Kazuhiro 한국재료학회 2011 한국재료학회지 Vol.21 No.7
This study was carried out to evaluate the microstructures and mechanical properties of a friction stir welded Ni based alloy. Inconel 600 (single phase type) alloy was selected as an experimental material. For this material, friction stir welding (FSW) was performed at a constant tool rotation speed of 400 rpm and a welding speed of 150~200 mm/min by a FSW machine, and argon shielding gas was utilized to prevent surface oxidation of the weld material. At all conditions, sound friction stir welds without any weld defects were obtained. The electron back-scattered diffraction (EBSD) method was used to analyze the grain boundary character distributions (GBCDs) of the welds. As a result, dynamic recrystallization was observed at all conditions. In addition, grain refinement was achieved in the stir zone, gradually accelerating from 19 ${\mu}m$ in average grain size of the base material to 5.5 ${\mu}m$ (150 mm/min) and 4.1 ${\mu}m$ (200 mm/min) in the stir zone with increasing welding speed. Grain refinement also led to enhancement of the mechanical properties: the 200 mm/min friction stir welded zone showed 25% higher microhardness and 15% higher tensile strength relative to the base material.