C.H. Ting,S. Ramesh,C.Y. Tan,N.I. Zainal Abidin,W.D. Teng,I. Urriés,L.T. Bang 한양대학교 세라믹연구소 2017 Journal of Ceramic Processing Research Vol.18 No.8
In the present work, the effect of low temperature sintering, focusing on varying the sintering holding times on the mechanicalproperties, microstructure and low temperature degradation behavior of undoped and MnO2-doped Y-TZP ceramics wereinvestigated. Green samples were sintered at temperatures ranging from 1100 to 1250 oC at varying holding times rangingfrom 12 min. to 480 min. The sintered bodies were characterized in terms of bulk density, Vickers hardness, fracturetoughness, phase stability and grain size. The results indicated that the relative density of above 95%, Vickers hardness of 14GPa and fracture toughness of 5 MPam1/2 were obtained when sintered at lower sintering temperature (below 1250 oC) andlonger sintering times for MnO2-doped Y-TZP samples. Grain growth was marginal and the average grain size of all samplesranged between 0.14 and 0.28 µm. The results indicated that the grain growth kinetics was influenced mainly by the sinteringtemperature and not by the sintering holding time. The addition of MnO2 was found to be beneficial in enhancing densificationand mechanical properties of Y-TZP particularly at low sintering temperature of 1100 oC and low holding time of 12 min. Thelow-temperature degradation experiment conducted in superheated steam indicated that all the samples did not transformedto the monoclinic symmetry, attributed mainly to the lower grain size sintered at relatively low sintering temperatures
연관 검색어 추천
이 검색어로 많이 본 자료
활용도 높은 자료