Fu‑xiang Cao,Kun‑kun Deng,Cui‑ju Wang,Kai‑bo Nie,Wei Liang,Jian‑feng Fan 대한금속·재료학회 2021 METALS AND MATERIALS International Vol.27 No.12
The 10 μm 10 vol% SiCp/2024Al composites sheet was successfully fabricated by semi-solid stir casting followed withtwo-step deformation (extrusion and rolling). The two-step thermal deformation solves the sheet rolling formability of theSiCp/2024Al composites produced by stir casting. Compared with the SiCp/2024Al composites prepared by traditional powdermetallurgy, this paper innovatively studied the synergistic enhancement between CuAl2phase and SiCpon the mechanicalproperties. The result shows that the two-step deformation can significantly improve the uniformity of the distribution of SiCpand CuAl2phases. At the same time, the average size of the SiCpand CuAl2phase decreases after the two-step deformation. During the hot extrusion, SiCphas an obvious hindrance to the refinement of the CuAl2phase. Moreover, the SiCp/2024Alcomposites sheet exhibits excellent yield strength (295 MPa), ultimate tensile strength (489 MPa), and elongation (10.42%). The performance improvement of SiCp/2024Al after two-step thermal deformation is mainly attributed to the improvedinterface bonding strength of SiCp-2024 Al matrix, the refined SiCpand the more uniform distribution of SiCp.