Calciumsilicate의 생성반응에 미치는$ SO_3$의 영향(II)
임은극,박병철 한국세라믹학회 1984 한국세라믹학회지 Vol.21 No.2
In this study a comparative investigation for the effect of $K_2SO_4$ and $CaSO_4$ on the decomposition of $C_3S$ was made. When pure $C_3S$ which was synthesized in the laboratory was mixed with $K_2SO_4$ and oxides such as MgO $Al_2O_3$ and $Fe_2O_3$ and then reburned at the temperature range between 135$0^{\circ}C$ and 145$0^{\circ}C$ no decompo-sition occurred, But when $CaSO_4$ and $Fe_2O_3$ were added to $C_3S$ and then reburned at below 130$0^{\circ}C$ $C_3S$ was partly decomposed to $C_2S$and CaO composing $2C_2S$.$CaSO_4$ When $CaSO_4$ and $Al_2O_3$were added $C_3S$ was entirely decomposed to $C_2S$ and CaO at 1300~140$0^{\circ}C$ but it was not decomposed at 145$0^{\circ}C$.
-
Calciumsilicate의 생성반응에 미치는 $SO_3$ 영향(III)
임은극,박병철 한국세라믹학회 1984 한국세라믹학회지 Vol.21 No.3
In this study an investigation was made to determine optimum ratio between $SO_3$, MgO and $K_2O$ that maximizes $C_2S$ formation in Clinkering reaction Using response surface analysis method. It was proved that 1) Residual $K_2O$ int he clinker should be converted to $K_2SO_4$ because $K_2SO_4$ has less effect on the burnability than $K_2O$, 2) Optimum ratio if $SO_3$/K2O is 1.5, 3) Optimun balance between $CaSO_4$ and MgO is to be adjusted to such a level that w/o SO3=0.7(w/o MgO-2).4) In case of lack of $K_2O$ free CaO was minimized when $K_2SO_4$=2.3w/o and MgO=1.5w/o but if remaining $K_2O$ was 2w/o free CaI was minimized in the level that $K_2SO_4$=2.3w/o and MgO =1.5 w/o but if remaining $K_2O$ was 2 w/o free CaO was minimized in the level that $K_2SO_4$=4.5w/o and MgO =3.0 w/o.
-
김환,임은극,고정하,황규홍,Kim, Hwan,Lim, Eung-Keuk,Koh, Jeong-Kyu,Hwang, Kyu-Hong 한국세라믹학회 1984 한국세라믹학회지 Vol.21 No.3
The effect of tetragonal $ZrO_2$ phase on the mechanical behavior in 7 mole% calcia partially stabilized zirconia has been studied. The $ZrO_2$ powder containg 7 mole% CaO prepared by Hot Petroleum Drying Method calcined at 80$0^{\circ}C$ for 1 hour was nearly 100% tetragonal but as the calcining temperature increased certain amount of monoclinic phase appeared. The sintered specimen at 1$700^{\circ}C$ for 5 hours was aged at 130$0^{\circ}C$ for 0, 24, 48, 72 hours. X-ray diffraction data showed that in the aged specimen monoclinic tetragonal and cubic phase coexisted. The Kc value of aged specimen for 48 hr was about 4.5MN/m3/2 much greater than unaged sample. But aged for 72 hr the KiC value was decreased. The increasing of toughness in PSZ is based on the Stress-Induced Phase Transformation that is metastable tetra-gonal $ZrO_2$ changes t stable monoclinic phase within the stress field of crack and the mechanical fracture energy absorption is occured But in this case due to certain amount of tetragonal phase transformed to monoclinic phase during cooling the microcrack effect by transformation also considered. Trerefore both Stress-Induced Phase Transformation and inclusion induced microcracking effect contrbute to the increase of fracture toughness of 7 mole% CaO-$ZrO_2$ containing monoclinic and tetragnola phase simulataneously.