송연호,이철태 ( Yon Ho Song,Chul Tae Lee ) 한국공업화학회 1995 공업화학 Vol.6 No.1
금속황화물과 NH₄Cl의 반응에 대한 열역학적 계산과 실험적 연구가 염소화제로서 NH₄Cl의 타당성을 검토하기 위하여 수행되었다. 본 연구에서는 Ag₂S, As₂S₃, CdS, CuS, Cu₂S, FeS, HgS, MoS₂, Ni₃S₂, PbS, Sb₂S₃ 및 ZnS의 금속황화물을 NH₄Cl에 의하여 염소화시킨 결과 NH₄Cl이 이들 금속황화물의 좋은 대체 염소화제임을 알 수 있었다. Thermodynamic calculation and experimental investigation for the reaction between metal sulfides and NH₄Cl were carried out to test the feasibility of NH₄Cl as an alternative chlorination agent for the chlorination of metal sulfides. In this experiment, 12 metal sulfides such as Ag₂S, As₂S₃, CdS, CuS, Cu₂S, FeS, HgS, MoS₂, Ni₃S₂, PbS, Sb₂S₃ and ZnS were selected for this test As the results, NH₄Cl was acted as a good alternative chlorination agent for the chlorination of these metal sulfides.
송연호,오치훈,이철태 ( Yon Ho Song,Chi Hoon Oh,Chul Tae Lee ) 한국공업화학회 1996 공업화학 Vol.7 No.3
NH₄Cl을 염소화제로 사용하여 시약 PbS와 Pb함유 자연광물인 방연광의 염소화 반응에대해 조사하였다. 방연광의 적정 염소화 반응조건은 반응온도 425℃, 방연광에 대한 NH₄Cl의 무게비 4.0, 반응시간 2시간이었다. 이 조건하에서 방연광중의 PbS는 NH₄Cl에 의해 효과적으로 PbCl₂로 염소화되었으며 그 전화율은 90%였다. 방연광의 염소화 반응에서 염소화제로 사용한 NH₄Cl은 NH₃와 HCl로 효과적으로 분리되었으며 양론적으로 90%의 NH₃를 회수할 수 있었다. The chlorination of reagent PbS and natural ore galena with NH₄Cl was investigatedto find a new extraction metallurgical process of lead. The proper conditions for the chlorination of galena were that reaction temperature ; 425℃, NH₄Cl weight ratio to galena ; 4.0 and reaction time ; 2hrs. Under these conditions, PbS was successfully chlorinated to PbCl₂and the conversion was 90%. And also NH₄Cl was effectively decomposed and was separated NH₃and HCl. HCl was a chlorinating agent and 90% of NH₃was recovered through this chlorination reaction.
Hydrous Titanium Dioxide로부터 H<sup>+</sup>/Na<sup>+</sup>의 이온교환에 의한 티탄산나트륨의 합성 및 성전이
이진식,송연호,이철태,Lee, Jin-Sik,Song, Yon-Ho,Lee, Chul-Tae 한국공업화학회 1998 공업화학 Vol.9 No.4
Fibrous $Na_xTi_nO_{2n+1}$ whisker was prepared by $H^+/Na^+$ ion-exchange on layered hydrous titanium dioxide ($H_2Ti_4O_9{\cdot}nH_2O$). The ion-exchange reaction was proceeded at 0.5~2.0 M NaOH solution. In the ion-exchange at 2.0 M NaOH solution, 73% of sodium was exchanged and the prepared $Na_xTi_nO_{2n+1}$ whisker was a fibrous crystal of about $10{\sim}20{\mu}m$ of length and about $0.7{\mu}m$ of diameter. The phase transition of the ion-exchange phases identified by the thermal analysis. The result showed that the $Na_xTi_nO_{2n+1}$ whisker was decomposed into $Na_2Ti_6O_{13}$ and $TiO_2$ in the temperature of $200{\sim}600^{\circ}C$. 섬유상의 $Na_xTi_nO_{2n+1}$는 층상구조의 $H_2Ti_4O_9{\cdot}nH_2O$에대한 $H^+/Na^+$의 이온교환에 의해서 합성되었다. 이온교환 반응은 0.5~2.0 M NaOH 용액에서 이루어졌으며, 2.0 M NaOH의 용액에서 이온 교환할 때 73%가 치환되었다. 이 때 길이가 $10{\sim}20{\mu}m$이고 직경이 약 $0.7{\mu}m$인 비교적 균일한 형태의 섬유상을 얻을 수 있었다. 그리고 층상구조의 티탄산나트륨에 대한 상전이는 열분석을 통해 확인하였으며, 이 결과 $Na_xTi_nO_{2n+1}$ 섬유는 $200{\sim}600^{\circ}C$의 온도에서 $Na_2Ti_6O_{13}$과 $TiO_2$로 분해되었다.
송연호,홍정선,이철태 ( Yon Ho Song,Jung Seun Hong,Chul Tae Lee ) 한국공업화학회 1994 공업화학 Vol.5 No.6
기존의 자료로부터 얻을 수 있는 열역학적 계산에 의하면 금속 황화물을 염소가스에 의하여 금속 염화물로 얻을 수 있음을 알 수 있다. 실제로 AgS, AS₂S₃, CdS, CuS, Cu₂S, FeS, HgS, MoS₂, Ni₃S₂, PbS, Sb₂S₃, ZnS의 황화금속을 염소가스와 반응시켜 이를 열중량법에 의하여 고찰하였다. 이론적 계산이나 실험적 연구에서 황화물의 염소화 반응은 황화광물의 추출 야금 공정에 대한 좋은 대체 방법임을 알 수 있었다. Thermodynamic calculations have been made from existing literature data to show that it is reasonable to expect to recover metal chlorides from the chlorination of metal sulfides with chlorine gas. The reactions between 12 metal sulfides, such as, Ag₂S, As₂S₃, CdS, CuS, Cu₂S, FeS, HgS, MoS₂, Ni₃S₂, PbS, Sb₂S₃ and chlorine gas were investigated by means of thermogravimetric method. The theorical calculation and the experimental investigation showed that chlorination of sulfide is a better alternative process for the extraction metallurgical process of sulfide ores.
저품위 Bauxite로부터 고순도 Al<sub>2</sub>O<sub>3</sub>의 합성(II)
권긍택,송연호,이철태,Kwon, Kung-Taek,Song, Yon-Ho,Lee, Chul-Tae 한국공업화학회 1994 공업화학 Vol.5 No.4
A new process for the production of high purity ${\alpha}-Al_2O_3$ from ammonium aluminium sulfate solution abtained through the sulfation of low grade bauxite ore with $(NH_4)_2SO_4$, and leaching of the sulfated product was investigated. This process is consisted of solvent extraction for Fe component removal from ammonium aluminum sulfate solution and homogeneous precipitation of Al containing precipitate from the refined ammonium aluminium sulfate solution by using urea as precipitator. The optimum conditions of solvent extraction with Alamine 336 as extractant were shaking time of 4min, organic phase ratio to aqueous phase of 0.25. The types of precipitation products from this precipitation were amorphous alumina gel, pseudo-boehmite and crystalline boehmite in the lower temperature of $100^{\circ}C$, in the range from $125^{\circ}C$ to $150^{\circ}C$, and above $150^{\circ}C$, respectively. And also amorphous alumina gel hydrate in $1000^{\circ}C$ and crystalline boehmite in $1250^{\circ}C$ were tranfered to ${\alpha}-Al_2O_3$, respectively. This alumina was identified as ${\alpha}-Al_2O_3$ of purity 99.7%. $(NH_4)_2SO_4$와 저품위 bauxite의 황산화 반응에 따라 얻어진 ammonium aluminium sulfate로부터 수열균일침전을 통해 무정형 alumina gel수화물 및 결정형 boehmite를 합성하고 이로 부터 고순도 $Al_2O_3$를 제조하는 새로운 공정 개발을 시도하였다. 이 공정은 ammonium aluminium sulfate용액 중의 Fe 성분을 제거하기 위한 용매추출공정과 정제된 ammonium aluminium sulfate용액으로부터 균일침전에 의한 Al 함유 침전물의 생성에 관한 것으로 이루어져 있다. 추출제 Alamine 336에 의한 적절한 용매추출조건은 shaking time 4분, 수상에 대한 유기상의 비 0.25였다. Urea를 이용한 수열균일 침전반응은 Al 함유용액 중의 Al에 대한 urea의 당량비 6.0의 조건에서 반응온도 $100^{\circ}C$ 이하에서는 무정형 alumina gel 수화물, $120^{\circ}C$ 이상 $150^{\circ}C$ 이하에서는 pseudo boehmite 그리고 $150^{\circ}C$ 이상에서는 결정형 boehmite가 합성되었다. 이 합성된 무정형 alumina gel 수화물은 소성시간 2시간, 소성온도 $1000^{\circ}C$ 이상에서 그리고 결정형 boehnite는 소성시간 2시간, 소성온도 $1250^{\circ}C$ 이상에서 ${\alpha}-Al_2O_3$로 전이되며 얻어진 ${\alpha}-Al_2O_3$의 순도는 99.97%의 고순도였다.
오치훈 ( Chi Hoon Oh ),송연호 ( Yon Ho Song ),이철태 ( Chul Tae Lee ) 한국공업화학회 2003 공업화학 Vol.14 No.2
Self-propagating High Temperature Synthesis (SHS) 공정에 의해 MoSi_2를 합성하였다. MoSi_2 합성의 상용화 공정의 위해 Si의 원료로는 철강 참가용 Si괴를 사용하여 단일상의 MoSi_2를 얻을 수 있었으며, MoSi_2 합성을 위한 적정조건은 상대밀도 40%, Si의 입도 -325 mesh, Si/Mo의 몰비 2.2였다. MoSi_2 was synthesized by Self-propagating High Temperature Synthesis (SHS) process. Silicon bulk was selected as a Si source for commercial process of MoSi_2 synthesis and single phase MoSi_2 has been prepared. The optimal conditions of MoSi_2 synthesis were relative density, 40%; particle size of Si bulk, -.02 mesh; mole ratio of silicon to molybdenum, 2.2.
소성법에 의한 Li_(2)Ti_(3)O_(7)의 합성 및 리튬이차전지용 부극 물질로의 응용
송연호,이진식,이철태 조선대학교 생산기술연구소 1999 生産技術硏究 Vol.21 No.1
The ramsdellite, Li₂Ti₃O_(7) was prepared by reacting, in air, mixtures of Li₂CO₃ and TiO₂ by calcination at 1050℃, for 12 hrs and was examined a possibility to use as an anode material. Li₂Ti₃O_(7) showed a discharge capacity of 120~140 mAh/g with good cycle ability during the 20 charge/discharge cycles in a Li/1M LiPF6〔in EC-DEC (1:1 by volume)〕Li₂Ti₃O_(7) cell at a current density of 0.15 mA/㎠ and the voltage range 0.5 ~ 3.0V.