Photoluminescence과 Conductance 측정을 이용한 자외선 조사된 Ge첨가 다성분계 산화물 유리의 구조변화 관찰
이회관,오영석,강원호 단국대학교 2001 산업기술연구 Vol.2 No.-
Ge-doped multicomponent oxide glasses were prepared by a conventional melting method. The structural change around Ge ions was investigated by using PL(photoluminescence) and conductance(G). After UV irrdiation, the PL intensity decreased and the change were maintained at room temperature, but a photodarkened glass recovered near its original properties when it was heat-treated at 500℃ for several hours. The conductance of the irradiated sample decreased because the disorder in structure was happened by UV irradiation. These results can be explained a structural change were occurred at bonding structure between Ge ions and glass components.
높은 개구수를 갖는 다성분계 Glass Fiber의 제조 및 특성
이희관,오영석,이용수,강원호 단국대학교 신소재기술연구소 2002 신소재 Vol.11 No.-
광전자 기술의 발전 및 광 응용 분야의 확대에 따라 광전송장치 사용이 증가하고 있으며, 이에 따라 광원과 광link사이에 불일치로 나타나는 손실을 줄일 수 있고, 다량의 정보를 전송할 수 있는 개구수가 큰 fiber개발이 대두되고 있다. 이에 본 연구에서는 보다 높은 개구수(numerical aperature : N.A.)를 갖는 fiber 제조를 위하여 SiO_2, PbO를 주성분으로 하고 K_2O, Na_2O, B_2O_3, Al_2O_3 등의 산화물을 적량 배합함으로써 core-clad 유리의 제조 및 제조된 유리의 물성 평가를 하였으며, double crucible method를 이용하여 fiber를 제조하였다. 또한 제조된 fiber의 구조적 및 기계적 특성을 관찰하였다. It is increasing to uses of the photo transmission devices because of development in photoelectronic techniques and enlargement of photo application fields. Therefore, we need to the optical fiber to transmit lots of information and decrease optical loss. For high-numerical aperture optical fiber, in this study, main components are SiO_2, PbO and glass composition mix component oxide such as K_2O, Na_2O, B_2O_3, Al_2O_3, Also, the optical, mechanical, structural properties of manufactured glasses and fibers by double crucible method are investigated.