Sol-gel법으로 제조한 SrZrO₃ 피막의 접착강도 특성

예경환,송요승 한국항공대학교 항공우주산업기술연구소 2003 航空宇宙産業技術硏究所 硏究誌 Vol.13 No.-

SrZrO₃ resistive oxide barriers on Ag sheathed Bi2223 tapes were prepared by the sol-gel and dip coating method to reduce AC coupling loss. The performance of the dip-coated SrZrO₃, thin films was evaluated in terms of bond strength by varying Sr/Zr mol ratio and amount of organic vehicle (ethyl cellulose and a-terpineol) additives. Although bond strength of the coatings increased as the Sr/Zr ratio decreased and the amount of organic vehicle rose, the effect of organic vehicle addition was more pronounced, suggesting that adherence of the SrZrO₃ films on Bi2223 tapes was governed primarily by the amount of organic vehicle additive.

은이 피복된 단심 Bi(2223) 초전도 선재에 대한 SrZrO₃ 코팅층의 접착강도 특성

이세종,예경환,이득용,송요승,Lee, Se-Jong,Ye, Kyung-Hwan,Lee, Deuk-Yong,Song, Yo-Seung 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.10

은이 피복된 Bi(2223) 단심 초전도 선재에 절연층으로 $SrZrO_3$ 피막을 졸-겔과 딥-코팅법으로 제조하여 $SrZrO_3$ 코팅층과 초전도 선재간 접착력 특성을 조사하였다. 실험인자로는 출발원료의 몰비, 유기화합물 첨가량, 건조온도 및 시간, 열처리 온도 및 시간이었으며 다구찌법의 망대특성과 $L_18(2^1{\times}3^7)$ 직교배열표를 이용하여 코팅층의 최적조건인 인자와 수준 조합의 최적화를 접착강도를 측정하여 분석하였다. 최적의 접착 특성을 가진 코팅조건은 Sr/Zr의 몰비가 0.3/0.7, 유기화합물 첨가량이 5wt%, 건조온도 및 시간은 160${\circ}C$ 10분, 열처리 온도 및 시간은 500${\circ}C$ 20분이었다. 분산분석 결과, 유의수준이 ${\alpha}$=0.1인 통계적으로 90% 신뢰공정이었다. Bond strength of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and $L_18(2^1{\times}3^7)$ orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160${\circ}C$, 10 min), heat treatment temperature and time(500${\circ}C$, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within ${\alpha}$=0.1 was significant with a 90% confidence level.

졸-겔법으로 제조한 SrZrO3 코팅층의 접착강도 특성

이세종,예경환,이득용,송요승 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.10

Bond strength of SrZrO3 resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and L18(21x37) orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed optimal condition is as follows: Sr/Zr mol ratio(0.3/0.7), amount of organic vehicle(5 wt%), drying temperature and time(160oC,10 min), heat treatment temperature and time(500oC, 20 min), respectively. ANOVA analysis suggested that the influence of the factors within α=0.1 was significant with a 90% confidence level. 은이 피복된 Bi(2223) 단심 초전도 선재에 절연층으로 SrZrO3 피막을 졸-겔과 딥-코팅법으로 제조하여 SrZrO3 코팅층과 초전도 선재간 접착력 특성을 조사하였다. 실험인자로는 출발원료의 몰비, 유기화합물 첨가량, 건조온도 및 시간, 열처리 온도 및 시간이었으며 다구찌법의 망대특성과 L18(21x37) 직교배열표를 이용하여 코팅층의 최적조건인 인자와 수준 조합의 최적화를 접착강도를 측정하여 분산분석하였다. 최적의 접착력 특성을 가진 코팅조건은 Sr/Zr의 몰비가 0.3/0.7, 유기화합물 첨가량이 5 wt%, 건조온도 및 시간은 160oC 10분, 열처리 온도 및 시간은 500oC 20분이었다. 분산분석 결과, 유의수준이 α=0.1인 통계적으로 90% 신뢰공정이었다.

SrZrO3 박막 미세조직에 미치는 PVP 결합제 첨가량 및 건조조건 영향

이세종,이득용,예경환,송요승 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.5

Taguchi법을 이용한 Ti/TiO2/IrO2-RuO2 전극의 부식특성 최적화

채경선,최형기,예경환,안준홍,송요승,이득용 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.6

Ti 기판에 TiO2 중간층을 플라즈마 용사법으로 증착 후 IrO2-RuO2 박막을 졸-겔과 dip coating법으로 제조하였다. 코팅층의 접착력을 향상시키기 위하여 유기화합물과 glass frit을 첨가하였다. Taguchi법의 망대특성과 L18(21×37)의 직교배열표를 이용하여 IrO2-RuO2 박막의 최적조건인 인자와 수준 조합의 최적화를 전류밀도를 측정 분산분석하였다. 최적의 코팅조건은 각각 ethyl cellulose의 점도는 100cp, 건조온도 및 시간은 170℃ 20분, 열처리온도 및 시간은 750℃ 10분, 전도성 분말과 glass frit의 무게비는 99:5, 최종열처리시간은 120분, 주입산소량은 5 sccm이었다. 분산분석결과, 유의수준이 α=0.1인 통계적으로 90% 신뢰공정이었다. IrO2-RuO2 films were deposited on plasma sprayed TiO2 buffer layer above Ti metal by sol-gel and dip-coating method. Organic vehicle (ethyl cellulose and α-terpineol) and glass frit were added to improve adherence of the coatings. Taguchi method and L18(21×37) orthogonal arrays were evaluated in terms of current density to determine the optimal combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed conditions were as follows: ethyl cellulose (100 cp), drying temperature and time (170oC, 20 min), heat treatment temperature and time (750oC, 10 min), the weight ratio of IrO2-RuO2 powders to glass frit (99:5), final heat treatment time (120 min) and flow rate of air (5 sccm), respectively. ANOVA analysis suggested that the influence of the factors within α=0.1 was significant with a 90% confidence level.

SrZrO₃ 박막 미세조직에 미치는 PVP 결합제 첨가량 및 건조조건 영향

이세종,이득용,예경환,송요승 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.5

은(Ag) 선재 위에 SrZrO$_3$ 절연 산화물을 졸-겔과 딥-코팅법으로 제조하여 박막표면의 미세균열에 미치는 PVP 함량과 건조조건 영향을 조사하였다. PVP 함량이 증가할수록 박막 두께는 증가하였지만, PVP 함량과 열처리 온도는 박막 표면의 미세균열에 영향을 미치지 못 하였다. 하지만, 낮은 건조온도와 긴 건조시간은 SrZrO$_3$ 박막 미세균열에 영향을 주었다. 그러므로, SrZrO$_3$ 코팅층 표면의 미세조직은 건조조건에 의하여 결정되는 것으로 관찰되었다. SrZrO$_3$ resistive oxides on Ag tapes were prepared by the sol-gel and dip coating method to investigate the effect of PVP content and drying condition on microstructure of the films. Although the film thickness increased with the addition of PVP, the amount of PVP and heat treatment were not effective to reduction of formation of microcracks at the films. However, lower drying temperature and longer drying time were beneficial to control the microcracks of the SrZrO$_3$ films, indicating that the microcracking of the films was governed primarily by the drying condition.

$SrZrO_3 $박막의 접착강도에 미치는 Sr/Zr 몰비와 유기화합물 첨가효과

이세종,이득용,예경환,송요승 한국초전도저온공학회 2002 한국초전도저온공학회논문지 Vol.4 No.1

$SrZrO_3 $resistive oxide barriers on Ag sheathed Bi2223 tapes were prepared by the sol-gel and dip coating method to reduce AC coupling loss. The performance of the dip-coated $SrZrO_3 $ thin films was evaluated in terms of bond strength by varying the Sr/Zr mol ratio and the amount of organic vehicle (ethyl cellulose and a-terpineol) additives. The bond strength of the coatings increased as the Sr/Zr ratio decreased and the amount of organic vehicle rose, respectively. It was found that the effect of organic vehicle addition was more pronounced, suggesting that the adherence of the $SrZrO_3 $ films on Bi2223 tapes was governed primarily by the amount of organic vehicle additive.

SrZrO3 박막 미세조직에 미치는 PVP 결합체 첨가량 및 건조조건 영향

이세종,이득용,예경환,송요승 한국세라믹학회 2003 한국세라믹학회지 Vol.40 No.5

Taguchi법을 이용한 Ti/TiO₂/IrO₂-RuO₂전극의 부식특성 최적화

이득용,채경선,최형기,예경환,안중홍,송요승 한국세라믹학회 2002 한국세라믹학회지 Vol.39 No.6

Ti 기판에 TiO$_2$ 중간층을 플라즈마 용사법으로 증착 후 IrO$_2$-RuO$_2$ 박막을 졸-겔과 dip coating법으로 제조하였다. 코팅 층의 접착력을 향상시키기 위하여 유기화합물과 glass brit을 첨가하였다. Taguchi법의 망대특성과 Lls(2$^1$$\times$3$^{7}$ )의 직교배열표를 이용하여 IrO$_2$-RuO$_2$ 박막의 최적조건인 인자와 수준 조합의 최적화를 전류밀도를 측정 분산분석하였다. 최적의 코팅조건은 각각 ethyl cellulose의 점도는 100cp, 건조온도 및 시간은 17$0^{\circ}C$ 20분, 열처리온도 및 시간은 75$0^{\circ}C$ 10분, 전도성 분말과 glass frit의 무게비는 99:5, 최종열처리시간은 120분, 주입산소량은 5sccm이었다. 분산분석결과, 유의수준이 $\alpha$=0.1인 통계적으로 90%신뢰공정이었다. IrO$_2$-RuO$_2$ films were deposited on plasma sprayed TiO$_2$ buffer layer above Ti metal by sol-gel and dip-coating method. Organic vehicle (ethyl cellulose and $\alpha$-terpineol) and glass frit were added to improve adherence of the coatings. Taguchi method and L$_{18}$ (2$^1$$\times$3$^{7}$ ) orthogonal arrays were evalvated in terms of current density to determine the optimal combination of levels of factors that best satisfy the bigger is better quality characteristic. The observed conditions were as fellows: ethyl cellulose (100 cp), drying temperature and time (17$0^{\circ}C$,20 min), heat treatment temperature and time (75$0^{\circ}C$,10 min), the weight ratio of IrO$_2$-RuO/powders to glass frit (99:5), final heat treatment time (120 min) and flow rate of air (5 sccm), respectively. ANOVA analysis suggested that the influence of the factors within $\alpha$= 0.1 was significant with a 90% confidence level.

플라즈마 용사법에 의한 열차폐 코팅의 열피로에 따른 AE신호 특성 연구

박진효,김정석,이구현,예경환,김승태,전채홍 한국정밀공학회 2005 한국정밀공학회 학술발표대회 논문집 Vol.2005 No.5월