주입선 및 열처리에 따른 IPS Empress 도재의 미세구조에 관한 연구
동진근,오상천,Dong, Jin-Keun,Oh, Sang-Chun 대한치과보철학회 1998 대한치과보철학회지 Vol.36 No.5
This study was undertaken to clarify the microstructure of the different IPS Empress ingots by etching and to observe the change of leucite crystal structure according to subsequent heat treatment and the crystal distribution according to sprue types(${\phi}2.8mm$, single sprue; ${\phi}1.8mm$, double sprue) by scanning electron microscopy. IPS Empress T1, O1 ingots used for staining technique, and Dentin(A2) ingots used for layering technique were selected for this study. To observe the microstructures of these ingots before pressing, the specimens were prepared in splinters($3{\times}3{\times}3mm$) taken from the original ingots. And to estimate crystal distribution and microstructural change by sprue type and subsequent heat treatment. the specimens($3{\times}3{\times}3mm$) were heat-pressed through the two types of sprues with different diameters and numbers, and all specimens were fired according to the recommended firing schedule. The observed surface was ground with waterproof papers($#800{\sim}#1800$) on the grind polisher and was cleaned ultrasonically. All specimen were etched with 0.5% hydrofluoric acid. After etching, the surface was treated by ion sputter coating for SEM observation at an accelerating voltage of 20kV. In all specimens, the central area of ground surface was observed because there was less difference in microstructure between the peripheral area and the central area. The results were as follows ; 1. In the microstructure according to the ingot type, there was a wide difference between the staining (T1,O1) and layering(Dentin A2) ingots, but there was not a considerable difference between the T1 ingot and the O1 ingot for staining technique. 2. In all specimens, the crystal dispersion of IPS Empress ceramic using double sprue was significantly more scattered than that of IPS Empress ceramic using single sprue. The degree of scattering was strongest in the Dentin(A2) specimen and weakest in the O1 ingot. 3. In the microstructural change according to the subsequent heat treatment, all of ingots had some microcracks in the inside of the leucite crystal and the glass matrix after pressing. The inner splinters of the leucite crystal became smaller, and more microcracks occurred in the glass matrix due to increasing heat treatment times. 4. The size of leucite crystals varied from $1{\mu}m\;to\;5{\mu}m$. The mean size of mature crystals was about $5{\mu}m$. The form of the crystal was similar to a circle when it was smaller and similar to an ellipse when it was larger.
IPS Empress 도재관의 파절강도 : 상악제1소구치에서 교합면 두께와 축면 경사도에 따른 영향
동진근,오상천,김상돈,Dong, Jin-Keun,Oh, Sang-Chun,Kim, Sang-Don 대한치과보철학회 1999 대한치과보철학회지 Vol.37 No.1
The purpose of this study was to compare the fracture strength of the IPS Empress ceramic crown according to the occlusal depth (1.5mm, 2.0mm, 2.5mm) and axial inclination ($4^{\circ},\;8^{\circ},\;12^{\circ}$) of the upper first premolar. After 10 metal dies were made fir each group, the IPS Empress ceramic crowns were fabricated and each crown was cemented on each metal die with resin cement. The cemented crowns mounted on the testing jig were inclined 30 degrees and a universal testing machine was used to measure the fracture strength. The results were : 1. The fracture strength of the ceramic crown with 2.5mm depth and $12^{\circ}$ inclination was the highest (630N). Crowns of 1.5mm depth and $4^{\circ}$ inclination had the lowest strength(378N). There were no significant differences of the fracture strength by axial inclination in same occlusal depth group. 2. The fracture mode of the crowns was similar. Most of fracture lines began at the loading area and extended through proximal surface perpendicular to the margin, irrespective of occlusal depth.
Coping design에 따른 도재전장관의 파절강도에 관한 연구
정완모,동진근,진태호,Chung Wan-Mo,Dong Jin-Keun,Jin Tai-Ho 대한치과보철학회 1992 대한치과보철학회지 Vol.30 No.1
The purpose of this study was to evaluate the effect of the metal coping design on the fracture resistance of ceramometal crown. The Ni-Cr alloy(Supranium, Krupp Co., German) and Vaccm-fired porcelain powder(Vita VMK 689, Vita Co., Germany) were used in this study. The measurement of fracture resisitance of ceramometal crown was done with Instron Universial Testing Machine(Instro Co., Model no.4201). The obained results were as fellows : 1. The fracture resistance measured at the buccal cusp tip was the highest value in the group that those position of ceramometal junction was 2mm superior to the lingual finshing margin(100.25Kg) and the fracture resistance revealed on order of the group that those position was 2mm buccal to the central groove(51.64Kg). 2. The fracture resistance measured at the central groove was higher value in the group that those position was 2mm lingual to the central groove than in the group that those position was 2mm lingual to the central groove than in the group that those position was 2mm superior to lingual finishing margin(132.48Kg). 3. In all cases, the fracture resistance at the central groove was higher than that at the buccal cusp tip.
한국인에 대한 가변형 치과 인상용 트레이의 적합성에 관한 연구
김태영,동진근,조혜원,Kim Tae-Young,Dong Jin-Keun,Cho Hye-Won 대한치과보철학회 2006 대한치과보철학회지 Vol.44 No.4
Purpose : this study was to evaluate the fitness of adjustable dental impression trays on the Koreans : the trays used in the previous study by Kim et al. as part of the dental adjustable tray development project were improved and modified. Material and method: The patterns of tray were made through CAD-CAM process, and a simple silicone-base molds were made from them. The trial products were reproduced by pouring polyurethane into these molds. 30 male students(Wonkwang University, Dental College) and 30 female students (Wonkwang Health Science College, Department of Dental Hygiene) were selected and Reversible hydrocolloid impression materials were used for this study. The fitness of the trays was evaluated by measuring the width and length of impression materials of each measurement sites. Results and conclusion : 1. In adapting the trays inside the mouth, a uniform width of impression material(3 $\sim$ 6mm) was obtained in most sites due to the tooth stops and the inclined planes accommodating the width of the tray 2. The thickness of impression material in the central part of the palate was a mean 9.8mm, which turned out to be somewhat thick. 3. In the mandible. the thickness of the impression material in the lingual side inferior to the contact point of the 1st and 2nd molars was 2.7mm, and the thickness of the material in the lingual side of the rearmost margin was 2.5 mm. The thickness of the impression material of these areas was relatively thin.
주입선 설계에 따른 Heat-pressed ceramic의 파절강도에 관한 연구
오상천,동진근,Oh, Sang-Chun,Dong, Jin-Keun 대한치과보철학회 1997 대한치과보철학회지 Vol.35 No.1
A heat-pressed technique(IPS-Empress, Ivoclar) has been described to construct single unit crown, inlay/onlay and veneers using a partially pre-cerammed and pre-colored glass-leucite ingot that has the greateast strength by the combination of heat-pressed procedure through the smalldiameter sprue and heat treatment procedure. The purpose of this study was to evaluate the flexure strength of a heat-pressed ceramic material(IPS-Empress) without simulated firing treatments according to pontic designs. Two groups of 9 disks(1.4mm thick, 14mm in diameter) each using two types of sprues with different diameters($({\Phi}2.8\;,{\Phi}1.8)$) and numbers were prepared. The specimens were mounted in the testing jig. The flexural strengths were determined, by means of the bi-axial bending test, by loading the center of disk to failure using a universal testing machine(Zwick 145141, Zwick, Germany) at a cross-head speed of 1.0 mm/min. The means flexural strength value of one group using a sprue with ${\Phi}2.8$ was $140.4{\pm}8.0Mpa$. That of the other group using two sprues with ${\Phi}1.8$ was $151.8{\pm}10.3Mpa$. After analysis, results showed that there was a statistical difference between groups(t=2.33m p<0.05). No clnical implications were drawn from these data because of absence of simulated firing treatment.