NBR/PVC의 polymer blend에 관(關)한 연구(硏究)(제2보(第2報))
허동섭,이정근,Huh, Dong-Sub,Lee, Jung-Keun 韓國고무學會 1971 엘라스토머 및 콤포지트 Vol. No.
The intention of this study is to investigate the properties of polymer blend, NBR/PVC vulcanizates and blending procedures such as roll-mixing temperatures and sequences for polymer blending of NBR and PVC(resin type). The results obtained are as follows: 1. The roll temperature applied for polymer blending is around $150^{\circ}C$. At this temperature region, the degradation of rubber stock, which may be caused by heat, can be minimized and mill processing in practical application in industries can also be facilitated. 2. It is obviously necessary that a small amount of plasticizers should be added to the stock for improving processibility of roll mixing and physical properties. 3. On roll-mixing sequence, it is more effective that PVC compounded with plasticizer is added to NBR milled on hot roll. 4. The vulcanizates of the blends with different degree of polymerization of PVC ale similar to one another in properties. 5. NBR/PVC(70/30) blends shows the better physical characters than eve,-made foreign latex blend except abrasion-resistance. 6. As PVC addition ratio is increased, the physical properties such as resistance to ozone, tear, heat and oil and tensile strength, modulus, hardness have also improved, on the other hand, tension set and rebound character decreased. 7. The curve of ultimate elongation have point of inflection at the ratio of $30\sim40$ part of PVC. 8. While CR is blended, the physical properties such as brittle point, rebound and resistance to oil in high temperature have improved. 9. Polymer blend of NBR and domestic PVC is applied for the industrial utility such as rubber sole and heel, electric wire cover and oil-resistant packing, coating and gasket, printing roll, film for food packing etc.
고무 제품(製品)의 노화성(老化性)에 관(關)한 연구(硏究)(제1보(第1報))
허동섭,백남철,Huh, Dong-Sub,Paik, Nam-Chul 韓國고무學會 1966 엘라스토머 및 콤포지트 Vol. No.
The aging characteristics of vulcanized rubber products manufactured in Korean industries have been studied, especially in terms of relationship between aging temperature and time, and also the comparison of results between Geer's oven testing and tube testing was made. It was assessed from changes in tensile properties resulting from conditioning at elevated temperatures for specified period of time. Even though the recipe of each sample is different, the results, as would be expected, has shown that at lower aging temperature the change of tensile strength indicate moderately and at the elovated severely as shown in Figure 9. Consequently, in spite of that the results from conditioning at various temperatures for certain specified period of time must be equivalent to each other, it shows inignorable tolerance. The results of Geer's oven test and tube test have shown slightly different value. It seemed to be caused by the result of migration phenomena on aging in Geer's oven.