Sasaki, T.T.,Hono, K.,Vierke, J.,Wollgarten, M.,Banhart, J. Elsevier Sequoia 2008 Materials science & engineering. properties, micro Vol.490 No.1
Amorphous Al<SUB>85</SUB>Ni<SUB>10</SUB>La<SUB>5</SUB> powders were consolidated to cylindrical samples by spark plasma sintering (SPS), and their microstructures and mechanical properties were investigated. When the powders were consolidated below the crystallization temperature, an amorphous phase was retained in the consolidated sample. Sintering above the crystallization temperature caused full crystallization. The Vickers hardness of the amorphous-containing sample was about 350HV in the as-sintered state and increased up to 450HV by a subsequent heat treatment just below the crystallization temperature. The highest hardness was achieved in a nanocrystalline microstructure. Compression tests revealed the brittle nature of the consolidated samples although the fracture and yield strength was higher than 1GPa. The brittleness is due to the low relative density of the amorphous-containing samples and the presence of a large amount of intermetallic compounds in the fully crystallized sample.