중량변화에 의한 폴리에스터 레이온 부직포의 정전기 대전 완화특성

이성일,박용순,Lee, Sung-Ill,Park, Yong-Soon 한국전기전자재료학회 2011 전기전자재료학회논문지 Vol.24 No.12

Non-wovens polyester rayon samples were manufactured, and the electrification properties of electrostatics were measured for three different samples (15 g/$m^2$, 25 g/$m^2$, and 40 g/$m^2$) with the environmental settings of temperature (20~40$^{\circ}C$) and humidity (40~90%). The conclusions are as follows. Heavy sample generated more static electricity when the temperature was constant. The static electricity decreased slowly when the humidity is less than 70%, while it sharply decreased over 70% humidity condition. For non-woven polyester rayon, static charge decreased as temperature and humidity increased. As the weight increased, less time were taken for the electrification voltage to drop to the half.

EPR의 열화에 의한 충.방전 전류 특성에 관한 연구

이성일,Lee, Sung-Ill 한국전기전자재료학회 2008 전기전자재료학회논문지 Vol.21 No.7

This paper describes the degraded properties of between the charge and discharge current for ${\gamma}$-ray irradiated in electric power cable rubbers using in nuclear power generating station. The charge and discharge current of degradation in EPR(Ethylene Propylene Rubber), which were irradiated with the radiant capacity of 0.033 Mrad/h, have been measured in order to investigate the influence of the atmosphere(in amount of reinforcing agent, moisture absorption and heat treatment) on electrical properties. When ${\gamma}$-ray were irradiated on the EPR with more reinforcing agent from 4 to 40 Phr, charge and discharge currents was increase due to the amount of reinforcing agent. It was verified that the discharging and charging currents irradiated by ${\gamma}$-ray were higher than those that was not irradiated. The amount of the degraded current was more after moisture absorption than before moisture absorption. The charge and discharge current after heat treatment was similar to that of before heat treatment and it was decreased with the time elapsed. As these properties related with ${\gamma}$-ray irradiation dose, it is suggested that these properties can be utilized as a index of irradiation degradation.

열 열화한 열전도성 실리콘 고무의 전기특성

이성일,Lee, Sung Ill 한국전기전자재료학회 2016 전기전자재료학회논문지 Vol.29 No.12

In this study, the electrostatic capacity and dielectric loss tangent for $20{\mu}m$ thick thermal conductivity silicone rubber which is heated at 80 degrees for 8 hours has been measured at temperature of $30^{\circ}C{\sim}170^{\circ}C$, frequency of 0.1~1 MHz. The results of degradation evaluation by this study are as follows. In low frequency, it found that the electrostatic capacity decreased with increasing temperature. On the other hand, it confirmed that the range of the electrostatic capacity narrowed with increasing frequency. It confirmed that there are the carboxylic acid structure and C-O bonding at range of wave number 1,000cm-1 to 1,300cm-1.

실리콘 고무의 부분방전 특성에 관한 연구

이성일,권영천,Lee, Sung-Ill,Kwon, Young-Cheon 한국전기전자재료학회 2011 전기전자재료학회논문지 Vol.24 No.11

In this thesis, the silicone filler with a sample size of 0~75 phr and void size of 2~4.5 mm is prepared in order to diagnose the defect of void which exists in widely used insulation material, silicone rubber. In this silicone rubber sample, electrodes are connected and whilst the voltage changes, applied voltage 7 kV~9 kV is increased constantly over time and discharge quantity, discharge frequency and applied voltage (T-QNV) were measured. The discharge quantity of the applied voltage (VQ) is measured to estimate inception voltage and extinction voltage. In addition, under the condition of maintaining constant applied voltage, discharge quantity and discharge frequency (QN) are measured, and its characteristics are analyzed.

보강제 변화에 따른 실리콘 고무의 정전기 열화 특성에 관한 연구

이성일,Lee, Sung Ill 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.2

In this study, we have come to the following conclusions regarding to the electrification properties (electrostatic electrification voltage and electrification relaxation time) of electrostatics in the three type of specimen (size: $4cm{\times}4cm{\times}0.103cm$) of silicone rubber which is mixed with the ATH (Aluminium Trihydrate(Al($OH_3$)) of 30 phr, 60 phr, 120 phr as reinforcing filler. The electrification properties of electrostatics were measured for the different mixing ratio of ATH with the applied voltage of DC 10 kV at the temperature range of $10^{\circ}C{\sim}30^{\circ}C$ and humidity range of 60%~80%. When the temperature remained constant, the electrical resistance decreased as the humidity increasing in the range of 60%, 70%, 80%. In contrast, when the humidity remained constant, the electrical resistance increased as the temperature increasing in the range of $10^{\circ}C$, $20^{\circ}C$, $30^{\circ}C$. Regarding these results, may be it is because the absorption of O-H molecule appeared in the silicone specimen. It was confirmed that when the temperature remained constant, the electrification relaxation time decreased as the humidity increased. In contrast, when the humidity remained constant, the electrification relaxation time increased as the temperature increased.

에틸렌프로필렌 고무의 전압에 의한 누설전류 특성에 관한 연구

이성일,Lee, Sung Ill 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.12

In this study, the leakage current - voltage characteristic and leakage current - time characteristic for the undegradated Ethylene Propylene Rubber and the Ethylene Propylene Rubber which is degradated by water tree for 200 hours have been measured on the temperature range of $50{\sim}80^{\circ}C$ and applied DC voltage range of 200 V~800 V for 90 minutes. The results of this study are listed below. In case the temperature is $50^{\circ}C$, it founds that the leakage current have shown a increase in proportion to the applied voltage as 2 pA in 200 V, 6 pA in 400 V, 10 pA in 600 V and 15 pA in 800 V. It founds that the leakage current increased with the rise of temperature. It founds that the leakage current was consistent as time goes by, the leakage current of the sample degradated by water tree for 200 hours has increased more than undegradated sample.

부분 방전에 의한 실리콘 케이블의 열화 특성에 관한 연구

이성일,Lee, Sung Ill 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.1

In this study, the characteristics of partial discharge was measured for the four core silicone cable (0.6/1.0 kV, $1.0SQ{\times}4C$) with insulated part of 15 cm and conductor of 1cm. The following results have been confirmed as a result of this study. When the first line of cable is connected to the positive electrode and the second, third line of cable is connected to the negative electrode, it found that the inception voltage and extinction voltage decreased with increasing the line of negative electrode, and the partial discharge charge quantity(Q) increases, while the number of discharge occurrence has decreased. The inception voltage and extinction voltage of partial discharge has decreased with increasing the degradation rate in the 33%, 67%, 100%. Also, it confirmed that the partial discharge charge quantity(Q) and the number of discharge occurrence has decreased.

오손액 변화에 따른 실리콘 고무의 정전기 대전열화 특성

이성일,Lee, Sung Ill 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.9

In this study, the electrification voltage of electrostatics for silicone rubber sample($4cm{\times}4cm{\times}0.103cm$) following immersion with contaminants of 2 ml, 5 ml, 10 ml for six hours has been measured in through the applied voltage of 10 kV DC at temperature of $80^{\circ}C{\sim}110^{\circ}C$, humidity of 50%~90%. The results of this study are as follows. In case the contaminants is constant, it found that the electrification voltage of electrostatic decreased with increasing temperature and humidity to $35^{\circ}C$, 90%. In case of 2 ml of contaminants concentration, it found that the electrification voltage of electrostatic decreased with increasing temperature and humidity to $35^{\circ}C$, 50%. In case of the sample at temperature of $15^{\circ}C$ and humidity of 50%, it found that the electrification voltage of electrostatic decreased with increasing contaminants to 10 ml.

전극재에 의한 실리콘 고무의 C-V 특성에 관한 연구

이성일,Lee, Sung Ill 한국전기전자재료학회 2015 전기전자재료학회논문지 Vol.28 No.11

In this study, the properties of C-V degradation for thermal conductivity silicone rubber sample which is attached by copper-copper, copper-aluminum, aluminum-aluminum on upper-side and under-side has been measured at temperature of $80^{\circ}C{\sim}140^{\circ}C$. The results of this study are as follows. In case the frequency is increased, it found that the electrostatic capacity increased with increasing temperature to $80^{\circ}C$, $110^{\circ}C$, $140^{\circ}C$ regardless of kind of electrode. It found that the electrostatic capacity increased with becoming high temperature range of frequency regardless of kind of electrode. This result is considered to be caused by thermal absorption on the thermal conductivity silicone rubber sample. It found that the electrostatic capacity decreased with increasing temperature and frequency. This result is considered to be caused by molecular motion of C-F radical or OH radical.

실리카 충진된 실리콘 고무의 유전 특성에 관한 연구

이성일,Lee, Sung Ill 한국전기전자재료학회 2013 전기전자재료학회논문지 Vol.26 No.11

In this study, the capacitance and dielectric loss tangent of the silicone rubber which is combined with filler (30 phr~50 phr) have been measured on the range of 100 Hz~100 kHz and $30{\sim}170^{\circ}C$. It was found that when the frequency is 0.1 kHz~100 kHz and the silicone rubber is combined with 30 phr to 50 phr of filler, the capacitance of silicone rubber has increased by about 28.6 pF to 33 pF in 30 phr of filler, about 20 pF to 46.1 pF in 40 phr of filler and about 36.4 pF to 44 pF in 50 phr of filler. It seems that the volume of dielectric loss has gradually increased due to the temperature rise and the rotating of dipole in electric field through the electric dipole generated by the Si-O group which is induced by adding of filler, or the carbonyl group which is caused by oxidation. It seems that the dielectric dispersion in 0.1 kHz is caused by molecular motion of Siloxane group in main chain, and the dielectric dispersion in 10 kHz is caused by molecular motion of Methyl group in side chain.