Jianlei Zhang,Yueshan Jiang,Conghui Hu,Gang Ji,Changjiang Song,Qijie Zhai 대한금속·재료학회 2022 METALS AND MATERIALS International Vol.28 No.11
The influence of Cr on the microstructural evolution of austenite in Fe-20Mn-9Al-1.2C-xCr (wt%, x = 0, 3 and 6) low-densitysteels during isothermal aging at 650 °C for various durations was systematically investigated. With the isothermal agingprocessed, the 0Cr and 3Cr samples underwent the divorced eutectoid transformation followed by the eutectoid transformation,while only the eutectoid transformation was observed in the 6Cr sample. Meanwhile, increasing Cr content changedthe eutectoid transformation products from ferrite + κ-carbide in the 0Cr sample to ferrite + κ-carbide + M23C6carbide in the3Cr sample, and to ferrite + M7C3carbide in the 6Cr sample. The Cr addition significantly increased the A1 temperature (655°C) of the 0Cr sample to 712 °C of the 3Cr sample, and to 841 °C of the 6Cr sample. As a result, the temperature differencebetween the A1 temperature and experimental phase transformation temperature (650 °C) was enlarged, which provided agreater driving force for the eutectoid transformation and accelerated the transformation rate of eutectoid transformation. Inaddition, the Cr addition had a significant effect on the diffusion of constituent elements, decreased the interlayer spacingof pearlite structure from 625 ± 30 nm in the 0Cr sample to 385 ± 25 nm in the 3Cr sample, and to 150 ± 20 nm in the 6Crsample, refining the eutectoid structure. These findings revealed the mechanism regarding the effect of Cr addition on theeutectoid transformation of austenite, offering valuable insights into the microstructure design of high-performance lowdensitysteels.
연관 검색어 추천
이 검색어로 많이 본 자료
활용도 높은 자료