G. Rajesh Kannan,P. Sathiya,T. Deepan Bharathi Kannan,M. Bhuvanesh Kumar 대한금속·재료학회 2023 METALS AND MATERIALS International Vol.29 No.9
In this work, the technique of spin arc welding has been used to weld HSLA steel of grade 15CDV6. Experiments wereperformed according to the L9 Taguchi matrix using current, travel speed, wire feed rate, and spin rotation speed as inputparameters. The quality of the weld was analysed by measuring the bead geometry and microhardness. The Whale OptimizationAlgorithm (WOA) was used to identify the optimized welding parameters. The optimised parameters were identifiedthrough WOA as follows: current 230 A, voltage 24 V, travel speed 720 mm/min, and spin rotation speed 1500 rpm. Thepost-weld heat treatment (PWHT) was performed on the optimised welded sample to enhance the weld properties. Themicrohardness was increased by 79% after PWHT. Ferrite content was found to have reduced after welding and PWHT thegrain size and structure of the BM, HAZ, and WM were analysed by EBSD technique. The decrease in ferrite content hada significant effect on the microhardness. The Energy Dispersive Spectroscopy results showed the presence of Vanadiumcarbide (VC) precipitates which helped in increasing the microhardness.