http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
( Anawati Anawati ),( Hidetaka Asoh ),( Sachiko Ono ) 한국부식방식학회 2016 Corrosion Science and Technology Vol.15 No.3
The effect of alloying element Ca (0, 1, and 2 wt%) on corrosion resistance and bioactivity of the as-received and anodized surface of rolled plate AM60 alloys was investigated. A plasma electrolytic oxidation (PEO) was carried out to form anodic oxide film in 0.5 mol dm-3 Na3PO4 solution. The corrosion behavior was studied by polarization measurements while the in vitro bioactivity was tested by soaking the specimens in Simulated Body Fluid (1.5xSBF). Optical micrograph and elemental analysis of the substrate surfaces indicated that the number of intermetallic particles increased with Ca content in the alloys owing to the formation of a new phase Al2Ca. The corrosion resistance of AM60 specimens improved only slightly by alloying with 2 wt% Ca which was attributed to the reticular distribution of Al2Ca phase existed in the alloy that might became barrier for corrosion propagation across grain boundaries. Corrosion resistance of the three alloys was significantly improved by coating the substrates with anodic oxide film formed by PEO. The film mainly composed of magnesium phosphate with thickness in the range 30 - 40 μm. The heat resistant phase of Al2Ca was believed to retard the plasma discharge during anodization and, hence, decreased the film thickness of Ca-containing alloys. The highest apatite forming ability in 1.5xSBF was observed for AM60-1Ca specimens (both substrate and anodized) that exhibited more degradation than the other two alloys as indicated by surface observation. The increase of surface roughness and the degree of supersaturation of 1.5xSBF due to dissolution of Mg ions from the substrate surface or the release of film compounds from the anodized surface are important factors to enhance deposition of Ca-P compound on the specimen surfaces.
Satoshi Kokai,Eiji Fukuyama,Susumu Omura,Sachiko Kimizuka,Ikuo Yonemitsu,Koichi Fujita,Takashi Ono 대한치과교정학회 2019 대한치과교정학회지 Vol.49 No.1
In this report, we describe a case involving a 34-year-old woman who showed good treatment outcomes with long-term stability after multidisciplinary treatment for unilateral cleft lip and palate (CLP), maxillary hypoplasia, severe maxillary arch constriction, severe occlusal collapse, and gingival recession. A comprehensive treatment approach was developed with maximum consideration of strong scar constriction and gingival recession; it included minimum maxillary arch expansion, maxillary advancement by distraction osteogenesis using an internal distraction device, and mandibular setback using sagittal split ramus osteotomy. Her post-treatment records demonstrated a balanced facial profile and occlusion with improved facial symmetry. The patient’s profile was dramatically improved, with reduced upper lip retrusion and lower lip protrusion as a result of the maxillary advancement and mandibular setback, respectively. Although gingival recession showed a slight increase, tooth mobility was within the normal physiological range. No tooth hyperesthesia was observed after treatment. There was negligible osseous relapse, and the occlusion remained stable after 5 years of post-treatment retention. Our findings suggest that such multidisciplinary approaches for the treatment of CLP with gingival recession and occlusal collapse help in improving occlusion and facial esthetics without the need for prostheses such as dental implants or bridges; in addition, the results show long-term post-treatment stability.