Chang, Ho-Jung,Kim, Byoung-Chul,Akihama, Ryozo,Song, Jin-Tae Materials Research Society of Korea 1994 한국재료학회지 Vol.4 No.3
As-grown $YBa_2Cu_3O_{7-x}$ films on MgO(100)substrates were prepated by a reactive co-evaporation method, and effects of activated oxygen plasma on the crystallinity and superconductivity at substrate temperature ranging from $450^{\circ}C$ to $590^{\circ}C$ were investigated. The film deposited under the activated oxygen plasma at the substrate temperature of $590^{\circ}C$ had a single crystal phase. Whereas, when films were deposited under only oxygen gas, they were not in perfect single crystal phase but with slight polycrystalline nature. When the substrate temperature was $590^{\circ}C$, $Tc_{zero}$'s were 83K and 80K for films with and without activated oxygen plasma, respectively. The critical temperature, the crystal structure and the surface morphology of as-grown films were found to be insensitive to the activated oxygen plasma which is introduced during deposition instead of oxygen gas, but the crystalline quality was improved somewhat by the introduction by the introduction of actvated oxygen plasma.
스크린 인쇄법에 의한 YBa2Cu3O7-x/ Ag 고온산화물초전도 후막의 제작
송진태,장호정,도부안광,토신전풍,청수현사,추병량삼 대한금속재료학회(대한금속학회) 1990 대한금속·재료학회지 Vol.28 No.9
Superconduction YBa₂Cu₃0_(7-x)./Ag composite thick films on a YSZ substrate were prepared by the screen printing method. Microstructure and supercduction properties such as zero-resistance Tc(Tc^(Zero)), Jc at 77k, and the interface reactions betwean the superconduction thick film and YSZ substrate were investigated. For the YBa₂Cu₃O_(7-x)/Ag composite thick films annealed at 980℃ and 1000℃ in flowing oxygen, Tc^(Zero) and Jc at 77k increased, and the normal state resistivity and the thickness of interface reaction layer decreased strongly with increasing Ag content. The drastic decrease in reaction layer thickness with Ag addition seemed to result from the prevention of interaction between the film and the substrate by liquid Ag which formed during high temperature annealing. SEM analysis showed that the grain size increased as Ag content increased from 7wt% to 24wt%. It seems that the liquid Ag in YBa₂Cu₃O_(7-x)/Ag composite thick films enhances the intergranular coupling of YBa₂Cu_O_(7-x)/Ag grains, which results in the favored sintering process at 980℃.