DELAYED HYDRIDE CRACKING IN ZIRCALOY FUEL CLADDING – AN IAEA COORDINATED RESEARCH PROGRAMME
C. COLEMAN,V. GRIGORIEV,V. INOZEMTSEV,V. MARKELOV,M. ROTH,V. MAKAREVICIUS,Y. S. KIM,KANWAR LIAGAT ALI,J.K. CHAKRAVARTTY,R. MIZRAHI,R. LALGUDI 한국원자력학회 2009 Nuclear Engineering and Technology Vol.41 No.2
The rate of delayed hydride cracking (DHC), V, has been measured in cold-worked and stress-relieved Zircaloy-4 fuel cladding using the Pin-Loading Tension technique. At 250 °C the mean value of V from 69 specimens was 3.3(±0.8)x10⁻⁸ m/s while the temperature dependence up to 275 °C was described by Aexp(-Q/RT), where Q is 48.3 kJ/mol. No cracking or cracking at very low rates was observed at higher temperatures. The fracture surface consisted of flat fracture with no striations. The results are compared with previous results on fuel cladding and pressure tubes.
DELAYED HYDRIDE CRACKING IN ZIRCALOY FUEL CLADDING - AN IAEA COORDINATED RESEARCH PROGRAMME
Coleman, C.,Grigoriev, V.,Inozemtsev, V.,Markelov, V.,Roth, M.,Makarevicius, V.,Kim, Y.S.,Ali, Kanwar Liagat,Chakravartty, J.K.,Mizrahi, R.,Lalgudi, R. Korean Nuclear Society 2009 Nuclear Engineering and Technology Vol.41 No.2
The rate of delayed hydride cracking (DHC), V, has been measured in cold-worked and stress-relieved Zircaloy-4 fuel cladding using the Pin-Loading Tension technique. At $250^{\circ}C$ the mean value of V from 69 specimens was $3.3({\pm}0.8)x10^{-8}$ m/s while the temperature dependence up to $275^{\circ}C$ was described by Aexp(-Q/RT), where Q is 48.3 kJ/mol. No cracking or cracking at very low rates was observed at higher temperatures. The fracture surface consisted of flat fracture with no striations. The results are compared with previous results on fuel cladding and pressure tubes.