Thermal Stability of Precipitates in Al-2.8wt%Cu-1.4wt%Li Alloy
Congcong Zhu,Guoai Li,Shijia Hao,Guoling Mao,Wenli Gao 대한금속·재료학회 2022 METALS AND MATERIALS International Vol.28 No.12
The microstructures and mechanical properties of Al-2.8 wt%Cu-1.4 wt%Li-T87 alloy after thermal exposure at 125, 150and 175 °C were measured and characterized by universal testing machine, scanning electron microscope and transmissionelectron microscope. The thermal stability of microstructures and mechanical properties of T87 heat-treated Al-2.8 wt%Cu-1.4 wt%Li alloy was investigated. The results show that the tensile strength of Al-2.8 wt%Cu-1.4 wt%Li-T87 alloy increasedfirst and then decreased with the increase of thermal exposure temperature, which is due to the change of the number and sizeof precipitates. After thermal exposure at 125 °C, the alloy exhibited higher strength due to further precipitation of θ′ phaseand stable size of T1phase. After thermal exposure at 175 °C, the mechanical properties of Al-2.8 wt%Cu-1.4 wt%Li-T87alloy decreased obviously, which was related to the dissolution of θ' phase and thickening of T1phase.