http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Dongsen Mao,Jun Yu,Qiangsheng Guo 한국공업화학회 2015 Journal of Industrial and Engineering Chemistry Vol.25 No.-
The effect of support pretreatment with ammonia on the performance of Cu–Fe/SiO2 catalyst for higher alcohols synthesis from syngas was studied by CO hydrogenation, X-ray diffraction, N2 adsorption– desorption, temperature-programmed reduction of H2, Fourier transform infrared spectroscopy, N2O chemisorption and temperature-programmed desorption of adsorbed CO. The results indicated that the pretreatment of SiO2 with ammonia resulted in the formation of more active sites of Cu and higher dispersion of Fe species on the catalyst surface and enhanced the synergistic effect between the copper and iron species. As a result, the CO conversion and the space time yield of alcohols of the Cu–Fe/SiO2 catalyst increased from 14.8% and 89.0 g kg1 h1 to 17.4% and 107.0 g kg1 h1, respectively.
Conversion of syngas to C2+ oxygenates over Rh-based/SiO2 catalyst: The promoting effect of Fe
Jun Yu,Dongsen Mao,Lupeng Han,Qiangsheng Guo,Guanzhong Lu 한국공업화학회 2013 Journal of Industrial and Engineering Chemistry Vol.19 No.3
The effect of Fe promoter on the catalytic properties of Rh–Mn–Li/SiO2 catalyst for CO hydrogenation was investigated. The catalysts were comprehensively characterized by means of X-ray diffraction (XRD), N2adsorption–desorption, temperature programmed reduction (TPR), temperature programmed desorption (TPD), temperature programmed surface reaction (TPSR), and diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). Activity testing results showed that low loading of Fe (≤0.1 wt%)improved the reactivity and yield of C2+ oxygenates; however, the opposite effect appeared at the high values of Fe (>0.1 wt%). Characterization results suggested that the addition of Fe strengthened the Rh–Mn interaction and increased the desorption/transformation rate of adsorbed CO, which could be responsible for the increase of CO conversion. But on the other hand, the existence of Fe might deposit over the Rh surface, and decreased the number of active sites, resulting in the decrease of CO conversion when the Fe amount was excessive. The selectivity to C2+ oxygenates varied inversely with the reducibility of Rh oxide species. Moreover, it is proposed that the transformation of dicarbonyl Rh+(CO)2into H–Rh–CO is favorable for the formation of C2+ oxygenates, and the hydrogenation ability of Fe can increase the hydrogenation of acetaldehyde to ethanol.
Guangying Fu,Dongsen Mao,Shuaishuai Sun,Jun Yu,Zhiqiang Yang 한국공업화학회 2015 Journal of Industrial and Engineering Chemistry Vol.31 No.-
CuO-CeO2-ZrO2 catalysts were prepared via facile dry oxalate-precursor synthesis and tested for COoxidation. The effect of Cu contents was investigated by N2 adsorption, TEM, XRD, XPS, H2-TPR, CO-TPDand Raman techniques. The results show that CuO dispersion, SBET and adsorbed CO amount exhibit avolcano trend with increasing the Cu content. The highest activity was achieved over the catalyst with18 mol% Cu with the CO conversion being 99% at 85 8C. The superior performance of the catalystprepared by this method is attributed to the finely dispersed CuO species and the strong interaction ofCuO with ceria-zirconia phase.
Xiaoya Xue,Jun Yu,Ying Han,Xiuzhen Xiao,Zhangping Shi,Haifang Mao,Dongsen Mao 한국공업화학회 2020 Journal of Industrial and Engineering Chemistry Vol.86 No.-
A series of Zr-based metal-organic frameworks (UiO-66) supported Rh–Mn catalysts with various metalloadings were prepared by using a co-impregnation method, and the catalytic activities wereinvestigated for the direct synthesis of ethanol-based C2+ oxygenates from CO hydrogenation. Thecatalysts were comprehensively characterized by means of N2 sorption, XRD, TEM, XPS, H2-TPR, andDRIFT. The structural and textural properties of the catalysts show clearly that the overall frameworkstructure of UiO-66 can be beneficial to the high dispersion of supported metals, but the synergistic effectof Rh and Mn would be influenced by the metal loading or Mn/Rh ratio. When the loadings of Rh and Mnreached 3 wt.% and 3 wt.%, the catalyst has the best catalytic activity with the highest yield of C2+oxygenates of 200.1 g/(kg h), which can be attributed to the enhanced CO dissociation ability of Rh sitesand weaker Rh CO band strength.