Fatigue Crack Growth Behavior in Ultrafine Grained Low Carbon Steel
Kim, Ho-Kyung,Park, Myung-Il,Chung, Chin-Sung,Shin, Dong-Hyuk The Korean Society of Mechanical Engineers 2002 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.16 No.10
Ultrafine grained (UFG) low carbon (0.15 wt.% C) steel produced by equal channel angula. pressing (ECAP) was tested for investigating the effect of load ratio on the fatigue crack growth rate. Fatigue crack growth resistance and threshold of UFG steel were lower than that of asreceived coarse grained steel. It was attributed to the less tortuous crack path. The UFG steel exhibited slightly higher crack growth rates and a lower △Kth with an increase of R ratio. The R ratio effect on crack growth rates and △Kth was basically indistinguishable at lower load ratio (R >0.3), compared to other alloys, which indicates that contribution of the crack closure vanishes. The crack growth rate curve for UFG steel exhibited a longer linear extension to the lower growth rate regime than that for the coarse grained as-received steel.
Fatigue Crack Growth Behavior in Ultrafine Grained Low Carbon Steel
Ho,Kyung Kim,Myung-Il Choi,Chin-Sung Chung Dong-Hyuk Shin 대한기계학회 2002 JOURNAL OF MECHANICAL SCIENCE AND TECHNOLOGY Vol.16 No.10
Ultrafine grained (UFG) low carbon (0.15 wt.% C) steel produced by equal channel angular pressing (ECAP) was tested for investigating the effect of load ratio on the fatigue crack growth rate. Fatigue crack growth resistance and threshold of UFG steel were lower than that of as-received coarse grained steel. It was attributed to the less tortuous crack path. The UFG steel exhibited slightly higher crack growth rates and a lower △K_th with an increase of R ratio. The R ratio effect on crack growth rates and △K_th was basically indistinguishable at lower load ratio (R>0.3), compared to other alloys, which indicates that contribution of the crack closure vanishes. The crack growth rate curve for UFG steel exhibited a longer linear extension to the lower growth rate regime than that for the coarse grained as-received steel.<br/>