합성고무계 건축용 방수제

최세영,Choi, Sei-Young 한국고분자학회 1997 고분자 과학과 기술 Vol.8 No.6

황가형 EVA 의 제조 및 고무와의 블렌드

최세영(Sei Young Choi),진제용(Je Yong Jin) 한국고무학회 1999 엘라스토머 및 콤포지트 Vol.34 No.3

N/A In this study, double bond, unsaturated group was introduced to the main chain of EVA by chemically treating EVA, nondiene polymer. Benzene sulfonic acid, ENB and DCPD were used as a third element. Also, from blending CR and SBR, conventional synthetic rubber we prepared vulcanizates and examined their physical properties. The datum lead to the following conclusion that some problems were modified; limited temperature in use and mechanical properties like hardness, tensile strength, tensile stress, and elongation rate of thermoplastic EVA, keeping the following advantages of original EVA; green strength, injection molding by pressure, adhesion, tackiness, dimensional stability, and ozone resistance, etc. It is expected that continuous research of the modification between nondiene and dime polymer will improve what were shown disadvantages in synthetic polymer; processing, oxidation resistance, and adhesion. In addition, it will be possible to continue process of rubber products by utilizing possible fluidity for fusion of EVA.

가시광촉매가 처리된 자동차 내장재의 VOC 분석방법에 대한 연구

최세영 ( Sei Young Choi ) 한국고무학회 2013 엘라스토머 및 콤포지트 Vol.48 No.3

가시광촉매가 처리된 자동차내장재의 VOC 분석방법에 있어서 샘플백에 충진하는 질소 대신 공기를 충진하여 시험하였다. 그 결과 자동차내장재의 VOC 분석시 질소를 충진한 샘플백은 VOCs 및 폼알데히드의 저감효과가 나타나지 않았다. 그러나 질소대신 공기를 충진한 샘플백에서는 VOCs 및 폼알데히드가 현저하게 감소하였으며 자동차내장재의 VOCs 분석시 샘플백에 질소 대신 공기를 충진하여야 가시광촉매에 의한 효과를 발휘할 수 있다는 것을 확인하였다. In this study, VOC analysis method of vehicle interior materials and parts treated to visible-light responsive photocatalyst was tested by sample bag filled with air instead of nitrogen. As a result, when analyzed VOC of vehicle interior materials and parts, sample bag filled with the nitrogen was not confirmed of effect reducing VOCs and formaldehyde. However, VOCs and formaldehyde of sample bag that was filled with air instead of nitrogen, decreased significantly. Reaction effect for visible light-responsive photocatalyst was confirmed that sample bag of vehicle interior materials and parts should be filled with air instead of nitrogen.

이산화티타늄 광촉매를 처리한 Polyester 섬유의 기능성 연구

최세영 ( Sei Young Choi ) 한국고무학회 2014 엘라스토머 및 콤포지트 Vol.49 No.4

본 연구에서는 광촉매 작용을 하는 이산화티타늄 광촉매를 polyester 섬유에 코팅하여 탈취, 항균 및 자외선차폐에 대한 기능을 부여하고 그 특성을 알아보았다. 그 결과 탈취성능은 세탁 전과 반복 20회 세탁 후에도 97%이상저감되는 것으로 나타났으며, 항균성은 균수가 99.9%이상 감소되는 것으로 나타났다. 그리고 Polyester 섬유를 20회반복 세탁을 행하여도 이산화티타늄 광촉매의 이탈 없이 표면에 견고하게 부착되어 있음을 확인하였으며, 또한 가스분해성능도 세탁전과 20회 반복 세탁 후에도 유지하는 것으로 나타나 세탁내구성이 우수함을 확인하였다. 자외선 차폐성도 세탁 전과 비교하여 20회 반복 세탁 후에도 83%이상 차단되는 것으로 나타났다. The functionality such as deodorant, antibacterial, ultraviolet shielding of titanium dioxide self-actuated photo catalyst WeltouchTM treated polyester fiber was characterized in conditions without light. The deodorizing capacity was maintained more than 97% reduction irrespective of before washing and after 20 times repeated washing, and antimicrobial capacity was also retained more than 99.9% reduction. Titanium dioxide self-actuated photo catalyst was still maintained to the surface of polyester fiber without separation even after 20 times repeated washing. According to washing durability of polyester fiber, the reduction effect for ammonia was still retained even after 20 times repeated washing as much asbefore washing. The ultraviolet shielding capacity was still maintained at least 83% irrespective of before washing and20 times repeated washing.

생체분해성 Poly(glycolide- co-ε-caprolactone- co-L-lactide) 블록 공중합물의 비등온 결정화 거동에 관한 연구

최세영 ( Sei Young Choi ),송승호 ( Seung Ho Song ) 한국고무학회 2014 엘라스토머 및 콤포지트 Vol.49 No.1

본 연구에서는 생체분해성 폴리에스터 계열의 glycolide, L-lactide 및 ε-caprolactone 단량체를 이용하여 2단계 중합법에 의한 삼원 공중합체를 제조하여, DSC를 이용한 비등온 결정화 거동을 고찰하였다. 보다 더 정확한 거동을 검토하기 위하여 Avrami 식과 Ozawa 식을 조합하여 비등온 결정화 거동을 고찰하였다. 과냉각도를 분석한 결과 PGCLA21의 값이 가장 큰 값을 보이고 있으며 L-lactide 함량이 증가함에 따라 과냉각도는 증가하는 경향을 보이고 있다. 수정된 Avrami 식을 이용하여 다양한 냉각속도에서 비등온 결정화 거동 결정화 속도 상수는 큰 경향을 보이고 있지 않는 것을 알 수 있었다. Avrami 및 Ozawa 식을 조합하여 특정한 상대적 결정화도에서의 냉각함수를 구한결과 L-lactide 함량이 증가하면서 PGCL과 비교시 결정화 속도를 향상시키는 역할을 하고 있는 것으로 여겨지는 반면 PGCLA41과 PGCLA21을 비교시 L-lactide 함량이 일정 이상 증가시 logF(T) 값이 큰 것을 확인 할 수 있는데 이는 동일한 결정을 얻는데 더 많은 냉각 속도를 필요로 한다는 것을 의미하며 결정화 속도 향상에 부정적인 영향을 미치는 것으로 판단된다. In this work, glycolide, L-lactide and ε-caprolactone monomers were polymerized into the triblock copolymers by two step polymerization method and their non-isothermal crystallization behaviors were studied by combination of modified Avrami and Ozawa formula for further analysis of their behaviors. The result showed that PGCLA21 gave the highest value for supercooling analysis and super cooling degree increased with L-lactide content. Crystallization velocity constant, however, showed no significant change. The result of cooling function in specific relative crystallization degree showed that the increase of L-lactide content made an effect on the more enhancement of crystallization velocity of the PGCLA than PGCL. The result of big logF(T) value with the L-lactide content above critical point for PGCLA41 and PGCLA21 showed that bigger cooling velocity needed to gain same crystal size compared with PGCL. This means that it gives negative effect in the increase of crystallization velocity.

가시광촉매를 이용한 자동차 내장재로부터 발생하는 VOCs의 저감연구

최세영 ( Sei Young Choi ),양승기 ( Seung Gi Yang ) 한국고무학회 2013 엘라스토머 및 콤포지트 Vol.48 No.3

가시광촉매를 이용하여 자동차 내장재에서 발생하는 VOCs의 저감 효과를 알아보았다. 가시광촉매는 sol-gel법으로 제조하였으며 UV-vis peak가 420 nm에서 적색이동 되어 가시광영역에서 감응하는 것으로 나타났다. 이러한 특성을 갖는 가시광촉매를 자동차 내장재에 코팅처리하고, 자동차 내장재에서 발생하는 VOCs를 측정한 결과 분해·저감율이 우수하게 나타났다. On this study, visible-light responsive photocatalyst prepared by sol-gel method was evaluated the effect of the reduction of volatile organic compounds (VOCs) occurred in vehicle interior and its property was examined. According to UV/visible result, visible-light responsive photocatalyst was found that the UV-visible peak is red shift at 420nm, is sensitive in the visible light region. With vehicle interior parts and materials coated visible-light responsive photocatalyst, VOCs was measured by GC/MS. Measuring the VOCs generated from vehicle interior parts and materials, the reduction of VOCs was confirmed.

부틸고무를 결합재로 사용한 바이오센서의 전기화학적 성질

최세영 ( Sei Young Choi ),윤길중 ( Kil Joong Yoon ) 한국고무학회 2006 엘라스토머 및 콤포지트 Vol.41 No.4

리튬이차전지용 양극 활물질(LiCoC₂)의 표면처리의 특성 분석 및 전기화학적 특성 고찰

장윤한,최세영,Chang, Youn-Han,Choi, Sei-Young 한국전기화학회 2007 한국전기화학회지 Vol.10 No.3

The importance of secondary battery industry is getting excited according to the development of battery industry as a high efficiency energy supplier of electronic machine of mobile information such as mobile phone, lap-top computer, PDA. It is rasing the interest about security of safety and high efficiency of cathode material for main part of secondary lithium battery. The cathode material which has been used like $LiCoO_2,\;LiMn_2O_4,\;LiNi_xCo_yMn_zO_2,\;LiNi_xCo_yM_zO_2$ (M=Al, Zr, Mg etc.,) the most typical material is $LiCoO_2$. But it is studying the development of substitute such as efficiency amelioration of $LiCoO_2$, thetiary element, olivine element because of the capacity of $LiCoO_2$, the matter of security; especially the betterment of efficiency, security research of safety has been actively processed in domestic and overseas about surface coating treatment of active cathode which is using oxide ($M_xO_3$). This study analyses side effect of battery according to increase of surface treatment, formation of precipitation for reagent condensation, non-reagent residue of oxide ($M_xO_3$) which is remains during the surface treatment of $LiCoO_2$; conducts study of new process, the consideration of the electrochemical property to improve oxide solution of mixing rate, mixture of surface treatment, dryness, calcinations conditionetc. 전자 산업의 발전과 함께 휴대폰, 노트북, PDA등과 같은 휴대 정보 전자 기기의 고성능 에너지 공급원으로서 이차전지 산업의 중요성이 높아지고 있다. 이에 따라 리튬이차전지의 핵심부품인 양극재료의 고성능화 및 안전성 확보에 대해 많은 관심이 증대되고 있다. 현재 사용되고 있는 양극재료에는 $LiCoO_2,\;LiMn_2O_4,\;LiNi_xCo_yMn_zO_2,\;LiNi_xCo_yM_zO_2$ (M=Al, Zr, Mg 등) 등이 있으며, 그중 가장 대표적으로 사용되고 있는 물질은 $LiCoO_2$이다. 그러나 $LiCoO_2$가 가지고 있는 용량적 한계 및 안전성 문제로 인하여 $LiCoO_2$의 성능 개선 및 3성분계, 올리빈계와 같은 대체물질의 개발에 대한 연구가 활발히 진행중이다. 특히 산화물($M_xO_3$)을 이용한 활물질 표면처리와 같은 성능개선 및 안전성 확보연구는 국내 및 국외에서 활발히 진행되고 있다. 본 연구에서는 $LiCoO_2$의 표면처리 과정에서 불균일 코팅된 산화물의 탈리 및 이의 응집에 의한 침전물 생성 및 표면처리량의 증가에 따른 전지에서의 부작용에 대하여 분석하고, 이와 같은 문제점을 개선하기 위해 코팅량 조정 및 표면처리 공정의 혼합, 건조, 소성 조건 등과 같은 신공정에 대한 연구와 전기화학적 특성 고찰을 실시하였다.

키토산과 말레익산 그라프트공중합체의 유화안정성에 관한 연구

최상희 ( Sang Hoi Choi ),최세영 ( Sei Young Choi ),정석진 ( Suk Jin Chung ) 한국키틴키토산학회 2009 한국키틴키토산학회지 Vol.14 No.1

3-Methylthiophene이 함유된 폴리우레탄 필름의 전기적 특성 연구

최교창 ( Kyo Chang Choi ),이은경 ( Eun Kyoung Lee ),최세영 ( Sei Young Choi ) 한국고무학회 2004 엘라스토머 및 콤포지트 Vol.39 No.3

본 연구에서는 poly(propylcne glycol) (PPG), toluene 2,4-diisocyanate, 3-methylthiophene (3-MT)으로부터 반응시간, FeCl₄의 농도, 3-MT와 PU의 무게비 반응온도 등의 다양한 조건에 따라 전도성 폴리우레탄 필름을 제조하였다. FeCl₃,와 ethy1 acetate로 구성된 유기용매에 제조한 필름을 함침 시킨 견과 3-MT와 FeCl₃의 확산-산화 반응을 통해 급속한 전도성 PMT 층이 형성되었다. 전도성 복합체의 전기 전도도는 제조조건에 따라 많은 영향을 받고 SEM 분석과 접촉카측정으로부터 반응시간과 반웅온도가 모폴로지와 표면 자유에너지에 미치는 영향을 조사하였으며 제조된 복합체의 전도도는 최대 42 S/cm 인 것으로 확인되었다. The clastomeric and conductive polyurethane (PU) films were prepared by poly(propylene glycol) (PPG). toluene 2,4-diisocvanate, 3-methylthiophenc (3-MT) at various preparation conditions, such as the reaction time, the FeCl₃ concentration, the weight ratio of the 3-MT to PU and the reaction temperature for the diffusion-oxidative reaction. The conductive poly (3-methylthiophene) (PMT) layers via the diffusion-oxidative reaction of 3-MT and ferric chloride were formed by immersing the film in organic solution of FeCl₃/ethyl acetate. The preparation conditions greatly affected the electrical conductivity of the 3-MT /PU composite. The effects of the reaction time and temperature on morphology and surface free energy were investigated by scanning electron microscopy (SEM) analysis and contact angle measurement, respectively. The conductivity of the composite was as high as 42 S/cm.