탄소섬유복합재료의 AE에 의한 충격손상재강도와 손상특성평가
이상국(Sang-Guk Lee),오세규(Sae-Kyoo Oh),남기우(Ki-Woo Nam),김옥균(Og-Gyun Kim) 한국해양공학회 1995 韓國海洋工學會誌 Vol.9 No.1
This study is aimed to have a database of system development for the prediction, monitoring, analyzing, and evaluation of tensile strength and damage characteristics through AE technique for CFRP. Therefore the correlations between impact characteristics(such as impact velocity, impact energy, delamination area etc) and AE signals for CFRP laminates were investigated. And also it were accomplished the evaluation of tensile strength and the investigation on correlation with AE signals for impact damaged specimen of CFRP laminates.
이상국,김옥균,남기우,오세규 韓國非破壞檢査學會 1995 한국비파괴검사학회지 Vol.15 No.1
본 연구는 [0°.90°]₂s와 [0°₂/90°₂]s의 2종류 탄소섬유복합재료에 대한 인장 및 파괴인성 시험시의 파괴거동과 음향방출 특성을 해석하고 성형시의 성형압력과 인장강도 및 파괴인성 간의 상관성을 알아내기 위하여 수행되었다. AE신호는 음향방출장비를 이용하여 성형과정, 인장 및 파괴인성 시험중에 각각 검출하였다. 인장강도는 성형가압 단계수가 적을수록, 그리고 [0°/90°]₂s 시험편 쪽이 [0°₂/90°₂]s 시험편보다 높은 강도를 나타내었다. 파괴인성은 동일한 온도영역에서 거의 같은 값을 나타내나 시험온도가 높아질수록 점차 낮아짐을 알 수 있었다. 한편 인장 및 파괴인성 시험시의 파괴거동과 AE신호간의 상관성을 조사하기 위하여 AE데이터의 AE변수들에 대한 후 신호처리(post processing)와 광학현미경 및 주사형 전자현미경 관찰이 각각 수행되었다. The study was carried out to analyze the fracture behavior and the acoustic emission(AE) characteristics and to find the relationship among tensile strength, fracture toughness and cure pressure in cure process of the carbon fiber reinforced composites of two types, [0°/90°]₂s and [0°₂/90°₂]s. AE signals were detected during the curing process, tensile tests and fracture toughness tests by acoustic emission(AE) measurements, respectively. Tensile strengths showed that the less cure pressurizing steps and the side of [0°/90°]₂s specimens had the higher strengths than those of the others. Fracture toughness by change of test temperature showed nearly same values in the same temperature region, but the higher test temperature had the lower fracture toughness values. In order to examine the relationship between fracture behavior of CFRP in tensile and fracture toughness tests and AE signals, the post processing for AE parameters of AE data and the observations of microscope and SEMA have been carried out respectively.