http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Maiping Yang,WeiQu Liu,Liyan Liang,Chi Jiang,Yankun Xie,Hongyi Shi,Fengyuan Zhang,Ke Pi 한국섬유공학회 2020 Fibers and polymers Vol.21 No.8
In this paper, various fabrics with good self-cleaning performance were prepared via a facile dip-coating method. The fabrics composed with different fibers and woven techniques were firstly immersed in ZnO sol to increase the surfaceroughness, then dip-coated in fluoroalkylsilane (HFT) solution to reduce the surface energy. The coated fabric showedexcellent superhydrophobicity with a water contact angle (WCA) of 157.8 o and water shedding angle (WSA) of 5 o. Themorphologies and chemical compositions of prepared fabrics were observed with SEM, XPS and EDS. The obtained fabrickept stable water-repelling property in acidic and alkaline solutions, solvents and UV irradiation. Benefited from its high antiwaterability and photocatalysis function of ZnO, the coated fabric demonstrated excellent self-cleaning performance. Thisversatile approach of constructing superhydrophobic fabrics is attractive and could be large-scaled employed in industrialproduction process.
Tengfei Shen,Mangeng Lu,Liyan Liang 한국고분자학회 2012 Macromolecular Research Vol.20 No.8
A series of novel biodegradable blocked polyurethane crosslinkers (BPUCs) were synthesized from the reaction of toluene 2,4-diisocyanate (TDI), isophorone diisocyanate (IPDI), polycaprolactone (PCL), 1,1,1-trimethylolpropane (TMP), and methyl ethyl ketoxime (MEKO). Synthesis of the accurate kind of BPUCs was confirmed by Fourier transform infrared spectroscopy (FTIR), proton nuclear magnetic resonance spectroscopy (1H NMR), and gel permeation chromatography (GPC). Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) were used to determine the deblocking temperatures of the BPUCs. The thermal analysis revealed that both TDI- and IPDI-based BPUC had the proper initial deblocking temperature (<160 oC) and the maximum deblocking temperature (<200 oC) for practical applications. Compared to IPDI-based BPUC, the TDI-based BPUC had a lower thermal dissociation temperature and a faster deblocking rate. Hydroxyl polyurethane (HPU) was introduced to study the crosslinking effect of prepared BPUCs. The reaction proceeded at various deblocking temperatures in different curing times. It was noticed that the elastic modulus and tensile strength of the HPU sample increased whereas elongation at break decreased with the addition of BPUC in comparison with pure HPU, which suggested better interfacial adhesion due to the strong chemical reaction between the released NCO groups from BPUC and hydroxyl groups from HPU. In addition, improvement on water resistance of the BPUC modified HPU samples compared to pure HPU samples also demonstrated the good crosslinking effect of prepared BPUCs.
Jian Zheng,Yan Zhang,Ying Wang,Jianqun Gan,Lu Shen,FuBin Luo,Liyan Liang,Kun Wu,Mangeng Lu 한국고분자학회 2016 Macromolecular Research Vol.24 No.5
A lateral phthalonitrile functionalized main-chain polybenzoxazine precursor has been successfully synthesized. The structure was characterized by proton nuclear magnetic resonance (1H NMR) and Fourier transform infrared (FTIR). The formation of benzoxazine rings were confirmed by the characteristic resonances observed at about 4.55 (C-CH2-N) and 5.30 ppm (N-CH2-O) and the absorbance at 950 cm-1 of benzene attached with an oxazine ring. The curing behavior was monitored by differential scanning calorimetry (DSC) and in situ FTIR. The completion of polymerization was proved by the disappearance of the band located at 950 cm-1 in FTIR. Thermogravimetric analysis (TGA) was used to investigate the thermal stability, and the results indicated that the thermal stability of the cured polymer gained significant improvement than that without phthalonitrile functionalization.