http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Shenoi, Pratima Ramakrishna,Badole, Gautam Pyarelal,Khode, Rajiv Tarachand The Korean Academy of Conservative Dentistry 2014 Restorative Dentistry & Endodontics Vol.39 No.1
Objectives: This study evaluated the efficacy of Endosolv-R and Xylene in softening epoxy resin based sealer after 1 to 2 min exposure. Materials and Methods: Sixty Teflon molds ($6mm{\times}1.5mm$ in inner diameter and depth) were equally divided into 3 groups of 20 each. AH 26 (Dentsply/De Trey), AH Plus (Dentsply/De Trey), Adseal (Meta-Biomed) were manipulated and placed in the molds allotted to each group and allowed to set at $37^{\circ}C$ in 100% humidity for 2 wk. Each group was further divided into 2 subgroups according to the solvents used, i.e. Xylene (Lobachemie) and Endosolv-R (Septodont). Specimens in each subgroup were exposed to respective solvents for 1 and 2 min and the corresponding Vicker's microhardness (HV) was assessed. Data was analysed by Mauchly's test and two-way analysis of variance (ANOVA) with repeated measures, and one-way ANOVA. Results: Initial hardness was significantly different among the three sealers with AH Plus having the greatest and Adseal having the least. After 2 min, Xylene softened AH Plus and Adseal sealer to 11% and 25% of their initial microhardness, respectively (p < 0.001), whereas AH 26 was least affected, maintaining 89.4% of its initial microhardness. After 2 min, Endosolv-R softened AH 26, AH Plus and Adseal to 12.7, 5.6 and 8.1% of their initial microhardness, respectively (p < 0.001). Conclusions: Endosolv-R was a significantly more effective short term softener for all the tested sealers after 2 min whereas Xylene was an effective short term softener against AH plus and Adseal but less effective against AH 26.
Pratima Ramakrishna Shenoi,Gautam Pyarelal Badole,Rajiv Tarachand Khode 대한치과보존학회 2014 Restorative Dentistry & Endodontics Vol.39 No.1
Objectives: This study evaluated the efficacy of Endosolv-R and Xylene in softening epoxy resin based sealer after 1 to 2 min exposure. Materials and Methods: Sixty Teflon molds (6 mm x 1.5 mm in inner diameter and depth) were equally divided into 3 groups of 20 each. AH 26 (Dentsply/De Trey), AH Plus (Dentsply/De Trey), Adseal (Meta-Biomed) were manipulated and placed in the molds allotted to each group and allowed to set at 37℃ in 100% humidity for 2 wk. Each group was further divided into 2 subgroups according to the solvents used, i.e. Xylene (Lobachemie) and Endosolv-R (Septodont). Specimens in each subgroup were exposed to respective solvents for 1 and 2 min and the corresponding Vicker's microhardness (HV) was assessed. Data was analysed by Mauchly’s test and two-way analysis of variance (ANOVA) with repeated measures, and one-way ANOVA. Results: Initial hardness was significantly different among the three sealers with AH Plus having the greatest and Adseal having the least. After 2 min, Xylene softened AH Plus and Adseal sealer to 11% and 25% of their initial microhardness, respectively (p < 0.001), whereas AH 26 was least affected, maintaining 89.4% of its initial microhardness. After 2 min, Endosolv-R softened AH 26, AH Plus and Adseal to 12.7, 5.6 and 8.1% of their initial microhardness, respectively (p < 0.001). Conclusions: Endosolv-R was a significantly more effective short term softener for all the tested sealers after 2 min whereas Xylene was an effective short term softener against AH plus and Adseal but less effective against AH 26.