다양한 분산제에 의한 AlN-Y<sub>2</sub>O<sub>3</sub> 혼합분말의 비수계 용매 중 분산특성
김신,방상우,황인준,윤상옥,신현호,Kim, Shin,Bang, Sang-Woo,Hwang, Injoon,Yoon, Sang-Ok,Shin, Hyunho 한국세라믹학회 2014 한국세라믹학회지 Vol.51 No.4
The dispersion characteristics of AlN-4.5 wt% $Y_2O_3$ powder mixture by various dispersants were investigated in ethanol and methyethly-ketone (MEK) solvents. In general, the cationic polymer dispersants demonstrated superior dispersion of the powder as compared to the non-ionic ester-type dispersants or anionic phosphate-ester-based ones. The dispersion performance of the cationic polymer dispersants was sensitive to the type of solvent. An anhydric maleic-acid-based graft copolymer dispersant, AFB-1521, demonstrated a very good dispersion capability in ethanol but exhibited a much inferior dispersion in MEK. On the other hand, the dispersion of the powder mixture was very good with a phosphate-ester-based block polymer dispersant, BYK-111, in MEK solvent, while dispersionwas much degraded in ethanol.
신현호,윤상옥,김신,황인준,Shin, Hyunho,Yoon, Sang-Ok,Kim, Shin,Hwang, Injoon 한국세라믹학회 2013 한국세라믹학회지 Vol.50 No.3
The effect of a $WO_3$ or $Ga_2O_3$ addition on the densification, phase evolution, optical reflectance, and elastic and dielectric properties of $Y_2O_3$-doped AlN ceramics sintered at $1800^{\circ}C$ for 3 h is investigated. The investigated compositions of the additives are 4.5 wt% $Y_2O_3$ (YA), 3.5 wt% $Y_2O_3$-1.0 wt% $Ga_2O_3$ (YGA), and 3.5 wt% $Y_2O_3$-1.0 wt% $WO_3$ (YWA). $YAlO_3$ and $Y_4Al_2O_9$ form as the secondary phases in all of the investigated compositions, whereas $W_2B$ appears additionally in the YWA. In the YGA, Ga is detected in the AlN grains, indicating that the dissolution of $Ga_2O_3$ into the AlN lattice occurs. The addition of $WO_3$ blackens the specimen more significantly than that of $Ga_2O_3$ does. In all of the investigated specimens, the linear shrinkage and the apparent density are above 20 percent and in the range of 3.34-3.37 $g/cm^3$, respectively. The elastic modulus, Poisson's ratio, the dielectric constant, and the dielectric loss are in the ranges of 335-368 GPa, 0.146-0.237, 8.60-8.63, $2.65-3.95{\times}10^{-3}$, respectively. The sinterability and the properties of $Y_2O_3$-doped AlN ceramics are not much altered by the addition of $WO_3$ or $Ga_2O_3$.