http://chineseinput.net/에서 pinyin(병음)방식으로 중국어를 변환할 수 있습니다.
변환된 중국어를 복사하여 사용하시면 됩니다.
Adil Othman Abdullah,Yu Hui,Xudong Sun,Sarah Pollington,Fenik Kaml Muhammed,Yi Liu 대한치과보철학회 2019 The Journal of Advanced Prosthodontics Vol.11 No.1
PURPOSE. To evaluate and compare the effect of different materials and techniques on the shear bond strength of veneering ceramic materials to zirconia. MATERIALS AND METHODS. 136 sintered zirconia cubes were prepared and randomly divided into four study groups according to corresponding methods of surface treatment and materials: GLN (grinding followed by laser scanning using Noritake Cerabien ZR), SLN (sandblasting followed by laser scanning using Noritake Cerabien ZR), GLV (grinding followed by laser scanning using VITA VM 9), and SLV (sandblasting followed by laser scanning using VITA VM 9). Spraying technique was performed to coat the core. Profilometer, SEM, XRD, EDS, universal testing machine, and stereomicroscope were used to record surface roughness Ra, surface morphology, phase transformation, elemental compositions, shear bond strength SBS values, and failure types, respectively. Specimens were investigated in unaged (not immersed in artificial saliva) and aged (stored in artificial saliva for a month) conditions to evaluate SBS values. RESULTS. Grinding and GLN as first and second surface treatments provided satisfactory Ra values in both conditions (1.05 ± 0.24 um, 1.30 ± 0.21 um) compared to sandblasting and other groups (P<.05). The group GLN showed the highest SBS values in both conditions (30.97 ± 3.12 MPa, 29.09 ± 4.17 MPa), while group SLV recorded the lowest (23.96 ± 3.60 MPa, 22.95 ± 3.68 Mpa) (P<.05). Sandblasting showed phase transformation from t-m. Mixed failure type was the commonest among all groups. CONCLUSION. GLN showed to be a reliable method which provided satisfactory bond strength between the veneer ceramic and zirconia. This method might preserve the integrity of fixed dental crowns. [ J Adv Prosthodont 2019;11:65-74] PURPOSE. To evaluate and compare the effect of different materials and techniques on the shear bond strength of veneering ceramic materials to zirconia. MATERIALS AND METHODS. 136 sintered zirconia cubes were prepared and randomly divided into four study groups according to corresponding methods of surface treatment and materials: GLN (grinding followed by laser scanning using Noritake Cerabien ZR), SLN (sandblasting followed by laser scanning using Noritake Cerabien ZR), GLV (grinding followed by laser scanning using VITA VM 9), and SLV (sandblasting followed by laser scanning using VITA VM 9). Spraying technique was performed to coat the core. Profilometer, SEM, XRD, EDS, universal testing machine, and stereomicroscope were used to record surface roughness Ra, surface morphology, phase transformation, elemental compositions, shear bond strength SBS values, and failure types, respectively. Specimens were investigated in unaged (not immersed in artificial saliva) and aged (stored in artificial saliva for a month) conditions to evaluate SBS values. RESULTS. Grinding and GLN as first and second surface treatments provided satisfactory Ra values in both conditions (1.05 ± 0.24 um, 1.30 ± 0.21 um) compared to sandblasting and other groups (P<.05). The group GLN showed the highest SBS values in both conditions (30.97 ± 3.12 MPa, 29.09 ± 4.17 MPa), while group SLV recorded the lowest (23.96 ± 3.60 MPa, 22.95 ± 3.68 Mpa) (P<.05). Sandblasting showed phase transformation from t-m. Mixed failure type was the commonest among all groups. CONCLUSION. GLN showed to be a reliable method which provided satisfactory bond strength between the veneer ceramic and zirconia. This method might preserve the integrity of fixed dental crowns. [ J Adv Prosthodont 2019;11:65-74]