Wenli Pei,Fazeng Lian,Meng Fu,Guiqin Zhou,M. Takahashi 한국자기학회 2004 Journal of Magnetics Vol.9 No.4
The crystallization behaviours of nanocomposite made by a function of quenching rate (roller speed) were studied. The results showed that there was one step crystallization process for the alloy quenched at roller speed of 32 ㎧, which could be shown as, Am (amorphouse) + α-Fe+Nd₂Fe₁₄B → α-Fe+Nd₂Fe₁₄B. For the alloy quenched at roller speed of 40 ㎧, there was two steps crystallization process taking place at different temperatures, which could be shown as, Am → α-Fe+Nd₂Fe₂₃B₃+Nd₂Fe₁₄B+Am' → α-Fe+Nd₂Fe₁₄B. The presence of transition phase (Nd₂Fe₂₃B₃) was harmful to get fine and uniform grain size during crystallization process. Uniform microstructures and high magnetic properties could be attained for the as-quenched alloy containing less amorphous phase and no presence of transition phase during annealing treatment. For the alloy prepared at roller speed of 32 m/s, the following properties were obtained, Br = 0.904 T, iHc = 801 ㎄/m, (BH)max = 122 kJ/㎥ and Mr/Ms = 0.6.
Study on the Interaction of Compound Bonded Magnets
Ying Chang,Nuo Ma,Xiaojun Yu,Fazeng Lian,Wei Li 한국자기학회 2004 Journal of Magnetics Vol.9 No.4
The attempt for the addition of double-phase nanocomposite Nd₂Fe₁₄B/Fe₃B powders, respectively, into several RE₂Fe₁₄B (RE=Pr, Nd) powders with high magnetic properties was carried out. The powders were compounded and compressed to take shape bonded magnets. By means of investigating the variation of compound magnet Br, the interaction between magnetic powders was revealed. The result shows that not chemical just but physical interaction exists between elements. The compound effect of Nd₂Fe₁₄B/Fe₃B-ferrite bonded magnets was detailed studied. The functional relation was revealed between magnetic properties and ferrite content. That is Y = 5.42 x²-11.34 x + 6.62. The variation of iHc temperature coefficient β_(iHc) with ferrite content was investigated. Following the ferrite content increased, β_(iHc) and hirr were obviously decreased, compression-resistant strength was enhanced.